The aim of this paper was to determine the influence of machining parameters on the surface layer, and consequently on the electrochemical properties, of ASTM F138 austenitic stainless steels. Eight different surface conditions were generated in cylindrical samples by turning and polishing. The surface was characterized by surface roughness Ra and Rt, Vickers microhardness and microstructural characteristics. Cyclic voltammetric tests were performed to evaluate the potential of repassivation and pitting. The surfaces were analyzed by Scanning Electron Microscopy after the electrochemical tests were performed. The cutting parameters were identified to have a significant influence, and the feed rate was as influential as the depth of cut. The use of polishing alone is not sufficient to ensure that a surface has good surface integrity. Even with the polishing application, usually used to produce prostheses, a significant reduction in corrosion resistance occurs if care is not taken to minimize surface machining damage. Corrosion resistance is lower and pitting nucleation is higher in the samples with no polishing and with more severe machining parameters. The tests indicated that softer machining parameters can contribute to an increase in the life of implantable components, reducing the probability of localized corrosion, as well as improving the mechanical properties of prostheses.

Tubos de trocadores de calor de usinas termoelétricas a carvão sofrem desgaste corrosivo devido à presença de enxofre e condensação dos gases da combustão, tendo por consequência uma redução na eficiência global do equipamento. Uma opção para o aumento da resistência à corrosão em meios agressivos é a utilização de revestimentos aplicados pela tecnologia de aspersão térmica. A resistência à corrosão dá-se com o emprego de materiais mais resistentes que o substrato. Dentre os processos existentes de aspersão térmica, o que utiliza o arco elétrico como fonte de energia (Arc Spray), possui alta taxa de deposição e menor custo operacional, sendo assim, escolhido para o estudo. Para a determinação do melhor revestimento a ser utilizado, foram testadas ligas metálicas resistentes à corrosão, em comparação com o material empregado nos tubos dos trocadores de calor, ASTM 178A. A seleção do revestimento mais resistente foi feita por meio de ensaio de corrosão acelerada em câmara de SO2 e também através do ensaio de polarização. Verificou-se que o revestimento de alumínio apresentou os melhores resultados nos testes realizados, quando comparados com material utilizado atualmente nos trocadores de calor (ASTM 178A).

Heat exchangers pipes for thermal power plants to coal suffer wear corrosive due to the presence of sulfur and condensation of combustion gases, which results in a reduction in overall equipment efficiency. A choice for increasing the corrosion resistance in corrosive environments is the use of coatings applied by thermal spray technology. The corrosion resistance occurs to the use of materials stronger than the substrate. the processes are thermal spray, which uses the electric arc as a source of energy (Arc Spray) has a high deposition rate and low operating costs, so chosen for the study. For the determination of the coating to be used, corrosion-resistant alloys were tested in comparison with material employed in the pipes of heat exchangers, ASTM 178A. The selection of the most resistant coating was made by means of accelerated corrosion test in SO2 chamber and also by testing polarization. It was found that the aluminum coating had the best results in the tests when compared with materials currently used in the heat exchangers (ASTM 178A).