Abstract To evaluate the polymerization shrinkage stress and cuspal strain (CS) generated in an artificial (typodont) and in a natural tooth using different resin composites. Twenty artificial and 20 extracted natural molars were selected. Each tooth was prepared with a 4x4 mm MOD cavity. The natural and typodont teeth were divided into four experimental groups (n=10), according to the resin composite used: Filtek Z100 (3M Oral Care) and Beautifil II LS (Shofu Dental). The cavities were filled using two horizontal increments and the CS (µS) was measured by the strain gauge method. Samples were sectioned into stick-shaped specimens and the bond strength (BS) (MPa) was evaluated using a microtensile BS test. Shrinkage stress and CS were analyzed using 3D finite element analysis. No difference was found between the type of teeth for the CS as shown by the pooled averages: Natural tooth: 541.2 A; Typodont model: 591.4 A. Filtek Z100 CS values were higher than those obtained for Beautifil II LS, regardless of the type of teeth. No statistical difference was found for the BS data. Adhesive failures were more prevalent (79.9%). High shrinkage stress values were observed for Filtek Z100 resin, regardless of tooth type. The CS of typodont teeth showed a shrinkage stress effect, generated during restoration, equivalent to that of natural teeth. (CS (typodont composites 2 selected x 4x cavity n=10, n10 n n=10 , 10 (n=10) used Z Z10 3M M Care Shofu Dental. Dental . Dental) µS (µS method stickshaped stick shaped (BS MPa (MPa test D analysis averages 5412 541 541. A model 5914 591 4 591. data 79.9%. 799 79.9% 79 9 (79.9%) effect restoration n1 n=1 1 (n=10 Z1 54 59 79.9 7 (79.9% n= (n=1 5 79. (79.9 (n= (79. (n (79 (7 (

Abstract The aim of this study was to evaluate the effect of different die materials used in the indirect resin composite restorative technique on the fracture resistance and failure mode of restored molars and compare it with the direct resin composite restorative technique. Two flexible die silicone materials for dental models (Die Silicone – Voco and Scan die – Yller) and a type IV dental stone material (Fujirock EP – GC) were evaluated. Sixty third molars were selected and divided into four groups: indirect resin composite restoration – Die silicone (IRCR-DS); indirect resin composite restoration – Scan die (IRCR-SD); indirect resin composite restoration – Fujirock EP (IRCR-FR), and direct resin composite restoration (DRCR). Class II MOD cavities were prepared with 5 mm of buccolingual width and depth. The specimens were restored and subjected to an axial compression load until fracture, and the data were analyzed by one-way ANOVA and Tukey’s HSD test (α=.05). The fracture mode was classified into restorable and unrestorable fractures. Fracture resistance values were influenced by the die material used for the IRCR fabrication and by the restorative technique (p<.001). Fracture resistance mean values and standard deviation were: IRCR-DS: 1835.5 ± 324.0 A; IRCR-SD: 1732.5 ± 384.1 AB; IRCR-FR: 1419.3 ± 318.8 BC; and DRCR: 1100.6 ± 224.9 C. Restorable fracture was more prevalent. IRCR with flexible die casts promoted higher fracture resistance and lower prevalence of unrestorable fractures. Yller GC evaluated groups IRCRDS DS (IRCR-DS) IRCRSD SD (IRCR-SD) IRCRFR, IRCRFR FR , (IRCR-FR) DRCR. DRCR . (DRCR) depth oneway one way Tukeys Tukey s α=.05. α05 α α=.05 05 (α=.05) fractures p<.001. p001 p p<.001 001 (p<.001) IRCR-DS 18355 1835 1835. 3240 324 0 324. A IRCR-SD 17325 1732 1732. 3841 384 1 384. AB IRCR-FR 14193 1419 3 1419. 3188 318 8 318. BC 11006 1100 6 1100. 2249 224 9 224. C prevalent (IRCR-DS (IRCR-SD (IRCR-FR (DRCR α0 α=.0 (α=.05 p00 p<.00 00 (p<.001 183 32 173 38 141 31 110 22 α=. (α=.0 p0 p<.0 (p<.00 18 17 14 11 2 α= (α=. p<. (p<.0 (α= p< (p<. (α (p< (p

