Abstract This study aimed to evaluate the bond strength between relined fiberglass posts with different composite resin opacities in different thirds of the intraradicular dentin. Thirty single-rooted premolars were endodontically treated and divided into three groups (n=10): fiberglass posts relined with translucent composite resin, fiberglass posts relined with opaque composite resin, and fiberglass posts without relining. After cementation of the posts, the specimens were cut perpendicular to the long axis of the tooth in slices of approximately 1.3 mm of each third to be analyzed (cervical, middle, and apical) and then subjected to the push-out test. The bond strength (MPa) data were subjected to Shapiro-Wilk normality tests and two-way repeated measures analysis of variance, considering the experimental groups and different regions as study factors. Tukey’s post-hoc test (p<.05) was applied for comparisons between the groups. In the cervical third, higher values of bond strength were found for the group relined with translucent resin, with a statistically significant difference for the other groups. In the other regions, both opaque and translucent resins showed similar results, but both showed higher values of bond strength compared to fiberglass posts without relining. The bond strength of fiberglass posts to different thirds of intraradicular dentin is influenced by composite resin relining as well as the opacity of the resin. The use of translucent composite resin is a more effective alternative for fiberglass posts relining. singlerooted single rooted n=10 n10 n 10 (n=10) 13 1 3 1. cervical, (cervical middle apical pushout push out MPa (MPa ShapiroWilk Shapiro Wilk twoway two way variance factors Tukeys Tukey s posthoc post hoc p<.05 p05 p 05 (p<.05 results n=1 n1 (n=10 p<.0 p0 0 (p<.0 n= (n=1 p<. (p<. (n= p< (p< (n (p

Resumo Este estudo teve como objetivo avaliar a resistência de união entre pinos de fibra de vidro anatomizados com resinas compostas de diferentes opacidades em diferentes terços da dentina intrarradicular. Trinta pré-molares uniradiculares foram tratados endodonticamente e divididos em três grupos (n=10): pinos de fibra de vidro anatomizados com resina composta translúcida, pinos de fibra de vidro anatomizados com resina composta opaca e pinos de fibra de vidro sem anatomização. Após a cimentação dos pinos, os corpos de prova foram cortados perpendicularmente ao longo eixo do dente em fatias de aproximadamente 1,3 mm de cada terço a ser analisado (cervical, médio e apical) e posteriormente submetidos ao teste de push-out. Os dados de resistência de união (MPa) foram submetidos a testes de normalidade de Shapiro-Wilk e ANOVA dois fatores para análises repetidas, considerando os grupos experimentais e diferentes regiões como fatores de estudo. O teste post-hoc de Tukey (p=0,05) foi aplicado para comparações entre os grupos. No terço cervical foram encontrados maiores valores de resistência de união no grupo com anatomização com resina translúcida, com diferença estatisticamente significativa para os demais grupos. Nas demais regiões, tanto as resinas opacas quanto as translúcidas apresentaram resultados semelhantes, mas ambas apresentaram valores de resistência de união superiores aos pinos de fibra de vidro sem anatomização. A resistência de união dos pinos de fibra de vidro aos diferentes terços da dentina intrarradicular é influenciada pela anatomização da resina composta, bem como pela opacidade da resina. A utilização de resina composta translúcida é uma alternativa mais eficaz para a anatomização de pinos de fibra de vidro. prémolares pré molares n=10 n10 n 10 (n=10) 13 1 3 1, cervical, (cervical apical pushout. pushout push out. out push-out MPa (MPa ShapiroWilk Shapiro Wilk repetidas posthoc post hoc p=0,05 p005 p 0 05 (p=0,05 semelhantes n=1 n1 (n=10 p=0,0 p00 (p=0,0 n= (n=1 p=0, p0 (p=0, (n= p=0 (p=0 (n p= (p= (p

