The present study describes a new procedure to obtain gold nanoparticles, directly in the pores of polycarbonate membranes commonly used in ultrafiltration. The dimensions of the particles may be controlled through the reduction time of the ions in the channels of the harbor matrix. The dissolution of the metallized polymer enables an investigation of the optical and morphologic properties of these elements.

Nanomaterials make up an emerging area in Chemistry and in the science of materials. This area constitutes the development of methods for synthesizing nanoscopic particles of a given material used for scientific investigation. Nanomaterials have a wide range of commercial possibilities and technological applications, including their use in analytical chemistry, as well as in electronics, optics, engineering, medicine, devices for liberation of drugs, bioencapsulation, among others. This paper presents a summary about nanoelectrodes, devices built from nanoparticles, which show great potential as electrochemical tools in many different types of analysis. The purpose of this paper is to review the construction methodologies of nanoelectrodes, and to point out their successful applicability in the various fields of immune assays and other analytical procedures with quantitative purposes.

Filmes ultrafinos do polímero perfluorado Nafion® foram depositados em eletrodos de óxido índio-titânio (ITO) usando a técnica de Langmuir-Scaefer (LS), depois da otimização das condições de composição da subfase. As características morfológicas das camadas foram obtidas por Microscopia de Força Atômica (AFM). Filmes de Nafion® LS mostraram boa uniformidade e cobertura completa da superfície do eletrodo. No entanto, diferentes graus de organização das camadas poliméricas ficaram evidentes com respeito a filmes finos depositados por revestimento rotacional. Eletrodos ITO modificados com camadas de Nafion® LS, pré-concentrados por cátions eletroativos de troca iônica, como o Ru[(NH3)6]3+, dissolveram-se em soluções diluídas. A espécie eletroativa foi retida pelo ITO com camada de Nafion® LS, mesmo depois da mudança do eletrodo modificado para eletrodo de suporte purificado. Isto possibilitou o uso do complexo de rutênio como padrão voltamétrico para o teste do fenômeno de difusão nos filmes de Nafion® LS. Os coeficientes de difusão aparentes (Dapp) do Ru[(NH3)6]3+ incorporado no filme de Nafion® LS foram obtidos por medidas voltamétricas. Os valores de Dapp diminuíram levemente com o aumento da quantidade de complexo de rutênio incorporado no filme ultrafino e foram significativamente mais baixos do que os valores para filmes de Nafion® recapados, em acordo com a natureza altamente condensada dos filmes de Nafion® LS.

Ultrathin films of Nafion® perfluorinated polymer were deposited on indium-tin oxide electrodes (ITO) by using Langmuir-Schaefer (LS) technique, after optimization of the subphase composition conditions. Morphological characteristics of these coatings were obtained by Atomic Force Microscopy (AFM). Nafion® LS films showed a good uniformity and complete coverage of the electrode surface, however a different organization degree of the polymer layer was evidenced with respect to thin films deposited by spin-coating. ITO electrodes modified with Nafion® LS coatings preconcentrate by ion-exchange electroactive cations, such as Ru[(NH3)6]3+, dissolved in diluted solutions. The electroactive species is retained by the Nafion® LS coated ITO also after transfer of the modified electrode into pure supporting electrolyte. This allowed the use of the ruthenium complex as voltammetric probe to test diffusion phenomena within the Nafion® LS films. Apparent diffusion coefficients (Dapp) of Ru[(NH3)6]3+ incorporated in Nafion® LS films were obtained by voltammetric measurements. Dapp values decrease slightly by increasing the amount of ruthenium complex incorporated in the ultrathin film. They are significantly lower than values typical for recasted Nafion® films, in agreement with the highly condensed nature of the Nafion® LS fims.