Abstract This study assessed the physicochemical and antibiofilm properties of white mineral trioxide aggregate (MTA) associated with 1 or 2% of farnesol. Setting time was evaluated based on ISO 6876/2012. Radiopacity was evaluated by radiographic analysis. pH was assessed after time intervals of 1, 3, 7, 14, 21, and 28 days. Solubility (% mass loss) and volumetric change (by micro-CT) of the cements were evaluated after immersion in distilled water. The presence of voids inside the materials was assessed by using micro-CT. Antibiofilm activity against Enterococcus faecalis was evaluated by crystal violet assay and the modified direct contact test performed with biofilm previously formed on bovine root dentin for 14 days. Data were submitted to ANOVA/Tukey tests with 5% significance level. The incorporation of farnesol into MTA increased its setting time, but decreased its solubility at 30 days and its volumetric loss in all periods (p < 0.05). Radiopacity and solubility after 7 days were similar among the materials (p > 0.05). The association of farnesol showed the highest pH value after 1 and 3 days (p < 0.05). The association of farnesol with MTA promoted a decrease in the presence of voids, and increased the antimicrobial activity on biofilm biomass of E. faecalis (p < 0.05). In conclusion, the addition of farnesol can be suggested to improve the antimicrobial properties and the consistency of MTA. (MTA 2 68762012 6876 2012 6876/2012 analysis 21 % ( microCT micro CT micro-CT water microCT. CT. ANOVATukey ANOVA Tukey 5 level p 0.05. 005 0.05 . 0 05 0.05) E conclusion 6876201 687 201 6876/201 00 0.0 687620 68 20 6876/20 0. 68762 6 6876/2 6876/

Abstract Both root canal sealer-based and supplementary protocols may influence removal of filling material during endodontic retreatment. Mesial root canals of extracted mandibular molars were prepared using HyFlex EDM 25/.08, and filled with a calcium silicate sealer (Bio-C Sealer), or an epoxy resin (AH Plus), using the single cone technique (n = 12). Retreatment was performed using ProDesign Logic (PDL) RT and PDL 35/.05. The specimens were randomly divided into two experimental groups (n = 12), and the sealers were distributed similarly. A supplementary protocol was performed with PDL 50/.01 or XP-endo Finisher. Root canal transportation and volume, in addition to the remaining filling material percentage were evaluated using high-resolution (5 µm voxel size) micro-CT. Statistical analysis was performed using t-tests (α = 0.05). Root canals filled with AH Plus presented high residual filling material (p < 0.05). Both protocols decreased residual volume of filling material in the apical third (p < 0.05). PDL 50/.01 increased the apical root canal volume (p < 0.05). No difference was observed between the systems regarding canal transportation (p > 0.05). In conclusion, AH Plus is more difficult to remove from the apical third than Bio-C Sealer. PDL 50/.01 and XP-endo Finisher enabled greater removal of filling materials in the apical third, in the retreatment of curved root canals, without promoting apical transport. sealerbased based 2508 25 08 25/.08 BioC Bio C Sealer, Sealer , Sealer) Plus, Plus) n 12. 12 . 12) (PDL 3505 35 05 35/.05 12, similarly 5001 50 01 50/.0 XPendo XP endo highresolution resolution 5 ( size microCT. microCT micro CT. CT micro-CT ttests t tests α 0.05. 005 0.05 0 0.05) p conclusion transport 250 2 25/.0 1 350 3 35/.0 500 50/. 00 0.0 25/. 35/. 50/ 0. 25/ 35/