Abstract This study evaluated the optical method for measuring free total shrinkage using a Digital Single Lens Reflex (DSLR) camera. Eight composites were evaluated, conventional, bulk fill and low-shrinkage: Z100 (3M Oral Care), Gradia Direct Anterior (GC corporation), Spectra Smart (Dentsply), Filtek Z350 XT (3M Oral Care), Aura Bulk Fill (SDI), Vittra APS (FGM), Opus Bulk Fill APS (FGM), and Beautifil II LS (Shofu Inc.). The samples (6 mm diameter and 1.5 mm thick, n = 10) were placed on a polyvinylsiloxane impression material. An image of the uncured sample was captured using a DSLR camera with 105 mm macro lens and a ring flash. Samples were light cured with a 700 mW/cm2 LED light-cure unit for 40s. Post-polymerization images were captured at 2, 10 and 60 min. Projected circumferential areas of the specimens were drawn using the ImageJ software. Volumetric total shrinkage was calculated from the ratio of the areas obtained from pre- and post-curing. Results were analyzed using One-way ANOVA (α = 0.05) and Tukey test. Volumetric total shrinkage values were significantly different among the composite materials (p < .001). The volumetric shrinkage (%) mean and results of Tukey test at 60 min were: Z100: 3.45±0.30 (A); Gradia Direct Anterior: 3.00 ± 0.23 (B); Spectra Smart 2.89 ± 0.35 (B); Filtek Z350 XT: 2.65 ± 0.37 (BC); Aura Bulk Fill: 2.42 ± 0.25 (CD); Vittra APS: 2.14 ± 0.35 (DE); Opus Bulk Fill APS: 1.91 ± 0.24 (E); Beautifil II LS: 1.18 ± 0.16 (F). The optical method using a DSLR camera, was suitable for total shrinkage evaluation and will allow assessment of total shrinkage without the need for specialized equipment.

Resumo O objetivo deste estudo foi analisar a influência da presença e tipo de bráquete ortodôntico (metálico ou cerâmico), e a presença de protetor bucal na resposta biomecânica durante impacto. Modelos bidimensionais em estado plano de deformação de paciente com incisivo central superior com overjet positivo acentuado foram criados baseados em tomografia computadorizada, simulando ligamento periodontal, suporte ósseo, tecido gengival, bráquetes ortodônticos (metálico e cerâmico) e o protetor bucal. Análise de elementos finitos não-linear de impacto foi realizada na qual uma esfera de aço atingiu o modelo a 1m/s. A distribuição de tensões (Von Mises e Von Mises modificado) e a deformação foram avaliadas. As distribuições de tensões foram afetadas pela presença e tipo de bráquete. Modelos com bráquete metálico e cerâmico produziram maiores valores de tensões sobre maior área do esmalte vestibular. Modelos com bráquetes cerâmicos geraram maiores tensões do que metálicos. O protetor bucal reduziu as tensões e deformações geradas independentemente do tipo de bráquete. A capacidade de absorção de choques foi de 88.37 e 89.27% para os bráquetes metálicos e cerâmicos, respectivamente. A presença e o tipo de bráquete influenciou a distribuição de tensões e deformações durante o impacto. Bráquetes cerâmicos geraram maiores valores de tensão do que metálicos. Protetor bucal reduziu significativamente os picos de tensão e deformação.

Abstract The aim of this study was to analyze the influence of orthodontic bracket type (metallic or ceramic) and mouthguard on biomechanical response during impact. Two-dimensional plane-strain models of a patient with increased positive overjet of the maxillary central incisor was created based on a CT scan, simulating the periodontal ligament, bone support, gingival tissue, orthodontic brackets (metallic or ceramic) and mouthguard. A nonlinear dynamic impact finite element analysis was performed in which a steel object hit the model at 1 m/s. Stress distributions (Von Mises and Modified Von Mises) and strain were evaluated. Stress distributions were affected by the bracket presence and type. Models with metallic and ceramic bracket had higher stresses over a larger buccal enamel impact area. Models with ceramic brackets generated higher stresses than the metallic brackets. Mouthguards reduced the stress and strain values regardless of bracket type. Mouthguard shock absorption were 88.37% and 89.27% for the metallic and ceramic bracket, respectively. Orthodontic bracket presence and type influenced the stress and strain generated during an impact. Ceramic brackets generated higher stresses than metallic brackets. Mouthguards substantially reduced impact stress and strain peaks, regardless of bracket type.

