Siloxane-poly(methyl methacrylate) (PMMA) organic-inorganic hybrid coatings were deposited on galvanized steel by the dip-coating sol-gel technique. Anticorrosion properties, as well as the morphological, surface and structural features were studied. Hybrid coatings were synthesized from tetraethoxy-silane (TEOS) and methyl methacrylate (MMA) as inorganic and organic phases, respectively, linked by 3-metacriloxypropyl-trimethoxysilane (TMSM) as a coupling agent. The MMA/TMSM ratio was kept constant, whereas the four TEOS/TMSM ratios were varied. The characterization of coatings was assessed using several techniques such as Scanning Electronic Microscopy (SEM), Contact Angle, Fourier Transform Infrared (FT-IR), Open Circuit Polarization (OCP), Atomic Force Microscopy (AFM) and Electrochemical Impedance Spectroscopy measurements (EIS). The EIS results, which were obtained for the hybrid coatings, were discussed based on an electrical equivalent circuit used to adjust the experimental data. The results showed that the increasing the TEOS content caused increase in coating thickness, increased in the surface roughness and increased in the surface hydrophobicity. The film with the highest TEOS content presented the best electrochemical performance, more effective in protecting against corrosion.

Tinplate is used to food packaging and other types of packages. The corrosion resistance of the tinplate has been study due the necessity of an alternative to high environmental impact of chromatization process. Therefore protective coatings as hybrid films base elaborations with different acids are studied to improve the barrier effect against corrosion. The objective of this work is characterize hybrid films deposited on a tinplate from a sol made up of the alkoxide precursors 3-(trimethoxysilylpropyl)methacrylate (TMSM), tetraethoxysilane (TEOS) and poly(methyl methacrylate) (PMMA) together with one of three acids (acetic, hydrochloric or nitric acid) and to verify their action against the corrosion of the substrate. The films were obtained by a dip-coating process and cured for 3 hours at 160 °C. The film hydrophobicity was determined by contact angle measurements, and the morphology was evaluated by SEM. FTIR measurements were performed to characterize the chemical structures of the films. The electrochemical behavior of the coatings was evaluated by techniques open circuit potential monitoring (OCP), potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results demonstrate that the siloxane-PMMA films improve the protective properties of the tinplate, with the films obtained by acetic acid addition exhibiting the greatest improvement.

The tetraethoxysilane (TEOS) influences morphological and electrochemical properties of hybrid films by function of concentration. Moreover, the use of acetic acid as a catalyst in the sol enables a more complete hydrolysis of the silane precursors due to the fact that the acetic acid goes through a more complete ionization when in aqueous solution. The aim of this paper is to study the effect of the concentration of tetraethoxysilane (TEOS) on the protective properties of the film on tinplate substrate. The tinplate was coated with a hybrid film obtained from a sol-gel method constituted of the following alkoxide precursors: 3 - (trimetoxisililpropil) methacrylate (TMSM) and poly(methyl methacrylate) PMMA. The effect of tetraethoxysilane (TEOS) concentration has also been evaluated. The films hydrolysis was performed at a pH value of 3. 0 using acetic acid as a catalyst. The films were obtained by dip-coating process, cured for 3 hours at 160 ºC. The film morphology was evaluated by SEM and profilometry. The electrochemical behavior of the films was evaluated by open circuit potential monitoring, potentiodynamic polarization and electrochemical impedance spectroscopy. The film hydrophobicity was determined by contact angle measurements. The studied films have shown good performance as to corrosion resistance on tinplate. The hybrid film which was obtained through the addition of an excessive amount of TEOS (T3A3) showed increased thickness. Nevertheless, due to an intense densification of the film, promoted by the addition of TEOS, a formation of cracks was registered, thereby compromising the corrosion resistance.