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas, citotoxicidade e bioatividade de um novo material biocerâmico pronto para uso, Bio-C Repair (Angelus), em comparação com MTA Branco (Angelus) e Biodentine (Septodont). Foram avaliadas as propriedades físico-químicas de tempo de presa, radiopacidade, pH, solubilidade, alterações dimensionais e volumétricas. A biocompatibilidade, bioatividade e capacidade de reparo foram avaliadas em culturas de células de osteoblastos Saos-2 pelo ensaio MTT brometo de 3-(4,5-dimetiltiazol-2-il)-2,5-difeniltetrazólio), vermelho neutro (NR), vermelho de alizarina ( ARS) e testes de migração celular. A análise estatística foi realizada pelos testes ANOVA, Tukey ou Bonferroni (α = 0,05). Bio-C Repair apresentou o maior tempo de presa (p < 0,05), mas radiopacidade e solubilidade de acordo com as normas ISO 6876/2012, além de expansão linear. Bio-C Repair e MTA tiveram variação volumétrica semelhante (p > 0,05), menor que Biodentine (p < 0,05). Todos os materiais avaliados apresentaram pH alcalino. Bio-C Repair foi citocompatível, além de promover deposição de nódulos mineralizados em 21 dias e migração celular em 3 dias. Em conclusão, o Bio-C Repair apresentou radiopacidade adequada acima de 3mmAl, solubilidade menor que 3%, expansão dimensional e baixa perda volumétrica.. Além disso, o Bio-C Repair promoveu um pH alcalino e apresentou bioatividade e biocompatibilidade semelhantes ao MTA e Biodentine, mostrando potencial para uso como material reparador físicoquímicas, físicoquímicas físico químicas, químicas BioC Bio C Angelus, Angelus , (Angelus Septodont. Septodont . (Septodont) volumétricas Saos2 Saos 2 Saos- 34,5dimetiltiazol2il2,5difeniltetrazólio, 345dimetiltiazol2il25difeniltetrazólio dimetiltiazolildifeniltetrazólio 4,5 dimetiltiazol il 2,5 difeniltetrazólio 4 5 3-(4,5-dimetiltiazol-2-il)-2,5-difeniltetrazólio) NR, NR (NR) ARS ANOVA α 0,05. 005 0,05 0 05 0,05) p 0,05, 68762012 6876 2012 6876/2012 linear citocompatível conclusão 3mmAl mmAl 3% volumétrica. disso (Septodont 34 5dimetiltiazol2il2 5difeniltetrazólio 34,5dimetiltiazol2il2,5difeniltetrazólio 45 4, 25 2, 3-(4,5-dimetiltiazol-2-il)-2,5-difeniltetrazólio (NR 00 0,0 6876201 687 201 6876/201 dimetiltiazolil 5dimetiltiazol2il 0, 687620 68 20 6876/20 68762 6 6876/2 6876/

Abstract The aim of this study was to evaluate the physicochemical properties, cytotoxicity and bioactivity of a ready-to-use bioceramic material, Bio-C Repair (Angelus), in comparison with White MTA (Angelus) and Biodentine (Septodont). The physicochemical properties of setting time, radiopacity, pH, solubility, dimensional and volumetric changes were evaluated. Biocompatibility and bioactivity were assessed in Saos-2 osteoblast cell cultures by the MTT assay 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), Neutral Red (NR), Alizarin Red (ARS), and cell migration tests. Statistical analysis was performed by ANOVA, Tukey or Bonferroni tests (α = 0.05). Bio-C Repair had the longest setting time (p < 0.05), but radiopacity and solubility were accordance with the ISO 6876/2012 standards, besides linear expansion. Bio-C Repair and MTA had similar volumetric change (p > 0.05); lower than Biodentine (p < 0.05). All the materials evaluated had an alkaline pH. Bio-C Repair was cytocompatible and promoted mineralized nodule deposition in 21 days and cell migration in 3 days. In conclusion, Bio-C Repair had adequate radiopacity above 3mm Al, solubility less than 3%, dimensional expansion, and low volumetric change. In addition, Bio-C Repair promoted an alkaline pH and presented bioactivity and biocompatibility similar to MTA and Biodentine, showing potential for use as a repair material. readytouse ready material BioC Bio C Angelus, Angelus , (Angelus Septodont. Septodont . (Septodont) Saos2 Saos 2 Saos- 34,5Dimethylthiazol2yl2,5diphenyltetrazolium 345Dimethylthiazol2yl25diphenyltetrazolium Dimethylthiazolyldiphenyltetrazolium 4,5 Dimethylthiazol yl 2,5 diphenyltetrazolium 4 5 bromide, bromide bromide) NR, NR (NR) ARS, ARS (ARS) ANOVA α 0.05. 005 0.05 0 05 0.05) p 0.05, 68762012 6876 2012 6876/201 standards expansion conclusion mm Al 3% addition (Septodont 34 5Dimethylthiazol2yl2 5diphenyltetrazolium 45 4, 25 2, (NR (ARS 00 0.0 6876201 687 201 6876/20 Dimethylthiazolyl 5Dimethylthiazol2yl 0. 687620 68 20 6876/2 68762 6 6876/

