ABSTRACT This study evaluated the influence of different levels of power density on resin polymerization in the staining of composite resins. Thirty-six specimens were made with composite resin (Z350 3M ESPE) with cylindrical Teflon matrix (8 mm X 1 mm). The light curing was performed with different degrees of power density for each group (n=12): 300mW/cm², 700mW/cm² e 1000mW/cm². Afterwards, the specimens had their color checked, with the help of a spectrophotometer and immersed in coffee solution during 7 days. After, a new measuring was done (CIEL*a*b* color system). Results showed, for Δa, only G1000 group obtained a significantly lower value, and the same result was found in the evaluation of Δb. For ΔE and ΔL, no significant differences were found between groups. It is concluded that, low and medium power density entails more reddish and bluish composite resin, while the specimens submitted to high power density and then immersed in coffee did not present color change in a short term.

OBJETIVO: Além da agressão química devido à penetração dos géis clareadores na polpa durante o clareamento de dentes com vitalidade pulpar, outro possível fator agressor pode ser o calor gerado pela reação de oxidação exotérmica do gel clareador, que pode também ser agravada pela fotoativação. Este estudo avaliou a variação da temperatura na câmara pulpar de dentes humanos, utilizando-se três diferentes géis clareadores, com ou sem fotoativação. METODOLOGIA: Trinta pré-molares humanos foram cortados longitudinalmente para obtenção de duas metades: vestibular e lingual. Os 60 espécimes foram divididos em 3 grupos e os agentes clareadores utilizados variaram como segue: peróxido de hidrogênio 35% (WHP), peróxido de carbamida 37% (W) e peróxido de hidrogênio 38% (OX). Metade dos espécimes foi submetida ao clareamento com fotoativação e, a outra metade, sem fotoativação. A fonte de luz utilizada foi o aparelho à base de diodo emissor de luz (LED, 3-Light, Clean Line) e as temperaturas foram medidas por um termômetro digital. Os dados foram analisados por análise de variância e teste de Tukey (alfa=5%). RESULTADOS: Os resultados de temperatura foram: sem fotoativação (WHP= 0.68b; W= 0.40b; OX= 0.48b); com fotoativação (WHP= 2.35a; W= 1.60a; OX= 1.80a). CONCLUSÃO: A fotoativação dos géis clareadores com LED contribuiu para um maior aumento de temperatura na câmara pulpar, mas não se atingiu a temperatura crítica de 5,5ºC.

PURPOSE: In addition to the chemical damage due to bleaching gels penetration into the pulp during pulp vitality dental bleaching, another possible aggressive factor could be the heat generated by the exothermal oxidation reaction of the bleaching gel, which may also be aggravated by the use of light activation. This study assessed the temperature variation in the pulp chamber in human teeth, using three different bleaching gels with or without LED light activation. METHODS: Thirty human pre-molars were cut longitudinally to obtain buccal and lingual halves. The 60 specimens were divided into 3 groups, and the bleaching gel used varied as follows: 35% hydrogen peroxide (WHP); 37% carbamide peroxide (W) and 38% hydrogen peroxide (OX). Half of the specimens were submitted to bleaching with light activation and, the other half, without light activation. The light source used was the light emitting diode appliance (LED, 3-Light, Clean Line), and the intrapulpal temperatures were measured by using a digital thermometer. Data were analyzed by ANOVA and Tukey's tests (alpha=5%). RESULTS: The intrapulpal temperatures (inºC) were as follows: without light activation (WHP= 0.68b; W= 0.40b; OX= 0.48b); with light activation (WHP= 2.35a; W= 1.60a; OX= 1.80a ). CONCLUSION: LED light activation of bleaching gels increased the temperature in the pulp chamber, but did not achieve the critical temperature value of 5.5ºC.

The aim of this in vitro study was to compare the photoactivation effects of QTH (Quartz-Tungsten-Halogen) and LED (Light-Emitting Diode) on the SBS (Shear Bond Strength) of orthodontic brackets at different debond times. Seventy-two bovine lower incisors were randomly divided into two groups according to the photoactivation system used (QTH or LED). The enamel surfaces were conditioned with Transbond self-etching primer, and APC (Adhesive Pre-Coated) brackets were used in all specimens. Group I was cured with QTH for 20 s and Group II with LED for 10 s. Both groups were subdivided according to the different experimental times after bonding (immediately, 24 h and 7 days). The specimens were tested for SBS and the enamel surfaces were analyzed according to the Adhesive Remnant Index (ARI). The statistical analysis included the Tukey's test to evaluate the main effects of photoactivation and debond time on SBS. The Chi-square test was used to compare the ARI values found for each group, and no statistically significant difference was observed. The debond time of 7 days for QTH photoactivation showed statistically greater values of SBS when compared to the immediate and 24 h periods. There was no statistically significant difference between the QTH and LED groups immediately and after the 24 h period. In conclusion, bonding orthodontic brackets with LED photoactivation for 10 s is suggested because it requires a reduced clinical chair time.