Abstract This study aimed to evaluate the influence of dental adhesive color on the chromatic stability and fluorescence intensity of composite resin restorations of different thicknesses. Ninety bovine enamel samples were obtained and restored with resin composite varying thicknesses of restorative material and enamel (1.0 mm enamel and 1.0 mm composite; 1.5 mm enamel and 0.5 mm composite; 0.5 mm enamel and 1.5 mm composite). The restorations were made of composite resin (Opallis E-bleach H) using different types of dental adhesives: Ambar, Ambar APS, and Single Bond Universal (n=10). The samples were subjected to color measurement tests in a spectrophotometer using CIEDE2000 and fluorescence intensity measurements before and after aging in a red wine coloring solution. Data were subjected to analysis of variance (ANOVA) and Tukey's test (α = 0.05). There were no statistically significant changes in color stability or fluorescence intensity for restorations made of different materials or thicknesses (p>0.05). Single Bond Universal showed greater color stability at 0.5 mm thickness (ΔE00 = 4.4 ± 1.6) compared to other thicknesses of the same material (p=0.003), as well as a greater difference in fluorescence intensity after aging at 1.5 mm thickness (-414.9 ± 103.8) compared to other materials (p=0.0002). Overall, it was concluded that the different adhesive systems did not influence the color stability and fluorescence of restorations of different thicknesses. 10 1 0 (1. 1. 15 5 05 0. composite. . composite) Opallis Ebleach E bleach H adhesives APS n=10. n10 n n=10 (n=10) CIEDE CIEDE200 solution ANOVA (ANOVA Tukeys Tukey s α 0.05. 005 0.05 0.05) p>0.05. p005 p p>0.05 (p>0.05) ΔE00 ΔE (ΔE0 44 4 4. 1.6 16 6 p=0.003, p0003 p=0.003 , 003 (p=0.003) 414.9 4149 414 9 (-414. 103.8 1038 103 8 p=0.0002. p00002 p=0.0002 0002 (p=0.0002) Overall (1 n1 n=1 (n=10 CIEDE20 00 0.0 p00 p>0.0 (p>0.05 ΔE0 (ΔE p000 p=0.00 (p=0.003 414. 41 (-414 103. p0000 p=0.000 000 (p=0.0002 ( n= (n=1 CIEDE2 p0 p>0. (p>0.0 p=0.0 (p=0.00 (-41 (p=0.000 (n= p>0 (p>0. p=0. (p=0.0 (-4 (n p> (p>0 p=0 (p=0. (- (p> p= (p=0 (p (p=

Resumo O objetivo deste estudo foi avaliar a influência da cor do adesivo dental na estabilidade cromática e intensidade de fluorescência das restaurações de resina composta de diferentes espessuras. Foram obtidos noventa amostras de esmalte bovino que foram restaurados com resina composta, variando a espessura do material restaurador e do esmalte (1,0 mm de esmalte e 1,0 mm de compósito; 1,5 mm de esmalte e 0,5 mm de compósito; 0,5 mm de esmalte e 1,5 mm de compósito). As restaurações foram feitas de resina composta (Opallis E-bleach H) utilizando diferentes tipos de adesivos odontológicos: Ambar, Ambar APS, e Single Bond Universal (n=10). As amostras foram submetidas a testes de medição de cor em um espectrofotômetro usando CIEDE2000 e medições de intensidade de fluorescência antes e depois do envelhecimento em uma solução de coloração de vinho tinto. Os dados foram submetidos à análise de variância (ANOVA) e ao teste de Tukey (α = 0,05). Não houve mudanças estatisticamente significativas na estabilidade da cor ou intensidade de fluorescência para restaurações feitas de diferentes materiais ou espessuras (p>0,05). O Single Bond Universal mostrou maior estabilidade de cor a 0,5 mm de espessura (ΔE00 = 4,4 ± 1,6) em comparação com outras espessuras do mesmo material (p=0,03), bem como uma maior diferença na intensidade de fluorescência após o envelhecimento a 1,5 mm de espessura (-414,9 ± 103,8) em comparação com outros materiais (p=0,0002). Em geral, concluiu-se que os diferentes sistemas adesivos não influenciaram a estabilidade de cor e a intensidade de fluorescência das restaurações de diferentes espessuras. 10 1 0 (1, 1, compósito 15 5 05 0, compósito. . compósito) Opallis Ebleach E bleach H odontológicos APS n=10. n10 n n=10 (n=10) CIEDE CIEDE200 tinto ANOVA (ANOVA α 0,05. 005 0,05 0,05) p>0,05. p005 p p>0,05 (p>0,05) ΔE00 ΔE (ΔE0 44 4 4, 1,6 16 6 p=0,03, p003 p=0,03 , 03 (p=0,03) 414,9 4149 414 9 (-414, 103,8 1038 103 8 p=0,0002. p00002 p=0,0002 0002 (p=0,0002) geral concluiuse concluiu se (1 n1 n=1 (n=10 CIEDE20 00 0,0 p00 p>0,0 (p>0,05 ΔE0 (ΔE p=0,0 (p=0,03 414, 41 (-414 103, p0000 p=0,000 000 (p=0,0002 ( n= (n=1 CIEDE2 p0 p>0, (p>0,0 p=0, (p=0,0 (-41 p000 p=0,00 (p=0,000 (n= p>0 (p>0, p=0 (p=0, (-4 (p=0,00 (n p> (p>0 p= (p=0 (- (p> (p= (p