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas, a citocompatibilidade e a atividade antibiofilme de um novo cimento endodôntico à base de silicato de cálcio, Sealer Plus BC (MK Life, Brasil), em comparação com TotalFill BC Sealer (FKG Dentaire SA, Suíça) e AH Plus (Dentsply, Alemanha). O tempo de presa e o escoamento foram avaliados com base nas normas ISO 6876. O pH foi avaliado após diferentes períodos, e a radiopacidade por análise radiográfica (mmAl). A solubilidade (% de perda de massa) e alteração volumétrica (por micro-CT) foram avaliadas após 30 dias de imersão em água destilada. Citocompatibilidade foi avaliada pelos ensaios metiltetrazólio (MTT) e vermelho neutro (NR), após exposição das células Saos-2 ao extrato de cimento por 24 horas. Análise adicional foi realizada através do ensaio MTT após 1, 3 e 7 dias de exposição das células Saos-2 aos extratos dos cimentos na diluição de 1:8. Atividade antibiofilme contra Enterococcus faecalis e/ou Candida albicans foi avaliada pelos ensaios cristal violeta e contato direto modificado. As propriedades físico-químicas foram analisadas utilizando os testes ANOVA e Tukey; MTT e NR foram analisados pelos testes ANOVA e Bonferroni; os ensaios antimicrobianos foram analisados pelos testes Kruskal-Wallis e Dunn (α=0.05). Sealer Plus BC apresentou tempo de presa, radiopacidade e escoamento adequados, além de capacidade de alcalinização. Sealer Plus BC foi significantemente mais solúvel que AH Plus (p<0.05) e apresentou alteração volumétrica similar à de AH Plus e TotalFill BC (p>0.05). Sealer Plus BC apresentou atividade antibiofilme, sem efeito citotóxico. Como conclusão, embora Sealer Plus BC apresente maior solubilidade, este cimento apresentou propriedades físico-químicas adequadas, citocompatibilidade e atividade antibiofilme.

Abstract The aim of this study was to evaluate the physicochemical properties, cytocompatibility and antibiofilm activity of a new calcium silicate-based endodontic sealer, Sealer Plus BC (MK Life, Brazil), in comparison with TotalFill BC Sealer (FKG Dentaire SA, Switzerland) and AH Plus (Dentsply, Germany). Setting time and flow were evaluated based on ISO 6876 standard. The pH was evaluated after different periods, and radiopacity by radiographic analysis (mmAl). Solubility (% mass loss) and volumetric change (by micro-CT) were assessed after 30 days of immersion in distilled water. Cytocompatibility was assessed by methyltetrazolium (MTT) and neutral red (NR) assays, after exposure of Saos-2 cells to the sealer extract for 24 h. An additional analysis was performed by using MTT assay after 1, 3 and 7 days of exposure of Saos-2 to the sealers 1:8 dilution extracts. Antibiofilm activity against Enterococcus faecalis and/or Candida albicans was evaluated by crystal violet assay and modified direct contact test. The physicochemical properties were analyzed using ANOVA/Tukey tests; MTT and NR data were analyzed by ANOVA and Bonferroni tests; the antimicrobial tests were analyzed by Kruskal-Wallis and Dunn tests (α=0.05). Sealer Plus BC had proper setting time, radiopacity, flow and alkalization capacity. Sealer Plus BC was significantly more soluble than AH Plus (p<0.05) and presented volumetric change similar to AH Plus and TotalFill BC (p>0.05). Sealer Plus BC presented antibiofilm activity and no cytotoxic effect. In conclusion, although Sealer Plus BC had higher solubility, this sealer showed proper physicochemical properties, cytocompatibility, and antibiofilm activity.

