Abstract There is growing evidence that C. albicans is associated with dental caries, but its role on caries development needs to be better clarified. Objective: To evaluate at the hard tissue level the effect of C. albicans on the cariogenic potential of S. mutans biofilms focusing on the mineral profile of induced carious lesions. This study also aimed to evaluate the effect of C. albicans on the acidogenic potential of S. mutans biofilms. Methodology: Dual-species (CA+SM) and single-species biofilms (CA or SM) were grown on the surface of enamel slabs in the presence of glucose/sucrose supplemented culture medium for 24, 48 and 72 hours. Demineralization was evaluated through percentage of surface microhardness change (%SMC) and transversal microradiography analysis (ILM and LD) and pH of the spent medium was recorded daily. Data were analyzed by two-way ANOVA followed by Bonferroni correction. Results: %SMC was statistically different among the biofilms at each time point being the highest for SM biofilms and the lowest for CA biofilms which also differed from CA+SM biofilms [SM (24 h: 47.0±7.3; 48 h: 66.3±8.3; 72 h: 75.4±3.9); CA (24 h: 7.3±3.3; 48 h: 7.1±6.4; 72 h: 6.6±3.6); CA+SM (24 h: 35.9±7.39.1; 48 h: 47.2±9.5; 72 h: 47.6±9.5)]. pH of spent medium was statistically lower for SM biofilms compared to the other biofilms at each time point and remained constant over time while pH values increased from 24 to 72 h for both CA and CA+SM biofilms [SM (24 h: 4.4±0.1; 48 h: 4.4±0.1; 72 h: 4.5±0.1); CA (24 h: 6.9±0.3; 48 h: 7.2±0.2; 72 h: 7.5±0.2); CA+MS (24 h: 4.7±0.2; 48 h: 5.1±0.1; 72 h: 6.1±0.6)]. IML and LD for SM biofilms increased over time while no difference was observed from 24 to 72 h for the other biofilms. Conclusions: The present data suggest that C. albicans has low enamel demineralization potential and the presence of C. albicans can reduce both the cariogenic and acidogenic potentials of S. mutans biofilms.

Abstract Objectives: Addition of chlorhexidine has enhanced the antimicrobial effect of glass ionomer cement (GIC) indicated to Atraumatic Restorative Treatment (ART); however, the impact of this mixture on the properties of these materials and on the longevity of restorations must be investigated. The aim of this study was to evaluate the effects of incorporating chlorhexidine (CHX) in the in vitro biological and chemical-mechanical properties of GIC and in vivo clinical/ microbiological follow-up of the ART with GIC containing or not CHX. Material and Methods: For in vitro studies, groups were divided into GIC, GIC with 1.25% CHX, and GIC with 2.5% CHX. Antimicrobial activity of GIC was analyzed using agar diffusion and anti-biofilm assays. Cytotoxic effects, compressive tensile strength, microhardness and fluoride (F) release were also evaluated. A randomized controlled trial was conducted on 36 children that received ART either with GIC or GIC with CHX. Saliva and biofilm were collected for mutans streptococci (MS) counts and the survival rate of restorations was checked after 7 days, 3 months and one year after ART. ANOVA/Tukey or Kruskal-Wallis/ Mann-Whitney tests were performed for in vitro tests and in vivo microbiological analysis. The Kaplan-Meier method and Log rank tests were applied to estimate survival percentages of restorations (p<0.05). Results: Incorporation of 1.25% and 2.5% CHX improved the antimicrobial/anti-biofilm activity of GIC, without affecting F release and mechanical characteristics, but 2.5% CHX was cytotoxic. Survival rate of restorations using GIC with 1.25% CHX was similar to GIC. A significant reduction of MS levels was observed for KM+CHX group in children saliva and biofilm 7 days after treatment. Conclusions: The incorporation of 1.25% CHX increased the in vitro antimicrobial activity, without changing chemical-mechanical properties of GIC and odontoblast-like cell viability. This combination improved the in vivo short-term microbiological effect without affecting clinical performance of ART restorations.

Since bacteria remain in the dentin following caries removal, restorative materials with antibacterial properties are desirable to help maintaining the residual microorganisms inactive. The adhesive system Clearfil Protect Bond (PB) contains the antibacterial monomer 12-methacryloyloxydodecylpyridinium bromide (MDPB) in its primer, which has shown antimicrobial activity. However, its bactericidal effect against biofilm on the dentin has been little investigated. Objective: The aim of this study was to analyze by confocal laser scanning microscopy (CLSM) and viable bacteria counting (CFU) the MDPB bactericidal effect against S. mutans biofilm on the dentin surface. Material and methods: Bovine dentin surfaces were obtained and subjected to S. mutans biofilm formation in BHI broth supplemented with 1% (w/v) sucrose for 18 h. Samples were divided into three groups, according to the primer application (n=3): Clearfil Protect Bond (PB), Clearfil SE Bond, which does not contain MDPB, (SE) and saline (control group). After the biofilm formation, Live/ Dead stain was applied directly to the surface of each sample. Next, 10 µL of each primer were applied on the samples during 590 s for the real-time CLSM analysis. The experiment was conducted in triplicate. The primers and saline were also applied on the other dentin samples during 20, 90, 300 and 590 s (n=9 for each group and period evaluated) and the CFU were assessed by colonies counting. Results: The results of the CLSM showed that with the Se application, although non-viable bacteria were detected at 20 s, there was no increase in their count during 590 s. In contrast, after the PB application there was a gradual increase of non-viable bacteria over 590 s. Conclusions: The quantitative analysis demonstrated a significant decrease of S. mutans CFU at 90 s PB exposure and only after 300 s of Se application. Protect Bond showed an earlier antibacterial effect than Se Bond.