Surfaces with very poor mechanical and frictional properties can be improved, or even, acquire new properties similar to diamond if good adherent CVD diamond film is obtained on it. In this work, nitrogen ions were sub-implanted on pure molybdenum as a means to enhance CVD diamond film adherence. Deposition time from 2 up to 60 h were used for deposition of 10 to 400 µm thick CVD diamond films with very good adherence on sub-implanted molybdenum substrate. Characterizations were carried out by XPS, X-ray diffraction and nano indentation on prepared surfaces prior to diamond growth and after the onset nucleation. The ionic sub-implantation with nitrogen possibly assists in adhesion, with the creation of a thin layer of nitrates and complexes.

Boron-doped polycrystalline diamond films have been deposited over silicon substrate by hot-filament chemical-vapor-deposition process. A gas mixture of 0,5 vol. % methane and 1 vol. % methanol on hydrogen at a pressure of 50 Torr, have been used. Boric oxide dissolved in methanol have been used as the boron doping source during the diamond growth process. Raman spectroscopy and Scanning Electron Microscopy (SEM) have been performed on the samples. A change of Raman spectra with film doping was observed. The diamond characteristic line at 1333 cm-1 down shifted and its intensity decreased as the film resistivity decreased. On the other hand, a broad peak around 1220 cm-1 appeared and its intensity increased with decreasing film resistivity. No modifications on films morphology have been observed with different boron doping level. The grains were well-faceted with 2 <FONT FACE="Symbol">m</font>m average size