Resumo Novas metodologias utilizando micro-CT são propostas para avaliar a solubilidade além de alterações dimensionais e morfológicas em materiais endodônticos. No entanto, não há padronização nos métodos. O objetivo deste estudo foi avaliar o efeito de diferentes dimensões de corpos de prova na avaliação da alteração volumétrica de diferentes materiais endodônticos. Os cimentos obturadores AH Plus, FillCanal e Sealapex e os cimentos retrobturadores Biodentine, IRM e MTA foram utilizados nos testes. Foram confeccionadas amostras de cada material com espessura de 1.5 mm e diâmetros diferentes: 6.3, 7.75 e 9.0 mm. As amostras foram escaneadas em microtomografia computadorizada (micro-CT) após a presa e após 7 dias de imersão em água destilada. A alteração volumétrica foi avaliada por meio da diferença no volume total dos corpos de prova antes e após a imersão. Os dados foram submetidos aos testes ANOVA e Tukey (p<0,05). A dimensão das amostras não afetou o percentual de alteração volumétrica dos materiais (p>0,05). Todos os diâmetros de amostra mostraram maior perda de volume para Sealapex entre os cimentos obturadores e Biodentine entre os cimentos retrobturadores (p<0,05). Como conclusão, Biodentine e Sealapex mostraram a maior perda volumétrica após a imersão. Amostras com 1.5 mm de espessura e diâmetros variando entre 6.3 e 9.0 mm podem ser usadas para avaliação da estabilidade de materiais endodônticos utilizando micro-CT, sem influenciar no percentual de alteração volumétrica.

Abstract New methodologies using micro-CT to evaluate solubility besides dimensional and morphological changes of endodontic materials are proposed. However, there is no standardization in the methods. The aim of this study was to assess the effect of different dimensions of test samples on volumetric change evaluation of different endodontic materials. AH Plus, FillCanal and Sealapex root canal sealers, Biodentine, IRM and MTA root-end filling cements were used in the tests. Samples of each material with a thickness of 1.5 mm and different diameters were manufactured: 6.3, 7.75, and 9.0 mm. The samples were scanned in micro-computed tomography (micro-CT) after setting and after 7 days of immersion in distilled water. The volumetric change was evaluated by means of the difference in the total volume of the specimens before and after immersion. Data were submitted to ANOVA and Tukey tests (p<0.05). The size of the samples did not affect the percentage of volumetric change of the materials (p>0.05). All sample sizes had greater volume loss for Sealapex among the sealers and Biodentine for the cements (p<0.05). In conclusion, Biodentine and Sealapex had the highest volume loss after immersion. Samples with 1.5 mm thickness, and diameters ranging between 6.3 and 9.0 mm can be used to assess the stability of endodontic materials using micro-CT without affecting the percentage of volumetric change.

Abstract The aim of this study was to assess the influence of micro-computed tomography (micro-CT) voxel size on dentinal microcrack detection after root canal preparation using rotary heat-treated nickel-titanium files. Curved mesial root canals (n = 24) of mandibular molars were prepared using ProDesign Logic 30/.05 (PDL) or HyFlex EDM 25/.08 (HEDM). The specimens were scanned by micro-CT at 5 μm voxel size before and after root canal preparation. The percentage of microcracks was evaluated in images at 5, 10 and 20 μm voxel size, by two examiners at two moments. The Kappa and McNemar tests (α = 0.05) were used. The percentage of dentinal microcracks was similar before and after PDL and HEDM preparations, at 10 and 20 μm (p > 0.05). HEDM showed a higher percentage of dentinal microcracks in the middle third at 5 μm after preparation (p < 0.05). The detection of dentinal microcracks before and after instrumentation using PDL was more accurate at 5 μm than at 20 μm, in all thirds (p < 0.05). Within the limitations of this ex vivo study, as expected, the results showed that different resolutions influence the micro-CT analysis of microcracks. The highest accuracy in detecting microcracks was observed for analyses performed at 5 μm voxel size. HyFlex EDM caused even more microcracks to develop in the middle third, detectable only by visualization of images made at 5 μm voxel size.

Abstract The aim of this study was to evaluate the filling ability of a new ready-to-use calcium silicate-based sealer using thermoplastic or single-cone technique in flattened root canals. Twenty-four flattened distal canals of mandibular molars with a buccolingual diameter 4 or more times larger than the mesiodistal diameter were selected. The root canals were prepared and filled (n = 12), according to the following techniques: thermoplastic or single-cone technique using Bio-C Sealer. The teeth were scanned using Skycan 1176 micro-computed tomography (micro-CT) - voxel size 8.74 µm, before and after filling the root canal. The percentage of voids in the filled root canals was evaluated, and the data were statistically analyzed using the unpaired t-test (α = 0.05). The root canals filled using the thermoplastic technique created a smaller percentage of voids in the cervical/middle thirds than those filled using the single-cone technique (p < 0.05). There was no difference in the percentage of voids using either technique in the apical third (p > 0.05). The flattened root canals in the cervical/middle thirds were better filled using the ready-to-use calcium silicate-based sealer associated to the thermoplastic technique, compared with the single-cone technique. In the apical third, the techniques showed similar filling ability.