Abstract Objective This study aimed to evaluate the effects of different toothpastes on the surface wear of enamel, dentin, composite resin (CR), and resin-modified glass ionomer cement (RMGIC), and to perform a topographic analysis of the surfaces, based on representative images generated by atomic force microscopy (AFM) after erosion-abrasion cycles. Methodology One hundred and forty bovine incisors were collected and divided into two groups: 72 enamel and 72 dentin blocks (4×4 mm). Half of the specimens were restored with CR (Filtek Z350 XT) and the other half with RMGIC (Fuji II LC). Then, samples were submitted to a demineralization cycle (5 days, 4×2 min/day, 1% citric acid, pH 3.2) and exposed to three different toothpastes (2×15 s/day): without fluoride (WF, n=12), sodium fluoride-based (NaF, n=12), and stannous fluoride-based (SnF2, n=12). Surface wear, as well as restoration interfaces wear, were investigated by profilometry of the dental substrates and restorative materials. All representative surfaces underwent AFM analysis. Data were analyzed by two-way analysis of variance and Tukey’s tests (α=0.05). Results NaF-based toothpaste caused the greater dentin surface wear (p<0.05). Toothpastes affected only enamel-restoration interfaces. AFM analysis showed precipitate formation in dentinal tubules caused by the use of fluoride toothpastes. Conclusions NaF-based toothpastes had no protective effect on enamel adjacent to CR and RMGIC against erosion-abrasion challenges, nor on dentin adjacent to RMGIC material. SnF2-based toothpastes caused more damage to interfaces between enamel and RMGIC.

Resumo O objetivo deste trabalho foi avaliar a resistência de união e permeabilidade da interface de pinos de fibra de vidro nos diferentes terços da dentina intrarradicular (cervical, médio e apical) submetidos a diferentes agentes irrigantes. Noventa dentes unirradiculares humanos foram submetidos ao tratamento endodôntico e foram divididos em cinco grupos de acordo com os agentes irrigantes: água destilada, hipoclorito de sódio 5,25%, ácido poliacrílico 25%, clorexidina 2% e dispersão de nanopartícula de prata à 23 ppm. Os grupos foram divididos em 3 subgrupos (n=6) de acordo com a técnica adotada para cimentação adesiva dos pinos de fibra de vidro: Grupo SBU: sistema adesivo ScotchbondTM Universal + cimento resinoso RelyX ARC; Grupo U200: cimento resinoso autoadesivo RelyX U200; Grupo MCE: cimento resinoso autoadesivo Maxcem Elite. A resistência de união e a permeabilidade da interface foram mensurados em diferentes áreas da dentina intrarradicular. Os dados foram submetidos a ANOVA e teste de Fisher (a=0,05). Amostras representativas foram levadas à microscopia eletrônica de varredura. A solução de nanopartícula de prata apresentou os maiores valores de resistência de união em todos os terços analisados para o grupo SBU. No grupo U200, os maiores valores foram encontrados para a solução de hipoclorito de sódio, com diferença para o ácido poliacrílico. Observou-se uma diminuição nos valores de resistência de união na direção cérvico-apical para o grupo MCE e o mesmo comportamento foram encontrados para os demais grupos. Com relação a permeabilidade da interface, o uso da solução de nanopartícula de prata resultou em menores valores nos terços cervical e apical. Houve diminuição dos valores de resistência de união no sentido cérvico-apical. As diferentes soluções irrigantes, bem como a profundidade intrarradicular influenciaram a resistência de união e permeabilidade da interface dos materiais adesivos ao substrato dentinário. A nanopartícula de prata pode ser utilizada como agente irrigador do conduto radicular previamente à cimentação de pinos de fibra de vidro.

