Three kinds of X70 steels with the same chemical composition and different microstructures fabricated by varying processes were compared in aspect of the microstructures and mechanical properties using SEM, TEM and tensile testing machine. The experimental results showed that the steel 1 with acicular ferritic microstructure fabricated by thermal-mechanical processing with online accelerated cooling (TMCP) exhibited an excellent combination of strength and toughness, but provided high yield ratio of 0.85, low uniform elongation of 8.3% as well as low strain hardening exponent of 0.09, indicating poor deformability. In contrast to above steel 1, the steel 2 and steel 3 having ferrite-bainite dual-phase microstructure respectively fabricated by TMCP and intercritical annealing exhibited the improved deformability in terms of the low yield ratio of 0.69 and 0.68, high uniform elongation of 12.8% and 11.8%, and strain hardening exponent of 0.157 and 0.155. It is argued that the optimum properties combination of strength, toughness and deformability can best be achieved by obtaining a ferrite-bainite dual-phase microstructure. This kind of ferrite-bainite dual-phase pipeline steel is appropriate to transmitting oil and natural gas in seismic zone and permafrost.

A kind of medium-carbon low-alloy dual-phase steels with high-content martensite produced by intercritical annealing at 785-830 ºC for 10-50 minutes were studied in aspect of microstructures and work hardening behavior using SEM and tensile testing machine. The experimental results showed that the work hardening of the studied steels obeyed the two-stage work hardening mechanism, whose work hardening exponent of the first stage was higher than that of the second stage. The work hardening exponent increased with increasing the intercritical annealing temperature and time. For series A steel intercritically annealed at 785 ºC with starting microstructure of ferrite plus pearlite, austenite nucleated at the pearlite colonies, so the holding time of only 50 minutes can increase the work hardening exponent obviously. For series B steel with starting microstructure of martensite, austenite nucleated at lath interfaces, lath colony boundaries of primary martensite and carbides, accelerating the formation of austenite, so holding time for 30 minutes made the work hardening exponent increase obviously. High work hardening rate during initial plastic deformation (<0.5% strain) was observed.

This study aims to investigate the effect of initial microstructures on the properties of ferrite-martensite dual-phase pipeline steels with strain-based design. For this purpose, the as-received acicular ferrite steels were first austenitized at 920 ºC for 15 minutes followed by air cooling and water quenching to produce ferrite-pearlite and ferrite-martensite microstructure, respectively. Subsequently, the steels with ferrite-pearlite, ferrite-martensite and as-received acicular ferrite microstructure were intercritically annealed at 820 ºC for 10 minutes followed by water quenching to produce three different ferrite-martensite dual-phase microstructures. Tensile tests, Vickers hardness and Charpy impact tests were carried out to investigate the mechanical properties. Scanning electron microscope was used to analyze the microstructures and tensile fractographs. The results showed that all the tensile specimens of these three different ferrite-martensite dual-phase steels fractured in ductile mode, however, their microstructures and mechanical properties varied significantly. By contrast, the ferrite-martensite dual-phase steel derived from acicular ferrite initial microstructure had optimal combination of the strength, toughness and deformability, which provided a good candidate for the pipeline steels with strain-based design used in severe geological environments.