Abstract Non-destructive magnetic particle testing is a technique widely used in industry to identify surface and subsurface discontinuities in ferromagnetic materials, both in the manufacturing stages (semi-finished parts) and in service conditions. The parts need to be subjected to a magnetic field, which allows magnetic particles to move and accumulate in areas with discontinuities. However, residual magnetism can cause problems in processing stages such as welding and machining. With this in mind, this study set out to investigate the behavior of parts subjected to magnetic inspection and the possible consequences of residual magnetism. Parts of different chemical compositions were subjected to the test and had the magnetic field strength values measured and underwent welding steps (GTAW). It was possible to identify the low-intensity occurrence of the phenomenon of magnetic blowing during welding. As it does not represent a high risk to the result of the weld, it can be concluded that, for this specific case and under the conditions established for the experiments, demagnetization after the test is optional. Demagnetization after the welding processes can be explained by the increase in temperature above the Curie point. Nondestructive Non destructive materials semifinished semi finished However machining mind GTAW. GTAW . (GTAW) lowintensity low intensity weld that experiments optional point (GTAW

Resumo O ensaio não-destrutivo por partículas magnéticas é uma técnica amplamente utilizada na indústria para identificação de descontinuidades superficiais e subsuperficiais em materiais ferromagnéticos, tanto nas etapas de fabricação (peças semiacabadas) quanto em condições de serviço. As peças precisam ser submetidas a um campo magnético, o qual possibilita a movimentação das partículas magnéticas e o acúmulo em regiões com descontinuidades. Todavia, o magnetismo residual pode ocasionar problemas em etapas de processamento, como a soldagem e usinagem. Nesse sentido, o presente trabalho se propôs a investigar o comportamento de peças que são submetidas a inspeção magnética e as possíveis consequências do magnetismo residual. As peças de diferentes composições químicas foram submetidas ao ensaio e tiveram os valores de intensidade de campo magnético medidos e passaram por etapas de soldagem (GTAW). Foi possível identificar a ocorrência, em baixa intensidade, do fenômeno de sopro magnético durante a soldagem. Por não representar um risco elevado ao resultado da solda, pôde-se concluir que, para esse caso especificamente e sob as condições estabelecidas para os experimentos, a desmagnetização após o ensaio é facultativa. A desmagnetização após os processos de soldagem pode ser explicada pelo aumento da temperatura acima do ponto de Curie. nãodestrutivo destrutivo ferromagnéticos semiacabadas serviço Todavia processamento usinagem sentido GTAW. GTAW . (GTAW) ocorrência solda pôdese pôde experimentos facultativa Curie (GTAW

Resumo: O estudo da fadiga em ambiente subaquático é dificultado pois envolve diversas variáveis, muitas delas estão relacionadas à interação do material com o meio em que está submetido. Em testes de fadiga em ambiente aquoso foi constatado o aparecimento de bolhas que se desprendem da região da ponta da trinca durante o ensaio, porém, até o momento a literatura não havia relatado esse fenômeno. Buscando a repetibilidade, este trabalho apresenta parâmetros de ensaio que promovam o desprendimento de bolhas, facilitando seu estudo e compreensão. Corpos de prova do tipo C(T) fabricados em aço ASTM A36 foram ensaiados em ambiente subaquático sob uma variação de carga constante (ΔP) de 5kN e frequência de 30Hz. Os desprendimentos das bolhas durante os ensaios foram registrados com uma câmera de alta velocidade (captura de 1000fps). Os resultados indicam que as primeiras bolhas desprendidas durante o ensaio são menores e aumentam de volume com o aumento do comprimento da trinca, chegando a um diâmetro médio máximo e após isso ocorre diminuição e supressão do fenômeno ao se aproximar do final do ensaio. A ocorrência foi associada à fragilização por hidrogênio, com existência já comprovada nesse tipo de ensaio

Abstract: The study of fatigue in an underwater environment is difficult because it involves several variables, many of them are related to the interaction of the material with the environment in which it is submitted. In fatigue tests in an aqueous environment, the appearance of bubbles that detach from the crack tip region during the test was observed, however, until now the literature had not reported this phenomenon. Seeking repeatability, this work presents test parameters that promote the detachment of bubbles, facilitating their study and understanding. Type C(T) specimens made of ASTM A36 steel were tested in an underwater environment under a constant load variation (ΔP) of 5kN and frequency of 30Hz. The detachments of the bubbles during the tests were recorded with a high-speed camera (capture of 1000fps). The results indicate that the first bubbles released during the test are smaller and increase in volume with increasing crack length, reaching a maximum average diameter and after that, there is a decrease and suppression of the phenomenon when approaching the end of the test. The occurrence was associated with hydrogen embrittlement, with proven existence in this type of test

Resumo Superfícies de fratura geradas por fadiga em soldas subaquáticas molhadas foram caracterizadas por reconstruções tridimensionais usando estereofotogrametria em um microscópio eletrônico de varredura. Análise de perfil, rugosidade e dimensão fractal foram avaliadas para essas superfícies com o intuito de correlacioná-los com os resultados de ensaios de propagação de trinca e densidade de porosidade. Verificou-se que o parâmetro de rugosidade superficial Sq apresentou-se como mais eficiente para descrever e comparar as superfícies estudadas do que a dimensão fractal. Além disso, pôde-se confirmar a aplicabilidade da técnica usada e da metodologia desenvolvida para o estudo proposto com a ressalva de que um estudo mais aprofundado é necessário para compreender os mecanismos de propagação de trinca por fadiga em soldas subaquáticas molhadas.

Abstract Fatigue fracture surfaces in wet underwater welds were characterized by means of three-dimensional reconstructions using stereophotogrammetry in a scanning electron microscope. Profile analysis, roughness and fractal dimension were evaluated for these surfaces in order to compare them with the results of crack growth tests and welding depth. It could be seen the areal roughness parameter Sq as more effective than the fractal dimension to describe and compare the studied surfaces. In addition, it was possible to endorse the pertinence of the used technique and the developed methodology for the proposed study. Nevertheless, it is stated that further study is required in order to fully understand the mechanisms of fatigue crack propagation in wet underwater welds.