We investigated the effect of adding the field-dependent recombination process, namely field-enhanced trapping, to the generation-recombination processes of charge carriers that model current oscillations in semiconductors. The main new features arising from this modification are identified in bifurcation diagrams with the electric field as the control parameter. The characteristic of the bifurcation diagrams is a function of impurity energy. Thus, we generated a set of bifurcation diagrams for a range of the impurity energy and applied bias. The energy dependence of the bifurcation diagrams is discussed considering the context of the competition between the generation-recombination mechanisms impact ionization and field-enhanced trapping.

We present an experimental study of bifurcation diagrams from low frequency current oscillations (LFO) measurements obtained from semi-insulating GaAs samples grown by low temperature molecular beam Epitaxy (LT-MBE). The considered growth temperatures were 215ºC and 265ºC. LFO are considered to be spontaneously generated oscillations under constant applied bias V. These oscillations were measurement and recorded in the form of time series. The bifurcation diagrams were obtained from the sequence of minima as a function of the applied bias. The standard measurement procedure was described elsewhere. As the control parameter, the bias allows the identification of a bifurcation route to chaos.

Electric transport properties measured by Van der Pauw resistivity experiments of Low-Temperature Molecular Beam Epitaxy (LT-MBE) GaAs samples are used to identify a method to improve the resistivity of GaAs material. We present results on five samples grown at 265, 310, 315, 325, and 345 ºC. The electric measurements were carried out at temperatures ranging from 130 to 300 K. In this temperature range the dominant transport process is identified as variable range hopping. The hopping parameter plotted against the growth temperature is shown to present a maximum. The mechanisms responsible for this behavior are discussed in relation to the compensation ratio.

Coherent emission efficiency in a 100Å GaAs SQW microcavity was enhanced one order when pumped resonantly at 10 K, compared to the off-resonant excitation. The usual kink observed in the exciton emission linewidth as well as in the emission intensity in relation to the pump power, changes smoothly instead of the usual abrupt kink observed in the off-resonant microcavity laser. In addition, polarization measurements show a correlation relationship between the pump light polarization and the cavity emission polarization.

We have observed Low Frequency Oscillations (LFO) in a GaAs sample grown by molecular beam epitaxy (MBE) at 300 °C as a function of applied electric field, temperature and illumination intensity. Time series of the oscillations for different values of the applied electric field at room temperature were obtained. We have also obtained the jxE characteristics as a function of temperature and light intensity. We were able to control the LFO using three experimental parameters, the electrical field, which controls the oscillation frequency, and the temperature and illumination intensity, which control the carrier density and field-enhanced trapping. We were able to identify the LFO dependence on the carrier density and on the field-enhanced trapping.