This paper reports on the preparation, characterization and study of the ion exchange behavior of hydrous zirconium oxides formed by homogeneous precipitation from zirconium oxychloride. The precipitants used were obtained by thermal decomposition of urea, sodium nitrite or ammonium carbonate. Seven compounds were prepared and characterized by thermal analysis, X-ray diffractometry and by surface area measurements. Amorphous forms were obtained in each case, a result that agrees with those obtained by conventional gel precipitation methodology. All these materials present surface area values of >148 m².g-1, determined after heat treatment at 50 °C. The ion exchange behavior of each hydrous zirconium oxide prepared was studied using K+ as the exchanged species and the results compared with those obtained for hydrous zirconium oxide originally precipitated by the sol gel method.

This work describes two methods of preparation of hydrous tantalum phosphates and their characterization as ion exchangers. The hydrous metallic phosphate compounds were chemically and physically characterized by thermal gravimetric analysis, X-ray diffractometry and surface area measurements. By the first method, tantalum phosphate was prepared by alkaline fusion of Ta2O5 with an excess of K2CO3, followed by lixiviation of the tantalate fusion product with hot water, and precipitation with diluted H3PO4. Preparation II was performed using metallic Ta dissolved in concentrated HF/HNO3 acidic mixture followed by hydrolysis of fluortantalic acid intermediary and precipitation with diluted H3PO4. Both freshly prepared materials (I and II) were exaustively refluxed with concentrated H3PO4, in its boiling point temperature, resulting respectively in Ta2O5. 2.1 H2O, (IR) and Ta2O5. 1.3 H2O, (IIR). Characterization of the prepared products have presented the following values: surface area of 108.27 ± 2.80; 220.14 ± 2.67; 117.07 ± 5.25 and 141.61 ± 0.27 m².g-1 respectively for I, IR, II and IIR. All these materials were amorphous. The ion exchange behavior for all four hydrous tantalum phosphates was studied using Na+, K+ and Ba+2 as the exchanged species. The values for typical ion exchange capacity were 1.64; 1.23; 1.47 and 1.01 miliequivalent.g-1, respectively for I, IR, II and IIR products.