Abstract One of the major health security challenges of the 21st century is the occurrence of microbial infections and bacterial complications that could affect 10 million people by 2050. On the biomaterial field, implant metallic currently replaces partial or total body parts and can fail to be integrated into the body due to infections. This study performs two combined surface modifications on Ti-30Ta alloy, in order to obtain an infection-resistance and osseointegration surface on metallic implants to be tested within bacterial biofilm. The Group 1 investigated surface modifications by the anodization process in the electrolyte glycerol + NH4F 0.25% at 30V- 9 hours and annealed in 530°C (5°C/min). The Group 2 underwent the same process as Group 1 and, additionally, the samples were immersed in 0.3 M CaCl2 and 0.5 M Na2HPO4 solutions for hydroxyapatite growth. The substrate was characterized using scanning electron microscopy (SEM), X-ray diffractometer (XRD) and dynamic contact angle. S. epidermidis bacterial adhesion and biofilm formation. The results indicated that the Group 1 shows a higher antimicrobial activity, hydrophilic behavior and potential to be used for metallic implant applications. The Group 2 with the hydroxyapatite film coating did not have an improvement in the antimicrobial response.

Several studies have been carried out to develop new materials for biomedical applications. Material surfaces that present biomimetic morphology like nanotubes or nanofibers that provides nanoscale architectures have been shown to alter cell/biomaterial interactions. The coated surface biomaterial with biocompatible polymers and nanotubes of TiO2 is an alternative to improve osseointegration. The anodization process was performed to obtain nanotubes of TiO2 covering the Ti-30Ta alloy surface and the electrospinning process has been used for producing polymer fibers. Characterization techniques such as scanning electron microscopy (SEM - FEG), X-ray diffraction analysis (X-rays), thermogravimetric analysis (TGA), Differential Scanning Calorimetry (DSC) and contact angle were used for samples analyses. Adult human adipose-derived stem cells (ADSCs) were used to investigate the cellular response and S. aureus antimicrobial activity on these coated surfaces. The results indicated that both surface modification treatment showed a favorable micro-environment for cells growth and proliferation such as adhesion, viability and morphology which is a desire property for an implant. In addition, the antimicrobial activity study presented both materials with similar growth of S. aureus. So, it can conclude nanotubes and nanofibers can be used at biomedical field and both present similar cell evaluation and antimicrobial activity results.