Resumo O objetivo foi avaliar a resistência de união à microtração (RUμT) à dentina e o estresse interfacial em cavidades classe II restauradas com resina composta de incremento único ou convencional e as interfaces marginais. Cavidades classe II na face mesial, com margem gengival em dentina, foram confeccionadas em 72 terceiros molares, sendo divididos em grupos (n=24): Grupo 1-Tetric N-Ceram; Grupo 2- Tetric N-Ceram Bulk-Fill; Grupo 3- SonicFill. O Sistema adesivo Clearfil SE Bond foi usado em todos os grupos. Metade dos dentes de cada grupo (n=12) foram submetidos à ciclagem termo-mecânica (CTM). Os dentes restaurados (n=9) foram cortados perpendicularmente para obter palitos que foram submetidos ao teste de RµT na máquina-EMIC. As margens cervicais em dentina dos dentes restaurados (n=3) foram observados em microscopia eletrônica de varredura (MEV) por meio de réplicas em resina epoxy, assim como os cortes das restaurações. O estresse interfacial após a aplicação da carga foram calculadas por análise de elementos finitos 2D. As médias de RUμT-MPa seguidas de letras distintas apresentam diferença estatística de acordo com ANOVA e teste de Games-Howell (p<0,05): Antes da CTM: G1-15.68±6.10a; G2-10.08±5.21ab; G3-7.98±3.76b. Após CTM: G1-9.70±5.52a; G2-5.79±1.42a; G3-4.37±1.87a. O estresse interfacial (MPa) foi 4,4 para SonicFill, 3,9 para Tetric N-Ceram e 3,5 para Tetric N-Ceram Bulk-Fill. Imagens em MEV mostraram margens contínuas para todas as restaurações em resina composta. Foi possível concluir que o SonicFill obteve um estresse interfacial ligeiramente mais alto e menor resistência de união à dentina em comparação com o Tetric N-Ceram e o Tetric N-Ceram Bulk-Fill. Interfaces de margem contínua foram obtidas para Tetric N-Ceram, Tetric N-Ceram Bulk-Fill e SonicFill. Entretanto, espaços vazios foram observados nas restaurações do SonicFill.

Abstract The aim was to evaluate the microtensile bond strength (mTBS) to dentin and interfacial stress in a class II cavity restored with bulk-fill or conventional composite resins and the margin interfaces. Vertical slot class II cavities in the mesial face, with the gingival end in dentin, were prepared in 72 third molars, being divided into groups (n=24): G1-Tetric N-Ceram; G2-Tetric N-Ceram Bulk-Fill; G3-SonicFill. Clearfil SE Bond adhesive system was used in all groups. Half of the teeth in each group (n=12) were submitted to thermo-mechanical cycling (TMC). Restored teeth (n=9) were cut perpendicular to obtain beams, which were submitted to a mTBS test in an EMIC machine. The cervical margins in dentin of the restored teeth (n=3) were assessed using SEM through epoxy resin replicas as well as the section of the restoration. Interfacial stresses after load application were calculated by 2D finite element analysis. The mTBS means-MPa followed by different letters represent statistical difference by ANOVA and Games-Howell’s test (p<0.05): Without TMC: G1-15.68±6.10a; G2-10.08±5.21ab; G3-7.98±3.76b. With TMC: G1-9.70±5.52a; G2-5.79±1.42a; G3-4.37±1.87a. Interfacial stress (MPa) was 4.4 for SonicFill, 3.9 for Tetric N-Ceram, and 3.5 for Tetric N-Ceram Bulk-Fill. SEM images showed continuous margins for all composite resin restorations. It was possible to conclude that SonicFill obtained a slightly higher interfacial stress and lower bond strength to dentin in comparison with Tetric N-Ceram and Tetric N-Ceram Bulk-Fill. Continuous margin interfaces were obtained for Tetric N-Ceram, Tetric N-Ceram Bulk-Fill, and SonicFill. However, voids were observed in the SonicFill restorations.

Abstract: Endodontic treatment is a common dental procedure used for treating teeth which the pulp tissue has become irreversibly inflamed or necrotic as a result of the carious process or dental trauma. This procedure which involves mechanical and chemical preparation of root canal may affect several mechanical and physical properties of the tooth structure. The endodontic treatment can also influence the longevity of the rehabilitation of endodontically treated teeth and biomechanics during the oral function. For restoring endodontically treated teeth several factor and clinical decisions should be observed. The decision of the fiberglass post usage and the restorative materials are related to several factors such as the quantity and quality of remaining dental structure, presence of ferrule, post cementation length and final coronal restoration. In this review, the authors will address the effect of the endodontic treatment procedures on canal shape and mechanical properties of a tooth, and also discuss the parameters and the biomechanical principles of root canal treated teeth.

