Abstract In this work, cobalt and zinc-doped Ce0.8Gd0.2O1.9 samples were prepared starting from a commercial nanopowder and compared to the undoped material. The powder samples were pressed and afterwards sintered by a two-step procedure, before characterization by X-Ray Diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Impedance Spectroscopy (IS) in air. Cobalt or zinc additions are effective as sintering aid, allowing peak sintering temperatures around 1000°C to reach densifications above of 93% of theoretical density, showing no evidence for the presence of secondary phases. The total conductivity at 800 °C of pressed Zn-doped samples (6.7x10-2 S/cm) and Co-doped samples (7.5x10-2 S/cm) is similar for undoped samples (7.2x10-2 S/cm) showing that Zn and Co has a positive effect on densification without compromising the electrical conductivity.

Adding ZnO reduces sintering temperature of yttria stabilized zirconia. Adding up to 0.5 wt% of ZnO is possible to densify to 8 mol% yttria stabilized zirconia (TZ8Y) to 95% of relative density at 1300 °C, besides, the electrical conductivity increases about 30% at 800 °C when compared to pure TZ8Y with the same relative density and average grain size. These results show that TZ8Y co-doped with ZnO can be a potential electrolyte to solid oxide fuel cells and electrolyzer cells.