Abstract This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey’s post-hoc test. The VL values were analyzed using the Kruskal–Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge. Er,CrYSGG ErCrYSGG Er,Cr YSGG Cr 980nm nm 980 (SR (VL Subsequently 1 NT gel varnish D follows 025 0 25 0.2 W 50 5 5. Hz 446 4 46 4.4 Jcm2 Jcm J cm2 cm J/cm 55 air Furthermore 20 2 2. 2141 21 41 21.4 cycling DESRE DES RE Tukeys Tukey s posthoc post hoc KruskalWallis Kruskal Wallis p 0.05. 005 0.05 . 05 0.05) 18073107bor38e025treatment boretreatment 1807 3107 bor 38 e025treatment e Moreover CrYSGG ErCr 98 02 0. 44 4. 214 21. 00 0.0 180 310 3 etreatment 9 18 31

Abstract This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn’s post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 μm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

Resumo O objetivo deste estudo in vitro foi avaliar a influência de uma nova proposta de design de implante e protocolo cirúrgico na estabilidade primária em diferentes densidades ósseas. Foram testados quatro grupos (n=9): G1 - cônico, cone morse, Ø 4,3 mm x 10 mm de comprimento (Alvim CM); G2 - experimental cônico; G3 - cilíndrico, cone morse, Ø 4,0 mm x 11 mm de comprimento (Titamax CM) e G4 - experimental cilíndrico. Os implantes experimentais foram obtidos a partir de uma mudança no design dos respectivos modelos comerciais. A inserção foi realizada em blocos de poliuretano (PU) 0,24 g/cm3 (20 pcf) e 0,64 g/cm3 (40 pcf), de acordo com diferentes protocolos cirúrgicos. A estabilidade primária foi aferida por meio do torque de inserção (TI) e ensaio de arrancamento. Os dados foram analisados por ANOVA, teste de Tukey (α=0,05) e correlação de Pearson. Para TI e arrancamento, os implantes convencionais e experimentais não mostraram diferença entre si quando inseridos na PU de 20 pcf (p>0,05). Na PU de 40 pcf, os implantes modificados exibiram maior TI (p <0,05) e menor arrancamento (p <0,05) em relação aos respectivos modelos convencionais. O design do implante testado associado ao protocolo cirúrgico, influenciou positivamente a estabilidade primária em ossos de maior densidade.

Abstract The purpose of thisin vitrostudy was to evaluate the influence of a new proposal of implant design and surgical protocol on primary stability in different bone densities. Four groups were tested (n=9): G1 - tapered, cone morse, Ø 4.3 mm x 10 mm in length (Alvim CM); G2 - experimental tapered; G3 - cylindrical, cone morse, Ø 4.0 mm x 11 mm in length (Titamax CM) and G4 - experimental cylindrical. The experimental implants were obtained from a design change in the respective commercial models. The insertion was performed in polyurethane (PU) blocks 0.24 g/cm3(20 pcf) and 0.64 g/cm3(40 pcf), according to different surgical protocols. The primary stability was measured by means of insertion torque (IT) and pullout test. Data were analyzed by ANOVA, Tukey’s test (α=0.05) and Pearson’s correlation. For IT and pullout, conventional and experimental implants showed no difference between them when inserted in the 20 pcf PU (p>0.05). In the 40 pcf PU, the modified implants exhibited greater IT (p<0.05) and lower pullout (p<0.05) compared to the respective conventional models. The implant design tested associated with the surgical protocol, positively influenced primary stability in higher density bones.

RESUMO O objetivo deste relato de caso foi descrever uma reabilitação protética associada a um modelo alternativo de cápsula polimérica para sistema de fixação de overdentures implantado-retidas. Paciente procurou tratamento na clínica da Faculdade de Odontologia de Ribeirão Preto, devido falta de retenção de suas próteses totais superiores convencionais e overdenture inferior. A queixa inicialfoi clinicamente confirmada por relações intermaxilares alteradas e reabsorção severa da crista maxilar. Para restaurar a função e melhorar sua qualidade de vida, propôs-se como solução protética, a confecção de prótese fixa sobre implantes para a maxila e overdenture mandibular, com acessórios tipo bola associados a um modelo alternativo de cápsula polimérica. Esse tratamento foiproposto a fim de restabelecer as relações intermaxilares e a oclusão adequada, manter a retenção e a estabilidade da prótese. Ao final do tratamento e durante o acompanhamento de um ano do caso, o paciente relatou satisfação e melhora significativa na qualidade de vida.

ABSTRACT The aim of this case report was to describe a prosthetic rehabilitation associated with an alternative model of polymer capsule for fixation system of implant-retained overdentures. Patient sought treatment at the clinic of School of Dentistry of Ribeirão Preto, due to lack of retention of their conventional total superior prostheses and inferior overdenture. The initial complaint was clinicallyconfirmed by altered intermaxillary relationships and severe reabsorption of the maxillary crest. In order to restore the function and improve its quality of life, it was proposed a prosthetic solution including implant fixed prosthesis to maxilla and a mandibular overdenture, with ball-type attachments associated with an alternative model of polymer capsule. This treatment was proposed inorder to reestablish the intermaxillary relationships and adequate occlusion, maintain retention and stability of the prosthesis. At the end of treatment and during a one-year follow-up of the case, the patient reported satisfaction and significant improvement in quality of life.