Abstract The aim of this study was to evaluate physicochemical properties of calcium silicate-based experimental (CS) endodontic sealers, developed using two different vehicles: polyethylene glycol (PG) (CS-PG) or polyethylene glycol associated to chitosan hydrogel (CS-PGCH). TotalFill BC Sealer (TF) and AH Plus (AHP) were evaluated for comparison. Setting time, flow, radiopacity, pH, solubility and volumetric change were analyzed. Data were submitted to ANOVA and Tukey tests with 5% significance level. The CS-PGCH had significantly greater setting time. CS-PG flow was similar to AHP. CS-PG had higher radiopacity than CS-PGCH. Calcium silicate-based sealers presented alkaline pH in all periods. CS-PGCH presented higher solubility in comparison with CS-PG. The volumetric change of CS-PG was similar to TF after 7 days, and to AHP after 30 days. CS-PG presented proper setting time, radiopacity, flow and pH, besides low volumetric change, showing better results than CS-PGCH, and potential for clinical application.

Abstract: The aim of this study was to assess the influence of micro-computed tomography (micro-CT) voxel size on the evaluation of debris accumulation after passive ultrasonic irrigation (PUI) in curved root canals prepared with rotary nickel-titanium files. Mesial root canals (n = 24) of mandibular molars with curvature between 25° and 35° were prepared using ProDesign Logic 30/.05 (PDL) or HyFlex EDM 25/.08 (HEDM). PUI was performed after root canal preparation of all root canals. The specimens were scanned using high-resolution (5 μm voxel size) micro-CT imaging before and after experimental procedures. The percentage of debris was analyzed in the middle and apical thirds using images with 5, 10 and 20 μm voxel sizes. Data were compared using unpaired and paired Student's t-test, ANOVA and Tukey's statistical tests (α = 0.05). There were no differences among the debris analyses performed at different voxel sizes (5, 10 and 20 μm) (p > 0.05). The percentage of debris was similar between the root canals prepared by PDL and HEDM before and after PUI (p > 0.05). In both groups, the percentage of debris decreased in the middle third after PUI (p < 0.05). Within the limitations of this ex vivo study, it can be concluded that the voxel sizes evaluated did not have a significant impact on the analysis of accumulated debris. However, the results showed a tendency for detection of more debris in the analysis performed using a lower voxel size. PUI decreased the debris accumulation in the middle third of curved root canals.

Resumo Este estudo avaliou por microtomografia computadorizada (μCT) a capacidade de preenchimento de canais radiculares curvos, além do escoamento dos cimentos AH Plus (AHP) e Neo MTA Plus (NMTAP) utilizando diferentes metodologias. Foram selecionadas raízes mesiais de molares inferiores com dois canais radiculares e grau de curvatura entre 20° e 40°. As amostras foram preparadas com o sistema ProDesign R até o tamanho 35.05 e foram obturadas com os cimentos por uma técnica de onda contínua de condensação, Thermo Pack II (n=12). Os dentes foram escaneados usando μCT após o preparo e obturação do canal radicular. A porcentagem volumétrica de material de preenchimento e vazios foram calculados. O escoamento foi avaliado com base na norma ISO 6876/2012 (n=10). O escoamento e o preenchimento também foram avaliados em μCT usando uma placa de vidro com uma cavidade central e quatro canaletas a partir da cavidade central (n=6). O escoamento foi calculado linearmente nas canaletas. O preenchimento da cavidade central (PCC) e o preenchimento da cavidade lateral (PCL) foram calculados em mm³. Os dados foram submetidos ao teste t não pareado com nível de significância de 5%. A porcentagem de preenchimento e vazios entre os canais radiculares preenchidos com AHP ou NMTAP foi semelhante (p>0,05). NMTAP apresentou o menor escoamento no teste convencional (p<0,05). Utilizando μCT, os cimentos apresentaram PCC, PCL e escoamento linear semelhantes (p>0,05). Em conclusão, NMTAP e AHP apresentaram capacidade de preenchimento semelhante em canais mesiais curvos de molares inferiores sem presença de istmo. Embora o AHP tenha apresentado melhor escoamento que o NMTAP usando a metodologia ISO, não houve diferença entre esses materiais em relação ao preenchimento volumétrico quando avaliados por μCT.