Abstract The aim of this study was to evaluate the push-out bond strength and interface permeability of glass-fiber posts in different regions of post space (cervical, middle, and apical) submitted to different irrigation solutions. Ninety single-rooted human teeth were submitted to endodontic treatment and divided into five groups, according to irrigation solutions: distilled water, 5.25% NaOCl, 25% polyacrylic acid, 2% chlorhexidine, and 23 ppm Ag NP dispersion. Each group was divided in 3 subgroups (n=6) according to cementation: SBU: Adper Scotchbond Universal + RelyX ARC; U200: RelyX U200; MCE: MaxCem Elite. Bond strength and sealing ability were measured in different areas of post space. The data was subjected to ANOVA and Fisher’s test (a=0,05). The silver nanoparticle solution showed highest bond strength values and lowest interface permeability in all thirds analyzed for SBU group. In the U200 group, the highest bond strength values were found for sodium hypochlorite solution, with significant difference between this solution and polyacrylic acid. A decrease in bond strength values in cervical to apical direction was found for MCE group and the same behavior were found for others groups. Regarding interface permeability, use of silver nanoparticle solution resulted in lower values in cervical and apical thirds. There was a decrease in bond strength in cervical to apical direction. Different irrigation solutions and intraradicular depth influenced the bond strength and interface permeability of adhesive material to dentin substrate. Silver nanoparticle solution can effectively be used as an irrigation agent in post space prior to fiber post cementation process.

Abstract: The aim of this study is to evaluate the effect of chitosan or nanodiamond incorporation on the color stability and surface roughness of a bisacrylic resin subjected to artificial aging. Four bisacrylic resins were evaluated, namely, control, chitosan-modified material, nanodiamond-modified material, and chitosan–nanodiamond-modified material. Twenty-four specimens were prepared for each material. The surface roughness was determined using a profilometer with a cut-off of 0.25 mm. The baseline color was measured according to the CIE L*a*b* system using a reflectance spectrophotometer. After these tests, the specimens were individually immersed in cola soft drink, red wine, or distilled water (n = 8) for 28 days. After the aging, the surface roughness and final color were re-evaluated. The color stability was determined using the difference between the coordinates obtained before and after the aging process. The data on roughness and color change were evaluated using ANOVA and the Tukey test (α = 0.05). The results show that the incorporation of nanodiamonds and chitosan into a bisacrylic resin provided a better color stability to the materials (p = 0.007). The storage in red wine resulted in a higher variation in the surface roughness values, especially when only the nanodiamond was incorporated to the material (p < 0.05). The incorporation of both chitosan and nanodiamonds are promising in providing an improvement in the properties of the bisacrylic resin when they are simultaneously incorporated in the product.

Abstract Objective This study verified the occurrence of dental sensitivity in patients submitted to a 35% hydrogen peroxide based product (Whiteness HP Maxx 35% – FGM), skin cold sensation threshold (SCST) and its influence on dental sensitivity. Material and Methods Sixty volunteers were divided into 4 groups (n = 15), according to SCST (low: GI and GIII, and high: GII and IV) and bleaching treatment (hydrogen peroxide: GI and GII, and placebo: GIII and GIV). SCST was determined in the inner forearm for 6 different times using a neurosensory analyzer, the TSA II (Medoc Advanced Medical Systems, Ramat Yishai, Northern District, Israel). Dental sensitivity measurements were performed 10 different times using a thermal stimulus and an intraoral device attached to TSA II, positioned in the buccal surface of the upper right central incisor. Spontaneous dental sensitivity was also determined using the Visual Analogue Scale (VAS). Data were submitted to Student's t-test and Pearson's Correlation Test (α=0.05). SCST remained the same during bleaching treatment. Results Distinct responses of dental sensitivity were found in patients with low and high SCST during the first and third bleaching session (p≤0.05). The teeth submitted to the bleaching treatment became more sensitive to cold than those treated with placebo. Moreover, data obtained with TSA and VAS presented moderate correlation. Conclusions Bleaching treatment increased dental sensitivity and skin cold sensation threshold might represent a determining factor in this occurrence, since low and high SCST patients had different responses to the thermal stimulus in the teeth.

Abstract Objective The objective of this study was to evaluate dental sensitivity using visual analogue scale, a Computerized Visual Analogue Scale (CoVAS) and a neurosensory analyzer (TSA II) during at-home bleaching with 10% carbamide peroxide, with and without potassium oxalate. Materials and Methods Power Bleaching 10% containing potassium oxalate was used on one maxillary hemi-arch of the 25 volunteers, and Opalescence 10% was used on the opposite hemi-arch. Bleaching agents were used daily for 3 weeks. Analysis was performed before treatment, 24 hours later, 7, 14, and 21 days after the start of the treatment, and 7 days after its conclusion. The spontaneous tooth sensitivity was evaluated using the visual analogue scale and the sensitivity caused by a continuous 0°C stimulus was analyzed using CoVAS. The cold sensation threshold was also analyzed using the TSA II. The temperatures obtained were statistically analyzed using ANOVA and Tukey's test (α=5%). Results The data obtained with the other methods were also analyzed. 24 hours, 7 and 14 days before the beginning of the treatment, over 20% of the teeth presented spontaneous sensitivity, the normal condition was restored after the end of the treatment. Regarding the cold sensation temperatures, both products sensitized the teeth (p<0.05) and no differences were detected between the products in each period (p>0.05). In addition, when they were compared using CoVAS, Power Bleaching caused the highest levels of sensitivity in all study periods, with the exception of the 14th day of treatment. Conclusion We concluded that the bleaching treatment sensitized the teeth and the product with potassium oxalate was not able to modulate tooth sensitivity.

