The influence of 0.01 mol L-1 NaNO2 addition on the corrosion and passivation of X65 carbon steel in pH 1 to 5 HNO3 solutions was investigated and compared by electrochemical methods and microstructural techniques. In the pH 1 to 5 solutions without NaNO2, the X65 steel presented the electrochemical characteristic of active dissolution, and the corrosion rate of X65 carbon steel decreased gradually with the raise of pH value. By contrast, with the addition of 0.01 mol L-1 NaNO2 in pH 1 to 5 HNO3 solutions, the electrochemical characteristic of X65 carbon steel transferred from the active dissolution in the pH 1 to 5 solutions without NaNO2 to the anodic passivation in the corresponding pH solutions with NaNO2. For the X65 steel in the pH 1 to 5 solutions with NaNO2, with the raise of pH value, the corrosion rate also decreased gradually but the passivation capability strengthened obviously. The corrosion and passivation of X65 carbon steel in pH 1 to 5 HNO3 solutions without and with 0.01 mol L-1 NaNO2 were related to the cathodic reactions of H+ reduction, O2 reduction and NO2-/HNO2 reduction.

For Q235 carbon steels in 0.01 mol L-1 NaNO2-HCl solutions with different pH values, the effects of pH values on the functional mechanisms of nitrite anions (NO2-) were studied. In the pH 1 and pH 2 solutions, the Q235 steels showed the electrochemical behavior of activation, and uniform corrosion (UC) was the main corrosion type on the Q235 surface. The presence of NO2- did not affect the electrochemical behavior and the corrosion type but only accelerated the anodic reaction of Fe oxidation. In the pH 3 and pH 4 solutions, the Q235 steels presented the electrochemical behavior of activation-passivation transition, and intergranular corrosion (IGC) occurred on the Q235 surface. The cathodic reaction of NO2- reduction resulted in the transition of electrochemical behavior from activation to passivation and the change of corrosion type from UC to IGC. In the pH 5 and pH 6 solutions, the Q235 steels exhibited the electrochemical behavior of self passivation-pitting, and pitting corrosion (PC) was present on the Q235 surface. The strong oxidability of NO2- played a critical role in the formation of γ-Fe2O3 passive film on the Q235 surface under the combined action of Fe2+ and NO2-.

Abstract This study aimed to investigate the cardioprotection of rosuvastatin pre-conditioning (R-Pre) in a rat model of myocardial ischemia / reperfusion (I/R). Male SD rats were assigned into three groups: sham group, I/R group and R-Pre group. Rats in I/R group and R-Pre group received ischemia for 30 min and reperfusion for 2 h. In R-Pre group, rats received intragastrical administration with rosuvastatin at 5 mg/kg once daily for 1 week. After 2-h reperfusion, the cardiac function was detected by ultrasonography; the blood was collected for biochemical analysis; the heart was collected for the TUNEL staining and immunohistochemistry for Bcl-2 and Bax. Our results showed rosuvastatin pre-conditioning for 1 week could significantly reduce the infarct ratio and improve the cardiac function after myocardial I/R injury, in which attenuation of oxidative stress and cell apoptosis played an important role. Our study provides evidence on the cardioprotection of rosuvastatin pre-conditioning and highlight the use of rosuvastatin before cardiopulmonary bypass.

ABSTRACT Phleum paniculatum Huds., commonly known as British timothy, is an increasingly serious weed in wheat field of China. However, the biology of its seed germination and seedling emergence remain unclear. In the present study, the effects of environmental factors on seed germination and seedling emergence of P. paniculatum were explored. Phleum paniculatum seeds had a shallow dormancy (20-30 d) when stored at room temperature (25 ± 5 °C). Seeds could germinate at constant temperatures between 10 and 25 °C, except for 5 or 30 °C. Light was not essential for seed germination, and pH values from 4 to 10 did not inhibit germination. Seeds were moderately adaptable to water potential and NaCl concentration, and germination rates would be decreased 50% when water potential was -0.4 MPa or NaCl concentration was 130 mM. Increased soil burial depth decreased the seedling emergence, and no seeds emerged when the burial depth was more than 4 cm. Taken together, our results provide useful information of the germination and emergence of P. paniculatum seed, and strategies such as proper drainage systems managed and deep plowing are recommended to limit its detrimental effects on agricultural production.