Abstract This study evaluated by micro-computed tomography (μCT) the filling ability in curved root canals, besides the flow of AH Plus (AHP) and Neo MTA Plus (NMTAP) sealers using different methodologies. Mandibular molars mesial roots with two root canals and degree of curvature between 20° and 40° were selected. The specimens were prepared with the ProDesign R system up to size 35.05 and were filled with the sealers by a continuous wave of condensation technique, Thermo Pack II (n=12). The teeth were scanned using μCT after root canal preparation and obturation. The volumetric percentage of filling material and voids were calculated. Flow was evaluated based on ISO 6876/2012 (n=10). Flow and filling were also evaluated in μCT using a glass plate with a central cavity and four grooves from the central cavity (n=6). Flow was linearly calculated into the grooves. The central cavity filling (CCF) and lateral cavity filling (LCF) were calculated in mm³. Data were submitted to non-paired t test with a significance threshold at 5%. The percentage of filling and voids between the root canals filled with AHP or NMTAP was similar (p>0.05). NMTAP presented the lowest flow in conventional test (p<0.05). Using μCT, sealers had similar CCF, LCF and linear flow (p>0.05). In conclusion, NMTAP and AHP had similar filling ability in curved mesial root canals of mandibular molars without presence of isthmus. Although AHP presented better flow than NMTAP using ISO methodology, there was no difference between these materials regarding volumetric filling when evaluated by μCT.

Abstract Dental materials should be stable over time. This study investigated volumetric change of the root canal sealers AH Plus, Fill Canal, and Sealapex; and the root-end filling materials Biodentine, IRM, and MTA after different periods of immersion in distilled water. Resin models were manufactured with cavities 3 mm deep. The cavities were filled with the materials and scanned by microcomputed tomography after setting, and after 7 and 30 days immersed in distilled water. Percentages of volumetric changes after 7 and 30 days of immersion were compared by t-test. ANOVA/Tukey tests were used to compare endodontic materials (5% significance level). All root canal sealers had an increase in their volumetric change after 30 days. Among root-end filling materials, only IRM showed difference between the periods. Biodentine showed more volumetric changes than MTA, but both materials kept their volume from 7 to 30 days. In conclusion, the immersion period of endodontic materials may affect their stability.

Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas e o potencial bioativo de Sealer Plus, em comparação com MTA Fillapex, Sealapex e AH Plus. Tempo de presa, escoamento e radiopacidade foram avaliados com base nas normas ISO 6876. O escoamento foi também avaliado em área (mm²). A solubilidade e a alteração volumétrica dos cimentos foram avaliadas após 7 e 30 dias de imersão em água destilada. A solubilidade foi analisada pela diferença entre as massas dos cimentos antes e após imersão. A alteração volumétrica foi avaliada por meio de microtomografia computadorizada (micro-CT). O potencial bioativo dos cimentos foi observado por Microscopia Eletrônica de Varredura (MEV) após imersão em PBS. Os dados foram comparados usando os testes ANOVA e Tukey (α=0.05). Sealer Plus apresentou o tempo de presa mais curto (196 min.) e Sealapex o mais longo (912 min.) (p<0.05). AH Plus mostrou a radiopacidade mais alta (9.5 mm Al) e MTA Fillapex a mais baixa (2.7 mm Al) (p<0.05). Todos os cimentos tiveram escoamento de acordo com as normas ISO 6876/2012 (>17 mm). Sealer Plus mostrou baixos valores de solubilidade e alteração volumétrica (<1%) e MTA Fillapex teve os valores mais altos de solubilidade (>25%) e alteração volumétrica (>4%) em todos os períodos avaliados (p<0.05). MTA Fillapex foi o único cimento que mostrou potencial bioativo. Como conclusão, Sealer Plus apresentou propriedades físico-químicas adequadas, entretanto, não apresentou potencial bioativo.