Resumo Este estudo teve como objetivo avaliar a penetração trans-amelodentinária do peróxido de hidrogênio (H2O2) aplicados em dentes bovinos pigmentados com chá preto em diferentes intensidades. Divisão dos grupos: AD em água destilada; CP100 em uma infusão de 1,6 g de chá preto para 100 mL de água destilada; CP10 em uma infusão de 1,6 g de chá preto para 10 mL de água destilada. Todos os grupos foram imersos por 6 dias. Para quantificar a penetração de H2O2, as amostras foram colocadas em câmaras pulpares artificiais (CPAs) e submetidas a um tratamento clareador com PH a 38%, uma vez por semana durante 3 semanas. Após o tratamento clareador, a solução tampão de acetato das CPAs com a enzima da peroxidase, foi avaliada num espectrofotômetro de reflexão. A penetração trans-amelodentinária de PH e os valores de L* obtidos em T1, T2 e T3 foram submetidos ao teste estatístico de Kruskal-Wallis e Friedman. Em T1, a difusão de H2O2 no AD foi mais elevada do que em CP100 e CP10. Nos outros tempos de avaliação, os valores de penetração no CP100 e CP10 aumentaram e permaneceram semelhantes. Os valores L* aumentaram significativamente em todos os grupos no T1. No T2, os valores L* foram maiores no AD e os valores em CP100 e CP10 foram semelhantes entre si. No último tempo, o CP10 apresentou os menores valores de L*. Diferentes níveis de pigmentação não afetaram a penetração de H2O2 através do esmalte e dentina e o agente de clareador foi eficaz na alteração cromática.

Abastract This study aimed to evaluate the transenamel and transdentinal penetration of hydrogen peroxide (H202) applied to bovine teeth pigmented with black tea at different intensities. The following groups were formed DW: immersion in distilled water; BT100: immersion in an infusion of 1.6 g of black tea per 100 mL distilled water; BT10: immersion in an infusion of 1.6 g black tea per 10 mL distilled water. All groups were immersed for 6 days. To quantify the penetration of H202, the specimens were placed in artificial pulp chambers (APCs) and subjected to bleaching treatment with 38% H2O2 once per week for 3 weeks. After bleaching treatment, the acetate buffer solution of APCs with peroxidase enzyme was evaluated in a reflection spectrophotometer. The transenamel and transdentinal penetration of H2O2 and the L* values obtained at T1, T2 and T3 were subjected to Kruskal-Wallis and Friedman statistical tests. At T1, the H2O2 diffusion in DW was higher than that in BT100 and BT10. At the other evaluation times, the penetration values in BT100 and BT10 increased and remained similar. The L* values increased significantly in all groups at T1. At T2, the L* values were higher in DW, while the values in BT100 and BT10 were similar to each other. At the end of the experiment, BT10 showed the lowest L* values. The pigmentation level did not affect the penetration of H2O2 through the enamel and dentin and the bleaching agent effectively changed the color of the teeth.

Resumo O objetivo deste estudo foi avaliar o efeito da ciclagem de pH erosiva com soluções que simulam a erosão dental, na dureza Martens (HMV) e módulo de elasticidade (Eit) da dentina restaurada com sistemas adesivos contendo fluoretos. Vinte e sete blocos de dentina foram restaurados com três sistemas adesivos: sistema adesivo de condicionamento total Adper Single Bond 2 e sistemas adesivos autocondicionantes contendo fluoreto One Up Bond F e Clearfil SE Protect. As restaurações foram realizadas com resina Filtek Z250. Os valores de HMV e Eit nas distâncias de 10, 30, 50 e 70µm da interface foram avaliadas em ultramicrodurômetro dinâmico antes e após a imersão em água deionizada, ácido cítrico e ácido clorídrico (n=9). Dados foram submetidos à ANOVA para medidas repetidas e Fisher PLSD (α=0,05). Após a ciclagem erosiva, os valores de HMV da dentina diminuíram em todos os grupos. Para a dentina restaurada com Adper Single Bond 2, os menores valores foram encontrados próximo a camada híbrida enquanto que, para os sistemas adesivos One Up Bond F e Clearfil SE Protect, os valores permaneceram inalterados em todas as distâncias. Para a dentina restaurada com os materiais que liberam fluoretos, uma redução nos valores de Eit foi encontrada, mas após 30µm essa diferença não foi mais significante. As substâncias ácidas foram capazes de alterar a HMV e o Eit da dentina subjacente. Para os adesivos que liberam fluoretos, quanto maior a distância da interface adesiva, menor os valores de Eit. O fluoreto presente no One Up Bond F e Clearfil SE Protect foi capaz de proteger a dentina subjacente próxima aos materiais. Dessa maneira, a presença do flúor em sistemas adesivos pode ter algum efeito positivo em estágios iniciais de lesões erosivas.

