This work investigates the effect of thermal cycling on the microstructure of a stainless steel superduplex, specifically on the sigma phase formation. The examined thermal cycles are similar to those produced in the heat affected zone of stainless steel when applying GTAW welding process. The temperatures and residence time for the cycle was determined using a typical thermal model of temperature distribution. The application of thermal cycles shows the microstructural evolution of steel in the range of 475ºC to 1100ºC with a short heating time and determines the temperature of formation and disolution of the sigma phase, and its maximum temperature of formation. The formation mechanism and chemical composition of the sigma phase is also examined.

Este trabajo investiga el efecto de los ciclos térmicos sobre la microestructura de un acero inoxidable superdúplex específicamente sobre la formación de fase sigma. Los ciclos térmicos examinados son similares a los que se producen en la zona afectada térmicamente del acero inoxidable cuando se aplica el proceso de soldadura GTAW. Las temperaturas y tiempo de permanencia para el ciclo térmico se determinan usando un modelo de distribución de temperatura típico. La aplicación de los ciclos térmicos permite conocer la evolución microestructural del acero en el rango de 475ºC a 1100ºC con un tiempo corto de calentamiento y determinar la temperatura de formación y disolución de la fase sigma, pasando por su temperatura de máxima formación. Se examina la formación preferencial y la composición química de la fase sigma.