Abstract In search of new materials from industrial waste, aiming at cost, efficiency and reduction of environmental liabilities, this study aimed to evaluate the physical, mechanical, acoustic and thermal characteristics of sandwich panels produced with sheets of Schizolobium amazonicum (paricá) and egg carton core made of cardboard, glued with adhesive phenol formaldehyde (FF), urea formaldehyde (UF) and interleaved the sheets glued with both. The panels were evaluated through thermal, acoustic, physical and mechanical tests. The FF and UF adhesives influenced the physical-mechanical properties of the panels. For thermal conductivity and thermal resistance, it was found that all panels met the normative requirements of NBR 15220 (ABNT, 2005) with emphasis on panels produced with FF. Therefore, the use of paricá sheets 32x12x0.2 cm (length, width and thickness, respectively) and egg box as a core with adhesive, proved to be promising for some uses in civil construction, in addition to adding value to the egg crate residues as thermal and acoustic insulators, can minimize the disposal of raw material in the environment.

Resumo Em busca de novos materiais a partir de resíduos industriais, visando ao custo, à eficiência e à redução do passivo ambiental, este trabalho teve como objetivo avaliar as características físicas, mecânicas, acústicas e térmicas de painéis sanduíche produzidos com lâminas de Schizolobium amazonicum (paricá) e núcleo de caixa de ovos feitos de papelão coladas com o adesivo fenol-formaldeído (FF) e com o adesivo ureia-formaldeído (UF), intercalando-se estas com lâminas coladas com ambos (FF+UF). Os painéis foram avaliados por meio de ensaios térmicos, acústicos, físicos e mecânicos. Os adesivos FF e UF influenciaram nas propriedades físico-mecânicas dos painéis. Para a condutividade térmica e resistência térmica, verificou-se que todos os painéis atingiram as exigências normativas da NBR 15220 (ABNT, 2005), com destaque para os painéis produzidos com FF. Sendo assim, a utilização das lâminas de paricá de 32x12x0,2 cm (comprimento, largura e espessura respectivamente) e de caixa de ovo como núcleo com adesivo se mostrou promissora para algumas aplicações na construção civil, além de agregar valor aos resíduos de caixa de ovo como isolantes térmicos e acústicos, por minimizar o descarte de matéria-prima no meio ambiente.

Abstract This study aimed to use the petiole residues of miriti to partially replace pine wood and evaluate the effects of this incorporation on the physical and mechanical properties of the particleboards. Panels were produced with 0, 25, 50, and 75% of miriti in partial replacement of wood and 12% of urea-formaldehyde adhesive. The chemical-physical properties of miriti residues showed potential particleboard production as they were similar to those of pinewood. For the physical properties, the panels were classified as low density. There was an increase in the compression ratio and, consequently, in the hygroscopicity . For the mechanical properties, it was observed that the modulus of elasticity (MOE) and modulus of rupture (MOR) did not show any statistical differences. For perpendicular traction (PT), there was a significant reduction in 50%. Considering a general analysis of the physical and mechanical properties, up to 40% of mirti can be substituted, as in this situation they meet the properties mentioned in CS-236-66, except for PT for commercialization of the panels.

Resumo O objetivo deste trabalho foi utilizar os resíduos do pecíolo do miriti em substituição parcial da madeira de pinus e avaliar os efeitos dessa incorporação nas propriedades físicas e mecânicas dos painéis aglomerados. Os painéis foram produzidos com 0, 25, 50 e 75% de miriti em substituição parcial de madeira e 12% de adesivo uréia-formaldeído. As propriedades físico-químicas dos resíduos de miriti mostraram potencial de produção de aglomerados, uma vez que foram semelhantes às do pinus. Quanto às propriedades físicas, os painéis foram classificados como de baixa densidade. Houve aumento na taxa de compressão e, consequentemente, na higroscopicidade. Para as propriedades mecânicas, observou-se que o módulo de elasticidade (MOE) e o módulo de ruptura (MOR) não houve diferença estatística. Para tração perpendicular (TP) houve redução significativa de 50%. Considerando uma análise geral das propriedades físicas e mecânicas, é possível uma substituição em até 40% de miriti, pois nessa situação atendem as propriedades mencionadas na CS-236-66, com exceção da TP para a comercialização dos painéis.