Abstract The aim of the study was to evaluate the effect of erosive pH cycling with solutions that simulate dental erosion on Martens hardness (HMV) and elastic modulus (Eit) of dentin restored with fluoride-releasing adhesive systems. Twenty-seven bovine dentin slabs were restored with three adhesive systems: Adper Single Bond 2 total-etch adhesive system, One Up Bond F and Clearfil SE Protect fluoride-containing self-etching adhesive systems. The restorations were made with Filtek Z250. The HMV and Eit values at distances of 10, 30, 50 and 70 µm from the interface were evaluated using a dynamic ultra microhardness tester before and after immersion in deionized water, citric acid and hydrochloric acid (n=9). Data were submitted to repeated-measures ANOVA and Fisher's PLSD tests (=0.05). After erosive cycling, HMV values of dentin decreased in all groups. For dentin restored with Adper Single Bond 2, the lowest values were found closer to the hybrid layer, while for One Up Bond F and Clearfil SE Protect, the values remained unaltered at all distances. For dentin restored with fluoride-releasing adhesive systems, a decrease in Eit was found, but after 30 µm this difference was not significant. The acid substances were able to alter HMV and Eit of the underlying dentin. For fluoride-releasing adhesives, the greater the distance from bonded interface, the lower the Eit values. The fluoride in One Up Bond F and Clearfil SE Protect was able to protect the underlying dentin closer to the materials. In this way, the fluoride from adhesive systems could have some positive effect in the early stages of erosive lesions.

<p>Este estudo avaliou a alteração de cor, a citotoxicidade e a difusão de peroxido de hidrogênio ocorridos em diferentes protocolos clareadores caseiros: peróxido de carbamida (PC) 10% por 3 ou 1,5 h; peróxido de hidrogênio (PH) 6% por 1,5 h ou 45 min. Para a quantificação da penetração do peróxido, discos de dentes bovinos foram posicionados em câmaras pulpares artificiais (CPAs) contendo solução tampão de acetato, que foi coletada para avaliação em espectrofotômetro. Para análise da citotoxicidade, os espécimes foram adaptados nas CPAs contendo meio de cultura, que posteriormente foi aplicado sobre células odontoblastóides MDPC-23 por 1 h. O metabolismo celular foi avaliado pelo teste MTT e a alteração de cor dos espécimes foi analisada pelo sistema CIE L*a*b*. Os dados foram submetidos a ANOVA e teste de Fisher (α=5). O tratamento com PC10% por 3 horas foi o mais efetivo, enquanto que o tratamento com PH 6% por 45 min produziu a menor alteração cromática. Os grupos PC 10% por 1,5 h e PH 6% por 45 min causaram a menor penetração trans-amelodentinária do peróxido, e PH 6% por 1,5 h, a maior difusão. Nenhum tratamento alterou o metabolismo celular. A redução do tempo de exposição aos peróxidos comprometeu o resultado clareador; maior penetração de peroxido não significa maior efetividade clareadora.</p>

<p>This study evaluated the color change, cytotoxicity and hydrogen peroxide (HP) diffusion caused by different home bleaching protocols: 10% carbamide peroxide (CP) for 3 or 1.5 h, 6% hydrogen peroxide for 1.5 h or 45 min. To quantify the peroxide penetration, disks of bovine teeth were placed in artificial pulp chambers (APCs) containing acetate buffer, which was collected for evaluation in a spectrophotometer. For analysis of cytotoxicity, specimens were adapted in APCs containing culture medium, which subsequently was applied on MDPC-23 odontoblast-like cells for 1 h. Cellular metabolism was evaluated by methyl tetrazolium (MTT) assay and the color change of the specimens was analyzed using the CIE L * a * b * system. The data were submitted to ANOVA and Fisher test (α=5%). The treatment with 10% CP for 3 h was the most effective, and 6% HP for 45 min produced the lowest color change. The groups 10% CP for 1.5 h and 6% HP for 45 min had the lowest trans-enamel dentinal HP penetration, and the 6% HP for 1.5 h had the highest. None of the protocols affected cellular metabolism and morphology. In conclusion, reduced peroxide exposure time reduced the bleaching result; higher HP diffusion did not mean higher effectiveness.</p>