The adhesion of biofilm on dental prostheses is a prerequisite for the occurrence of oral diseases. Objective: To assess the antimicrobial activity and the mechanical properties of an acrylic resin embedded with nanostructured silver vanadate (β-AgVO3). Material and Methods: The minimum inhibitory concentration (MIC) of β-AgVO3 was studied in relation to the species Staphylococcus aureus ATCC 25923, Streptococcus mutans ATCC 25175, Pseudomonas aeruginosa ATCC 27853, and Candida albicans ATCC 10231. The halo zone of inhibition method was performed in triplicate to determine the inhibitory effect of the modified self-curing acrylic resin Dencor Lay - Clássico®. The surface hardness and compressive strength were examined. The specimens were prepared according to the percentage of β-AgVO3 (0%-control, 0.5%, 1%, 2.5%, 5%, and 10%), with a sample size of 9x2 mm for surface hardness and antimicrobial activity tests, and 8x4 mm for the compression test. The values of the microbiologic analysis were compared and evaluated using the Kruskal-Wallis test (α=0.05); the mechanical analysis used the Shapiro-Wilk's tests, Levene's test, ANOVA (one-way), and Tukey's test (α=0.05). Results: The addition of 10% β-AgVO3 promoted antimicrobial activity against all strains. The antimicrobial effect was observed at a minimum concentration of 1% for P. aeruginosa, 2.5% for S. aureus, 5% for C. albicans, and 10% for S. mutans. Surface hardness and compressive strength increased significantly with the addition of 0.5% β-AgVO3 (p<0.05). Higher rates of the nanomaterial did not alter the mechanical properties of the resin in comparison with the control group (p>0.05). Conclusions: The incorporation of β-AgVO3 has the potential to promote antimicrobial activity in the acrylic resin. At reduced rates, it improves the mechanical properties, and, at higher rates, it does not promote changes in the control.

A influência do sistema de envelhecimento artificial acelerado (EAA) na microestrutura e nas propriedades mecânicas das resinas compostas Z250, Filtek Supreme, 4 Seasons, Herculite, P60, Tetric Ceram, Charisma e Filtek Z100 foi investigada. Os compósitos foram caracterizados por espectroscopia de infravermelho com transformada de Fourier (FTIR) e análises térmicas (calorimetria exploratória diferencial - DSC e termogravimetria - TG). A microestrutura dos materiais foi analisada por microscopia eletrônica de varredura. Os dados de dureza superficial e resistência à compressão foram registados para as resinas e os valores médios foram submetidos ao teste de Kolmogorov-Smirnov (p>0,05), ANOVA e teste de Tukey (α=0,05). Os resultados mostraram diferenças significativas entre as marcas comerciais em termos de dureza (F=86,74, p<0,0001) e resistência à compressão (F=40,31, p<0,0001), mas o EAA não afetou as propriedades (dureza superficial: F=0,39, p=0,53, resistência à compressão: F=2,82, p=0,09) de qualquer uma das resinas. FTIR, DSC e análise de TG revelou que a polimerização da resina foi completa, e não houve diferenças entre os espectros e os perfis de curva térmica dos materiais obtidos, antes e depois de EAA. TG mostrou a ausência de compostos voláteis e evidenciou uma boa estabilidade térmica até 200 °C, e quantidades similares de resíduos foram encontradas em todas as resinas avaliadas, antes e depois de EAA. O tratamento de EAA não afetou significativamente a superfície das resinas. Portanto, independentemente do tipo de resina, o EAA não influenciou a microestrutura e as propriedades mecânicas.

The aim of this study was to investigate the influence of accelerated artificial aging (AAA) on the microstructure and mechanical properties of the Filtek Z250, Filtek Supreme, 4 Seasons, Herculite, P60, Tetric Ceram, Charisma and Filtek Z100. composite resins. The composites were characterized by Fourier-transform Infrared spectroscopy (FTIR) and thermal analyses (Differential Scanning Calorimetry - DSC and Thermogravimetry - TG). The microstructure of the materials was examined by scanning electron microscopy. Surface hardness and compressive strength data of the resins were recorded and the mean values were analyzed statistically by ANOVA and Tukey's test (α=0.05). The results showed significant differences among the commercial brands for surface hardness (F=86.74, p<0.0001) and compressive strength (F=40.31, p<0.0001), but AAA did not affect the properties (surface hardness: F=0.39, p=0.53; compressive strength: F=2.82, p=0.09) of any of the composite resins. FTIR, DSC and TG analyses showed that resin polymerization was complete, and there were no differences between the spectra and thermal curve profiles of the materials obtained before and after AAA. TG confirmed the absence of volatile compounds and evidenced good thermal stability up to 200 °C, and similar amounts of residues were found in all resins evaluated before and after AAA. The AAA treatment did not significantly affect resin surface. Therefore, regardless of the resin brand, AAA did not influence the microstructure or the mechanical properties.