ABSTRACT Despite the increasing use of plaster as a construction material, due to its numerous advantages when compared to cement, its use is still restricted, because of its low mechanical resistance and high solubility in water. In this context, research has been carried out related to the addition of nanomaterials to improve the mechanical and physical properties of plaster in civil construction. A highly available, low-cost nanomaterial with excellent properties is nanotalc. In this work, nanocomposites with dimensions of 40 × 40 × 160 mm were produced with ultrafine micronized nanotalc replacing plaster in proportions of 0%; 0.5%; 1%; 1.5% and 2%. The physical and mechanical properties of the nanocomposites were evaluated according to standards. The nanocomposites produced with 1% nanotalc showed satisfactory results for physical and mechanical properties, with an increase of 1.8% in apparent density and 24.12% in compressive strength, and a decrease in water absorption of 6.23%, compared to the composite without the incorporation of nanotalc. The production of nanocomposites with the incorporation of 1% nanotalc is viable and shown to be promising, presenting potential for application as linings and internal partitions, since they showed low water absorption due to the hydrophobicity of nanotalc.

RESUMO O descarte inadequado de polímeros de origem petrolífera contribui para o aumento da poluição ambiental devido ao grande período de tempo que estes materiais levam para degradar. Assim, o desenvolvimento de materiais poliméricos reforçados com resíduos de materiais lignocelulósicos pode proporcionar uma melhor taxa de biodegradação ao polímero, por se tratar de materiais de origem natural, renovável e biodegradável. Neste sentido, o objetivo desta pesquisa foi verificar o potencial de utilização do resíduo de soja como carga em polietileno de baixa densidade (PEBD) através de caracterização físico-mecânica. Foram avaliadas diferentes composições do resíduo de soja em relação à massa total de PEBD 0%, 5%, 10%, 15% e 20%. O resíduo de soja utilizado foi caracterizado quimicamente para determinação do teor de extrativos, lignina, cinzas e hemicelulose. Os pellets formados por extrusão foram prensados a uma temperatura de 160°C sem pressão durante 12 minutos, onde se obteve os corpos de prova para os ensaios físico-mecânicos. Após a produção, os mesmos foram acondicionados em sala de climatização com temperatura de 20±2°C e umidade relativa de 65±3%, sendo posteriormente realizada a determinação da densidade aparente, umidade na base seca, absorção total de água e realizados de flexão e tração. Com base nos resultados, conclui-se que os valores encontrados para os constituintes químicos do resíduo de soja mostram satisfatórios, uma vez que, a substituição parcial do PEBD puro pelo não afetou as propriedades de densidade e resistência à tração do material. O aumento do teor deste resíduo, também contribui para um maior alongamento do polímero. Assim, conclui-se que é possível transformar este polímero de origem petrolífera em um material mais sustentável, tornando algumas propriedades até mais atrativas do que aquelas encontradas no PEBD puro.

ABSTRACT The improper disposal of polymers of petroleum origin contributes to the increase of environmental pollution due to the long period of time that these materials take to degrade. Thus, the development of polymeric materials reinforced with residues of lignocellulosic materials can provide a better rate of biodegradation to the polymer, as they are materials of natural, renewable and biodegradable origin. In this sense, the objective of this research was to verify the potential of using soybean residue as a filler in low density polyethylene (LDPE) through physical-mechanical characterization. Different soy residue compositions were evaluated in relation to the total mass of LDPE 0%, 5%, 10%, 15% and 20%. The soybean residue used was chemically characterized to determine the content of extractives, lignin, ash and hemicellulose. The pellets formed by extrusion were pressed at a temperature of 160 ° C without pressure for 12 minutes, where the specimens were obtained for the physical-mechanical tests. After production, they were stored in an air conditioning room with a temperature of 20 ± 2 ° C and a relative humidity of 65 ± 3%, with the determination of apparent density, moisture on the dry basis, total water absorption and subsequently carried out. flexion and traction. Based on the results, it is concluded that the values found for the chemical constituents of the soy residue are satisfactory, since the partial substitution of pure LDPE by the material did not affect the density and tensile strength properties of the material. The increase in the content of this residue also contributes to a greater elongation of the polymer. Thus, it is concluded that it is possible to transform this petroleum-based polymer into a more sustainable material, making some properties even more attractive than those found in pure LDPE.. Keywords: Polymeric materials. Lignocellulosic waste. Sustainability.