Abstract This study evaluated surface roughness, color stability, whitening index, and opacity of different types of modeling liquids for resin composite coating after exposure to staining and toothbrushing. Disc-shaped resin composite (Vittra APS, FGM) specimens were fabricated and divided into four groups (n = 10 each): control group, Composite Wetting resin (Ultradent Products), Adper Scotchbond Multipurpose adhesive (3M ESPE), and Adper Universal adhesive (3M ESPE). Surface roughness (Ra) was measured using a rugosimeter, while color stability (∆E00), whitening index (WI), and opacity (%) were measured using a spectrophotometer. Assessments were made at four time points: after polishing (baseline, T1), after immersion in red wine for 24 h (T2), and after 5,000 (T3) and 10,000 (T4) cycles of toothbrushing. Scanning electron microscopy images were captured to analyze the scratches created. The data were statistically analyzed by two-way repeated-measures analysis of variance and Tukey’s honestly significant difference tests (α = .05). Modeling with the Wetting resin resulted in higher surface roughness (p < 0.05) and low color stability, which were attributable to porosities. Higher color change values were observed in the control group after staining. Both adhesives showed the lowest mean ΔE00 values (p < 0.005). WI decreased after staining, except with the use of the Universal adhesive (p < 0.005). The lowest opacity values were observed at baseline for all groups (p < 0.005). The Universal and Scotchbond adhesives had lower surface roughness, better color stability, higher WI, and the lowest opacity values after staining with red wine and toothbrushing. toothbrushing Discshaped Disc shaped Vittra APS FGM n 1 each each) Ultradent Products, Products , Products) 3M M ESPE, ESPE ESPE) ESPE. . Ra (Ra rugosimeter ∆E00, E00 E ∆E00 (∆E00) (WI) % (% spectrophotometer points baseline, (baseline T1, T1 T T1) 2 T2, T2 (T2) 5000 5 000 5,00 T3 (T3 10000 10,00 T4 (T4 created twoway two way repeatedmeasures repeated measures Tukeys Tukey s α .05. 05 .05 .05) p 0.05 005 0 porosities ΔE ΔE0 0.005. 0005 0.005 0.005) E0 ∆E0 (∆E00 (WI ( (T2 500 00 5,0 (T 1000 10,0 .0 0.0 0.00 ∆E (∆E0 50 5, 100 10, 0. (∆E

Resumo Este estudo investigou os efeitos da inibição de oxigênio e dos procedimentos de acabamento/polimento nas propriedades das resinas compostas. Foram avaliadas uma resina composta bulk fill e duas resinas convencionais (nanoparticulada e microhíbrida). Os espécimes foram confeccionados, variando o tratamento de superfície: controle, sem tratamento; glicerina (inibidor de oxigênio); acabamento e polimento; glicerina + acabamento e polimento. O grau de conversão (GC) foi medido pela Espectroscopia de Infravermelho Transformada de Fourier (FTIR) imediatamente e após 15 dias da confecção dos espécimes (n=5). Os índices de alteração de cor ΔEab, ΔE00 e opacidade foram avaliados por meio de espectrofotômetro, após 15 dias de imersão no café, utilizando o sistema CIELAB (n=5). Os dados da alteração da cor foram analisados pelos testes ANOVA de dois fatores e Tukey (α=0,05) e a opacidade por ANOVA de medidas repetidas. O uso de glicerina aumentou significativamente o GC, no entanto, não teve influência sobre os valores ΔEab e ΔE00. O acabamento e o polimento reduziram os valores de ΔEab e ΔE00, independentemente da resina composta. A resina microhíbrida apresentou maior opacidade, seguida pela nanoparticula e bulk-fill, independentemente do tratamento de superfície. O acabamento e polimento resultou em menor grau de conversão das resinas compostas se comparado ao uso de um agente inibidor de oxigênio (glicerina), porém apresenta resultados similares para a pigmentação pelo café.

Abstract This study investigated the effects of oxygen inhibition and finishing/polishing procedures on the composite resin properties. One bulk-fill and two conventional composite resins (nanoparticle and microhybrid) were evaluated. Specimens were prepared using 4 surface treatments: control, no treatment; Gly, oxygen inhibition with glycerin; FP, finishing and polishing; Gly + FP, glycerin followed by finishing and polishing. The degree of conversion (DC) was measured using Fourier Transformed Infrared Spectroscopy (FTIR) immediately and after 15 days (n=5). Color stability (ΔEab, and ΔE00) and opacity were evaluated using a spectrophotometer after 15 days of immersion in coffee, using the CIELAB system (n=5). Data were analyzed by two-way ANOVA and Tukey tests (α=0.05) and opacity by two-way repeated-measures ANOVA. Glycerin usage increased significantly the DC however had no influence on the ΔEab, ΔE00 and, opacity values. Finishing and polishing reduced ΔEab and ΔE00 values, regardless of composite resins. Microhybrid showed higher opacity, followed by the nanoparticle and bulk fill, regardless of surface treatment. Post-polymerization polishing procedures resulted in lower conversion than using an oxygen inhibitor agent (Gly condition), but similar staining caused by coffee.