For carbon steels immersed in CO2 saturated solutions at different temperatures, the structure and the composition of corrosion product film formed on the steel surface were studied by scanning electron microscope (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The corrosion rate of the steel was evaluated by potentiodynamic polarization, and the relation between the corrosion rate and the film property was discussed. The corrosion rate of the steel was very closely associated with the structure and the composition of corrosion product film, which were affected significantly by the solution temperature. From 30 to 60 ºC, the corrosion product film composed of FeCO3 was porous and poorly adherent, and the corrosion rate increased with the rise of temperature. At 70 and 80 ºC, the corrosion product film was also composed of FeCO3 and presented a compact and dense cubic crystal structure, resulting in the decrease on the corrosion rate. The corrosion rate increased once again when the temperature was up to 90 ºC, which was attributed to the negative effect of high temperature water vapor corrosion on the grain coarsening and the part exfoliation for the FeCO3 film.

Ni-Co alloy and ZrO2 micron particles were codeposited on 45 carbon steel by electrodeposition. The composition and microstructure of the composite coating were characterized. The high temperature tribological properties were carried out by a pin-on-disk tribo-tester. Additionally, the oxidation resistance was evaluated via high temperature circulating oxidation test. The results indicated that the deposited composite coating showed dispersed ZrO2 particles and continuous Ni-Co matrix, and there were no obvious pores, cracks and other defects at the interface between the composite coating and the substrate. The embedded ZrO2 particles changed the friction mechanism from adhesive wear to abrasive wear, the wear loss rate and friction coefficient of Ni-Co-ZrO2 composite coating were lower in comparison with that of Ni-Co alloy coating and carbon steel substrate. In addition, the embedded ZrO2 particles exerted a reactive-phase effect on the growth of nickel oxide and cobalt oxide, and effectively reduced the oxidation rate of the substrate at high temperature. Therefore, the Ni-Co-ZrO2 composite coating presents better oxidation resistance, when compared with Ni-Co coating.

Crop growth in a saline environment depends on its tolerance to salt stress and capacity to recover after salt stress relief. To evalúate recovery mechanisms in cotton after salt stress relief, the changes of plants growth, root vigor, lipid peroxidation, antioxidant enzymes activity, organic solutes in root after salt stress relief were studied for two cotton (Gossypium hirsutum L.) cultivars (Lumianyan 37 and Sumian 22) grown under control (salt content of soil grown cotton was maintained at 0.2%), salt stressed (salt content of soil grown cotton was maintained at 0.5%) and salt recovered (salt content of soil grown cotton was reduced from 0.5% to 0.2% level at the 57 d after seeding) conditions. The results showed that root and shoot growth rate and root vigor significantly increased after salt stress relief, and the increase in growth rate and root vigor was more pronounced in ’Lumianyan 37’. In salt-recovered root, malondialdehyde (MDA) content decrease, the activities of superoxide dismutase (SOD) and peroxidase (POD) decreased, but catalase (CAT) activity increased compared with those in the salt-stressed root. For salt-recovered root, MDA content and POD activity of ’Lumianyan 37’ was lower, while the SOD and CAT activities were higher. Salt-recovered cotton root showed a decrease in soluble sugar and free amino acid content compared with the salt-stressed root, especially in ’Lumianyan 37’. The results indicated that growth and root metabolism of cotton plants gradually recovered after salt stress relief, and the high capacity of cotton plants to recover after salt stress relief may be related to the high capacity of antioxidative system and the high utilization capacity of organic solutes as important nutritional components in root.