O objetivo deste estudo foi avaliar a desmineralização e a penetração do peróxido de hidrogênio (HP) em dentes com lesões incipientes submetidos ao tratamento clareador. Para analisar a penetração do peróxido de hidrogênio, discos de esmalte/dentina hígidos e desmineralizados foram posicionados em câmaras pulpares artificiais contendo solução tampão de acetato. Após o tratamento clareador, esta solução foi submetida à análise da densidade óptica no espectrofotômetro e as superfícies dos discos foram analisadas por meio de microscopia eletrônica de varredura (MEV) e microscopia de luz polarizada (MLP). Os discos restantes foram submetidos à análise de microdureza transversal em diferentes profundidades. Os dados foram submetidos aos testes ANOVA e teste PLSD Fisher (= 5%). Observou-se que os dentes previamente desmineralizados mostraram maior penetração de HP (p<0,05). O tratamento clareador causou alterações em uma profundidade de 20 μm em esmalte hígido e até 90 μm em esmalte desmineralizado. As imagens obtidas em PLM e MEV mostraram que o tratamento clareador promove alterações superficiais no esmalte, sendo mais pronunciadas em dentes previamente desmineralizados. Foi concluído que o nível de mineralização do esmalte influencia a penetração do PH e que o agente clareador contribuiu para o aumento da profundidade de desmineralização.

The aim of this study was to evaluate the demineralization and hydrogen peroxide (HP) penetration in teeth with incipient lesions submitted to bleaching treatment. For analysis of HP penetration, sound and demineralized enamel/dentin discs were placed in artificial pulp chambers containing acetate buffer solution. After bleaching treatment, this solution was subjected for analysis of optical density by spectrophotometry and the disc surfaces were analyzed with scanning electron microscopy (SEM) and polarized light microscopy (PLM). The remaining discs were subjected for cross-sectional hardness analysis at different depths. Data were analyzed by repeated measures ANOVA and PLSD Fisher test (a=0.05). It was observed that previously demineralized teeth showed greater HP penetration (p<0.05). The bleaching treatment caused changes to a depth of 20 µm in sound enamel and up to 90 µm in demineralized enamel. SEM and PLM images revealed that the bleaching treatment caused superficial changes that were considerably more accentuated in previously demineralized teeth. It may be concluded that the enamel mineralization level influences HP penetration and the bleaching agent contributed to increase the demineralization depth.

AIM: To evaluate the effect of different radiant exposures on the degree of conversion (DC), Knoop hardness number (KHN), plasticization (P), water sorption (WS), and solubility (S) of different monomer resin-based composites. METHODS: Circular specimens (5 x 2 mm) were manufactured from methacrylate and silorane composite resins, and light-cured at 19.8, 27.8, 39.6, and 55.6 J/cm2, using second-generation LED at 1,390 mW/cm2. After 24 h, DC was obtained using a FT-Raman spectrometer equipped with a Nd:YAG laser, KHN was measured with 50-g load for 15 s, and P was evaluated on the top and bottom surfaces by the percentage of hardness reduction after 24 h immersed in absolute alcohol. WS and S were determined according to ISO 4049. Data were subjected to statistical analysis (α=0.05). RESULTS: Methacrylate material presented higher DC, KHN, P, and WS than silorane (p<0.05). There was no difference in the S values (p>0.05). The increased radiant exposures improved only the KHN (p<0.05). In general, top surfaces showed higher DC and KHN than bottom, for both materials (p<0.05). The increase of the radiant exposure did not improve most physical properties of the composites and were monomer-base dependent. CONCLUSIONS: Chemical composition of the composite resins resulted in different physical properties behavior and could affect the clinical longevity of dental restorations, but overall these properties were not influenced by the different radiant exposures evaluated in the study.

Para a reabilitação bucal com as próteses implantossuportadas é necessário a realização de procedimentos para criar o volume ósseo necessário para a instalação dos implantes. Com isso, os enxertos ósseos provenientes de áreas doadoras intrabucais ou extrabucais, representam uma possibilidade bastante favorável. O presente trabalho objetivou realizar uma revisão da literatura em que procurou discutir parâmetros para as indicações, as vantagens e complicações para as técnicas dos enxertos ósseos autógenos.

