Abstract The biodegradable aliphatic oligoester oligo(trimethylene separate) (OTS) was synthesized by polycondensation and used to plasticize poly(lactic acid) (PLA). Casting films of PLA and PLA/OTS with concentrations of 1, 5 and 10 wt.% were prepared, and these films were characterized by thermal analyses, crystallinity, rheology and mechanical tests. DSC revealed the decrease in the Tg of PLA films with addition of the oligomer and a partial immiscibility. Addition of OTS to PLA slightly decrease the thermal stability as well as increase the degree of crystallinity of these films. Dynamic-mechanical analyses of casting films showed that the PLA/OTS system presented lower storage modulus than PLA and mechanical test revealed an increased in the elongation at break for PLA films containing the oligoester. The results make possible to conclude that the oligomer synthesized from bio-based monomers acts as a plasticizer of PLA increasing the PLA ductility.

Poly(lactic acid)/Somasif fluoromica nanocomposites were prepared by melt blending and their thermal properties investigated by DSC, TGA and DMA. Three different types of synthetic mica (Somasif ME-100, Somasif MAE and Somasif MPE) were used at different contents (2.5, 5.0 and 7.5 wt %). The melt blending of PLA and these micas is characterized by a considerable reduction in the matrix molecular weight, which decreases when the nanofiller content is increased. For all nanocomposites, the thermal stability increases when mica is added to the polymer, with the Somasif MPE, producing the highest increase of the degradation temperature and highest reduction of Tg.