Abstract: The aim of this study is to evaluate the machinability of four CAD/CAM materials (n = 13) assessed by brittleness index, Vickers hardness, and fracture toughness and interaction among such mechanical properties. The materials selected in this in vitro study are Feldspathic ceramic [FC], Lithium-disilicate glass ceramic [LD], leucite-reinforced glass ceramic [LR], and nanofilled resin material [RN]. Slices were made from the blocks following original dimensions 14 × 12 × 3 mm (L × W × H), using a precision slow-speed saw device and then surfaces were regularized through a polishing device. Brittleness index and fracture toughness were calculated by the use of specific equations for each one of the properties. The Vickers hardness was calculated automated software in the microhardness device. One-way Anova and Pearson's correlation were applied to data evaluation. LD obtained the highest values for brittleness index and was not significantly different from FC. LR presented statistically significant difference compared with RN, which had the lowest mean. Vickers hardness showed LD with the highest average, and no statistical difference was found between FC and LR. RN presented the lowest average. Fracture toughness showed FC and LR not statistically different from each other, likewise LD and RN. The brittleness index, considered also as the machinability of a material, showed within this study as positively dependent on Vickers hardness, which leads to conclusion that hardness of ceramics is related to its milling capacity. In addition, fracture toughness of pre-sintered ceramics is compared to polymer-based materials.

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different non-metallic post. Eighty mandibular incisors were endodontically treated and randomly divided in 10 groups (n = 8): G1- restored with composite resin (CR), G2- CR + fiber-reinforced composite post (FRC, Everstick post, Sticktech) cemented with resin cement self-etch adhesive (RCS, Panavia F 2.0, Kuraray), G3- CR + FRC + self-adhesive resin cement (SRC, Breeze, Pentral Clinical), G4- CR+ glass fiber post (GF, Exacto Post, Angelus) + RCS, G5- CR + GF + SRC. The G6 to G10 were bleached with hydrogen peroxide (HP) and restored with the same restorative procedures used for G1 to G5, respectively. After 7 days storage in artificial saliva, the specimens were submitted to the compressive strength test (N) at 0.5 mm/min cross-head speed and the failure pattern was identified as either reparable (failure showed until 2 mm below the cement-enamel junction) or irreparable (the failure showed <2 mm or more below the cement-enamel). Data were analyzed by ANOVA and Tukey test (α = 0.05). No significant difference (p < 0.05) was found among G1 to G10. The results suggest that intracoronal bleaching did not significantly weaken the teeth and the failure patterns were predominately reparable for all groups. The non-metallic posts in these teeth did not improve fracture resistance.

The purpose of this study was to evaluate the transmittance of seven different composite resins. Ten specimens were prepared (10 mm diameter, 2 mm thickness) for each experimental group, as follows: G1- Charisma® A2 (Heraeus-Kulzer); G2- FiltekTM Supreme A2E (3M/ESPE); G3- FiltekTM Supreme A2B (3M/ESPE); G4-FiltekTM Supreme YT (3M/ESPE); G5- Esthet-X® A2 (Dentsply); G6- Esthet-X® YE (Dentsply); G7- Durafill® A2 (Heraeus-Kulzer) and G8- FiltekTM Z-100 A2 (3M/ESPE). The transmittance mode was measured using a UV-visible spectrophotometer (Cary Instruments) at 400-760 nm. The specimens were evaluated at three different times: zero hour (initial), 24 hours and 10 days after immersion in artificial saliva. The differences in transmittance were determined by two-way analysis of variance (ANOVA) and Tukey's test. The various composite resins showed significant differences in the wavelength dependence of transmittance. The mean values of transmittance increased significantly, with wavelengths increasing from 400 to 760 nm. The performance of the experimental groups was similar in terms of immersion time, considering that at time zero and after 10 days, all the groups showed similar results, which were statistically higher than the values obtained after 24 hours of immersion. The FiltekTM Supreme YT composite resin presented the highest mean transmittance values along the wavelengths at the three measured times. Esthet-X® YE and Durafill® yielded similar mean transmittance values, which were higher than those of the other groups. This study shows that the transmittance values of composite resins are directly related with the type, size and amount of inorganic filler particles.