Abstract The aim of this study was to evaluate physicochemical properties and bioactive potential of Sealer Plus, in comparison with MTA Fillapex, Sealapex and AH Plus. Setting time, flow, and radiopacity were evaluated based on ISO 6876 Standard. Flow was also assessed in area (mm²). The solubility and volumetric change of the sealers were evaluated after 7 and 30 days of immersion in distilled water. Solubility was evaluated by the difference in mass of materials before and after immersion. Volumetric change was evaluated by using microcomputed tomography (micro-CT). The bioactive potential was observed by Scanning Electron Microscopy (SEM) after immersion in PBS. Data were compared using ANOVA and Tukey tests (α=0.05). Sealer Plus presented the shortest setting time (196 min.) and Sealapex the longest (912 min.) (p<0.05). AH Plus showed the highest radiopacity (9.5 mm Al) and MTA Fillapex the lowest (2.7 mm Al) (p<0.05). All the sealers presented flow in accordance with ISO 6876/2012 (>17 mm). Sealer Plus showed low solubility and volumetric change (<1%), and MTA Fillapex showed the highest solubility (>25%), and volumetric change (>4%) after all time intervals (p<0.05). MTA Fillapex was the only sealer that showed bioactive potential. In conclusion, Sealer Plus presented proper physicochemical properties. However, this sealer did not present a bioactive potential.

Resumo O objetivo deste estudo foi avaliar propriedades físicas de cimentos endodônticos (AH Plus, MTA Fillapex e Endofill), por meio de testes convencionais e micro-CT. A estabilidade dimensional foi avaliada após imersão dos materiais em água destilada por 30 dias. A solubilidade e a alteração volumétrica dos materiais foram avaliadas após 7 e 30 dias de imersão em água destilada. A solubilidade foi avaliada por meio de perda de massa e a alteração volumétrica foi avaliada por micro-CT. A porosidade foi avaliada por microscopia após 7 dias de imersão em água destilada e por micro-CT após a presa e imersão em água destilada por 7 e 30 dias. A análise estatística foi realizada por meio dos testes ANOVA e Tukey, com nível de significância de 5%. MTA Fillapex apresentou a maior solubilidade (p<0,05), com valores acima das recomendações ISO/ADA. As alterações volumétricas e dimensionais foram maiores para MTA Fillapex, seguido por Endofill e AH Plus (p<0,05). MTA Fillapex e AH Plus não cumpriram os padrões ISO/ADA em relação à estabilidade dimensional. Uma maior porosidade total foi observada para MTA Fillapex (p <0,05). Endofill apresentou maior porosidade total que o AH Plus pela avaliação em microscopia (p<0,05), e ambos os cimentos foram semelhantes na avaliação por micro-CT (p>0,05). Em conclusão, MTA Fillapex apresentou maior solubilidade, alteração dimensional e volumétrica, além de maior porosidade em relação aos demais cimentos avaliados. As propriedades físicas avaliadas estão relacionadas, e os diferentes testes forneceram dados complementares. Micro-CT é um método valioso para avaliação das propriedades físicas dos materiais endodônticos.

Abstract The aim of this study was to evaluate physical properties of endodontic sealers (AH Plus, MTA Fillapex and Endofill), by conventional and micro-CT tests. Dimensional stability was evaluated after immersion of materials in distilled water for 30 days. Solubility and volumetric change were evaluated after 7 and 30 days of immersion in distilled water. Solubility was evaluated by means of mass loss and volumetric change was assessed by micro-CT. Porosity was evaluated under a microscope after 7 days of immersion in distilled water, and by using micro-CT after setting and immersion in distilled water for 7 and 30 days. Statistical analysis was performed by ANOVA and Tukey’s test with 5% significance level. MTA Fillapex presented the highest solubility (p<0.05), showing values above the ISO/ADA recommendations. MTA Fillapex presented higher volumetric and dimensional changes, followed by Endofill and AH Plus (p<0.05). Dimensional stability of the MTA Fillapex and AH Plus did not follow ISO/ADA standards. The highest total porosity was observed for MTA Fillapex (p<0.05). Endofill had higher total porosity than AH Plus according to microscope evaluation (p<0,05), and both sealers were similar in micro-CT assessment (p>0,05). In conclusion, MTA Fillapex presented higher solubility, dimensional and volumetric change besides porosity compared to the other evaluated sealers. The assessed physical properties of sealers are related, and the different tests provided complementary data. Micro-CT is a valuable method for assessment of physical properties of endodontic materials.