For oral rehabilitation with implant-supported prostheses, there are required procedures to create the bone volume needed for installation of the implants. Thus, bone grafts from intraoral or extraoral donor sites represent a very favorable opportunity. This study aimed to review the literature on the subject, seeking to discuss parameters for the indications, advantages and complications of techniques for autogenous bone grafts.

O objetivo deste estudo foi avaliar o efeito de agentes clareadores no esmalte sadio (ES) ou esmalte com lesão inicial de cárie artificial (LC), utilizando microscopia confocal laser de varredura (CLSM). Oitenta blocos (4 x 5 x 5 mm) de esmalte bovino foram usados, sendo que 40 destes foram desmineralizados com ciclagem de pH para induzir a LC. Oito grupos experimentais foram obtidos a partir dos tratamentos e condição do esmalte (ES ou LC), com n=10: Grupos ES: G1 - sem tratamento (controle); G2 - peróxido de hidrogênio 4% (PH4); G3: PH4 contendo 0,05% cálcio (Ca); G4 - peróxido de hidrogênio 7,5% (pH 7,5) contendo fosfato de cálcio amorfo (ACP). Grupos LC: G5 - não clareado; G6 - pH 4; G7 - pH 4 Ca; G8 - pH 7,5 ACP. Os grupos G2, G3, G6 e G7 foram tratados com o gel clareador por 8 h/dia durante 14 dias, enquanto as amostras dos grupos G4 e G8 foram submetidas ao agente clareador por 30 min/duas vezes ao dia, durante 14 dias. Os blocos de esmalte foram corados com solução de Rodamina B e a área fluorescente de desmineralização foi quantificada utilizando CLSM. Os dados foram submetidos a ANOVA e teste de Fisher (p<0,05). Para ES, os tratamentos clareadores aumentaram significativamente a área de desmineralização quando comparado com os grupos não clareados, entretanto, para LC não foi observado diferença estatística significante entre os grupos. A adição de ACP e Ca na composição dos géis clareadores não anulou os efeitos dos tratamentos clareadores no ES, assim como não teve capacidade de remineralizar o LC.

The aim of this study was to evaluate effect of bleaching agents on sound enamel (SE) and enamel with early artificial caries lesions (CL) using confocal laser scanning microscopy (CLSM). Eighty blocks (4 x 5 x 5 mm) of bovine enamel were used and half of them were submitted to a pH cycling model to induce CL. Eight experimental groups were obtained from the treatments and mineralization level of the enamel (SE or CL) (n=10). SE groups: G1 - unbleached (control); G2 - 4% hydrogen peroxide (4 HP); G3 - 4 HP containing 0.05% Ca (Ca); G4 - 7.5% hydrogen peroxide (7.5 HP) containing amorphous calcium phosphate (ACP). CL groups: G5 - unbleached; G6 - 4 HP; G7 - 4 HP containing Ca; G8 - 7.5 HP ACP. G2, G3, G6, G7 were treated with the bleaching agents for 8 h/day during 14 days, while G4 and G8 were exposed to the bleaching agents for 30 min twice a day during 14 days. The enamel blocks were stained with 0.1 mM rhodamine B solution and the demineralization was quantified using fluorescence intensity detected by CLSM. Data were analyzed using ANOVA and Fisher’s tests (α=0.05). For the SE groups, the bleaching treatments increased significantly the demineralization area when compared with the unbleached group. In the CL groups, no statistically significant difference was observed (p>0.05).The addition of ACP or Ca in the composition of the whitening products did not overcome the effects caused by bleaching treatments on SE and neither was able to promote remineralization of CL.

This study evaluated the effect of heat treatment on CrNi stainless steel orthodontic archwires. Half of forty archwires of each thickness - 0.014" (0.35 mm), 0.016" (0.40 mm), 0.018" (0.45 mm) and 0.020" (0.50 mm) (totalling 160 archwires) - were subjected to heat treatment while the remainder were not. All of the archwires had their individual thickness measured in the anterior and posterior regions using AutoCad 2000 software before and after compressive and tensile strength testing. The data was statistically analysed utilising multivariance ANOVA at a 5% significance level. All archwires without heat treatment that were subjected to tensile strength testing presented with anterior opening, which was more accentuated in the 0.020" archwires. In the posterior region, the opening produced by the tensile force was more accentuated in the archwires without heat treatment. There was greater stability in the thermally treated archwires, especially those subjected to tensile strength testing, which indicates that the heat treatment of orthodontic archwires establishes a favourable and indispensable condition to preserve the intercanine width.