Resumo O objetivo deste estudo foi avaliar o efeito da integridade do cimento resinoso autoadesivo, expresso pela presença de bolhas, sobre a distribuição de tensão, resistência adesiva e modo de falha de pinos de fibra cimentados à dentina radicular humana. Dez incisivos centrais superiores humanos com canais radiculares circulares foram selecionados. Os mesmos foram seccionados com 15 mm e tratados endodonticamente. As raízes foram digitalizadas utilizando micro-CT após preparo do pino para avaliação de remanescentes de material obturador. Pinos de fibra foram cimentados utilizando cimento autoadesivo (Rely X U200, 3M-ESPE). Duas fatias de 1 mm de espessura dos terços cervical, médio e apical foram escaneados para mensuração do volume de bolhas no cimento resinoso e submetidos ao teste de push-out. Três operadores classificaram o modo de falha utilizando microscopia confocal à laser e lupa estereoscópica. Distribuição de tensão foi analisada pelo método de elementos finitos 3D. Os valores de resistência adesiva (MPa) foram submetidos ao teste ANOVA em fator único seguido do teste de Tukey. Foi utilizado o coeficiente de Kappa para avaliar a concordância entre operadores. O teste Qui-quadrado foi utilizado para determinar diferenças significativas entre os métodos (α=0,05). A resistência adesiva foi significativamente afetada pela presença de bolhas independentemente da profundidade radicular (p<0,05). A concentração de tensão foi maior na presença de bolhas. Maior frequência de falha adesiva ocorreu na interface cimento/dentina. A microscopia confocal foi melhor do que estereomicroscopia para análise de falhas. A presença de bolhas afetou negativamente a distribuição de tensão e a resistência de união. Recomenda-se uso de microscopia confocal para análise de falhas.

The aim of this study was to evaluate the effect of porosity of self-adhesive resin on the stress distribution, post retention and failure mode of fiber post cemented to human root dentin. Ten human central upper incisors with circular root canal were selected. They were sectioned with 15 mm and were endodontically filled. The roots were scanned using micro-CT after post space preparation for root filling remaining evaluation. Fiber posts were cemented using self-adhesive resin cement (Rely X U200, 3M-ESPE). Two 1-mm-thick slices from the cervical, medium and apical thirds were scanned for resin cement bubbles volume measurements and submitted to a push-out test (PBS). Three operators using stereomicroscopy and confocal laser microscopy classified the failure mode. Stress distributions during the push-out test were analyzed using 3D finite element analysis. PBS values (MPa) were submitted to one-way ANOVA and Tukey's post hoc tests and the failure modes using the Kappa coefficient to assess inter-operator agreement. Chi-square test was used to determine significant differences between the methods ( = 0.05). Push-out bond strength was significantly affected by the bubbles presence in all root depth (p<0.05). The stress concentration was higher when the bubbles were present. Adhesive dentin/resin cement interface failure was the most frequent type of failure. Confocal microscopy was better than stereomicroscopy for failure analysis. Bubbles generated during resin cement insertion into the root canal negatively affect the stress distribution and the bond strength. The use of confocal microscopy is recommended for failure analysis.

The aim of this study was to evaluate the amount of deformation from compression caused by different diameters of Morse taper implants and the residual deformation after load removal. Thirty Morse taper implants lacking external threads were divided into 3 groups (n = 10) according to their diameter as follows: 3.5 mm, 4.0 mm and 5.0 mm. Two-piece abutments were fixed into the implants, and the samples were subjected to compressive axial loading up to 1500 N of force. During the test, one strain gauge remained fixed to the cervical portion of each implant to measure the strain variation. The strain values were recorded at two different time points: at the maximum load (1500 N) and 60 seconds after load removal. To calculate the strain at the implant/abutment interface, a mathematical formula was applied. Data were analyzed using a one-way Anova and Tukey’s test (α = 0.05). The 5.0 mm diameter implant showed a significantly lower strain (650.5 μS ± 170.0) than the 4.0 mm group (1170.2 μS ± 374.7) and the 3.5 mm group (1388.1 μS ± 326.6) (p < 0.001), regardless of the load presence. The strain values decreased by approximately 50% after removal of the load, regardless of the implant diameter. The 5.0 mm implant showed a significantly lower strain at the implant/abutment interface (943.4 μS ± 504.5) than the 4.0 mm group (1057.4 μS ± 681.3) and the 3.5 mm group (1159.6 μS ± 425.9) (p < 0.001). According to the results of this study, the diameter influenced the strain around the internal and external walls of the cervical region of Morse taper implants; all diameters demonstrated clinically acceptable values of strain.