Abstract Purpose: This study determined the effectiveness of the preemptive administration of etodolac on risk and intensity of tooth sensitivity and the bleaching effect caused by in-office bleaching using 35% hydrogen peroxide. Material and methods: Fifty patients were selected for this tripleblind, randomized, crossover, and placebo-controlled clinical trial. Etodolac (400 mg) or placebo was administrated in a single-dose 1 hour prior to the bleaching procedure. The whitening treatment with 35% hydrogen peroxide was carried out in two sessions with a 7-day interval. Tooth sensitivity was assessed before, during, and 24 hours after the procedure using the analog visual scale and the verbal rating scale. Color alteration was assessed by a bleach guide scale, 7 days after each session. Relative risk of sensitivity was calculated and adjusted by session, while overall risk was compared by the McNemar's test. Data on the sensitivity level of both scales and color shade were subjected to Friedman, Wilcoxon, and Mann-Whitney tests, respectively (α=0.05). Results: The preemptive administration of etodolac did not affect the risk of tooth sensitivity and the level of sensitivity reported, regardless of the time of evaluation and scale used. The sequence of treatment allocation did not affect bleaching effectiveness, while the second session resulted in additional color modification. The preemptive administration of etodolac in a single dose 1 hour prior to in-office tooth bleaching did not alter tooth color, and the risk and intensity of tooth sensitivity reported by patients. Conclusion: A single-dose preemptive administration of 400 mg of etodolac did not affect either risk of tooth sensitivity or level of sensitivity reported by patients, during or after the in-office tooth bleaching procedure.

Abstract The aim of the present study was to evaluate the bond strength (BS) of root canal fillings to root dentin using the reciprocating file-matched single-cone or lateral compaction techniques with resin-based and calcium-silicate-based sealers. Maxillary canine roots were prepared and filled using one of the following approaches: Reciproc R40 file and R40 single cone, WaveOne Large file and Large single cone, or ProTaper up to F4 file with lateral compaction. The root filling was performed using AH Plus, Epiphany SE or MTA Fillapex (n = 10). Three 1-mm-thick slices were obtained from each third of each root. Two slices were subjected to a push-out test, and the other slices were prepared for scanning electron microscopy (SEM) to examine the dentin-sealer interface. Data (in MPa) from the push-out tests were analyzed using a two-way ANOVA and Tukey’s test (p < 0.05). Failure modes (adhesive, cohesive or mixed) were evaluated at ×25 magnification. The single-cone techniques resulted in lower BS values than the lateral compaction technique. For lateral compaction, AH Plus and Epiphany SE showed the highest and lowest BS values, respectively. Slight differences were observed between sealers when the single-cone techniques were used. A tendency to reduce the BS toward the apical third was observed. Adhesive failures were predominant for all experimental conditions. A closer adaption of the filling material on the root dentin was observed for the AH Plus and lateral compaction techniques. The Reciproc and WaveOne techniques were associated with lower BS values than the lateral compaction technique. However, the effect of the root canal filling technique appears to be sealer-dependent.

One of the clinically relevant problems dentists face when restoring endodontically treated teeth is the mismatch between fiber post and post space diameters, which results in an excessively thick resin cement layer. Fiber post relining appears as a solution for this problem. OBJECTIVES: The aim of this study was to evaluate the effect of fiber post relining with composite resin on push-out bond strength. MATERIAL AND METHODS: Twenty bovine incisors were selected to assess post retention. The crowns were removed below the cementoenamel junction and the root canals were treated endodontically and flared with diamond burs. The roots were allocated into two groups (n=10): G1: fiber posts without relining and G2: fiber posts relined with composite resin. The posts were cemented with a dual-cured resin cement and the specimens were sectioned transversally. Three 1.5-mm thick slabs were obtained per root and identified as cervical, medium and apical thirds. The push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. The failure mode of fractured specimens was analyzed under scanning electron microscopy. Data were analyzed by split-plot ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. RESULTS: Relined fiber posts presented higher retention values than non-relined post in all thirds. No statistically significant differences (p>0.05) were found among thirds for relined posts. All failures occurred at the interface between resin cement and root dentin. CONCLUSIONS: Relining with composite resin seems to be an effective method to improve the retention of fiber posts to flared root canals.