Resumo Introdução Escoamento e capacidade de preenchimento de cimentos obturadores são indispensáveis para um selamento hermético do canal radicular. Microtomografia computadorizada (micro-CT) pode ser utilizada como uma metodologia complementar para avaliação de tais propriedades. Objetivo Avaliar escoamento e capacidade de preenchimento de AH Plus, Endofill e Sealapex, por meio de metodologia convencional e micro-CT. Material e método O escoamento dos cimentos foi analisado de acordo com as normas ISO 6876/2012 e complementado pela avaliação em área. Placas de vidro foram confeccionadas nos diâmetros de 1×1×2 mm e 1×1×1 mm (comprimento, largura e altura), com uma cavidade central e quatro canaletas nas direções horizontal e vertical. Cada material foi colocado na cavidade central. Outra placa de vidro e um peso de metal foram colocados sobre o cimento e mantidos por 10 minutos. O conjunto placa de vidro/cimento foi escaneado usando micro-CT. O escoamento foi calculado por medição linear do material nas canaletas. O preenchimento (mm3) central foi calculado na cavidade central e o preenchimento lateral foi medido até 2 mm a partir da cavidade central. Os dados foram submetidos aos testes ANOVA/Tukey (α=0.05). Resultado Todos os cimentos avaliados apresentaram escoamento de acordo com as normas ISO 6876. Os materiais mostraram capacidade de preenchimento da cavidade central superior a 80% e preenchimento lateral superior a 75%. Não houve diferença no escoamento (mm e mm2) e na capacidade de preenchimento (mm3) proporcionada pelos materiais (p>0.05). Conclusão Todos os cimentos obturadores avaliados mostraram adequado escoamento e capacidade de preenchimento, sugerindo a aplicação clínica dos mesmos.

Abstract Introduction Flow and filling ability of root canal sealers are indispensable for hermetic sealing of the root canal. Micro-computed tomography (micro-CT) can be used as a complementary methodology to evaluate such properties. Objective To evaluate the flow and filling ability of AH Plus, Endofill and Sealapex by conventional methodology and micro-CT. Material and method The flow of the sealers was analyzed according to ISO 6876/2012 and complemented by the area evaluation. Glass plates were manufactured with diameters of 1×1×2 mm and 1×1×1 mm (length, width and height), with a central cavity and four grooves in the horizontal and vertical directions. Each material was placed in the central cavity. Another glass plate and a metal weight were placed on the cement and kept for 10 minutes. The glass plate/sealer set was scanned using micro-CT. The flow was calculated by linear measurement of the material in the grooves. The central filling (mm3) was calculated in the central cavity and the lateral filling was measured up to 2 mm from the central cavity. Data were submitted to ANOVA/Tukey tests (α=0.05). Result All evaluated sealers presented flow according to ISO 6876 standards. The materials showed central cavity filling capacity higher than 80% and lateral filling greater than 75%. There was no difference in flow (mm and mm2) and in the filling ability (mm3) provided by the materials (p>0.05). Conclusion All evaluated root canal sealers showed adequate flow and filling capacity, suggesting their clinical application.

Abstract Objective: To evaluate the absorption/fluid uptake, solubility and porosity of White mineral trioxide aggregate (MTA) Angelus, Biodentine (BIO), and zinc oxide-eugenol (ZOE). Material and Methods: Solubility was evaluated after immersion in distilled water for 7 and 30 days. Porosity was evaluated using digital inverted microscope, scanning electron microscope (SEM) and micro-computed tomography (micro-CT). For the fluid uptake test, specimens were immersed in Hank's balanced salt solution (HBSS) for 1, 7, 14 and 28 days. Fluid absorption, solubility and porosity of the materials were measured after each period. Statistical evaluation was performed using one-way analysis of variance (ANOVA) and Tukey tests, with a significance level at 5%. Results: After 7 and 30 days, BIO showed the highest solubility (p<0.05). All methods demonstrated that MTA had total porosity higher than BIO and ZOE (p<0.05). Micro-CT analysis showed that MTA had the highest porosity at the initial period, after its setting time (p<0.05). After 7 and 30 days, ZOE had porosity lower than MTA and BIO (p<0.05). Absorption was similar among the materials (p>0.05), and higher fluid uptake and solubility were observed for MTA in the fluid uptake test (p<0.05). Conclusions: BIO had the highest solubility in the conventional test and MTA had higher porosity and fluid uptake. ZOE had lower values of solubility, porosity and fluid uptake. Solubility, porosity and fluid uptake are related, and the tests used provided complementary data.