Abstract In this research, oven-dry density, air-dry density, and water absorption levels of Oriental beech treated with flame-resistant chemicals (FRC) and coated with polyurethane/polyure (PU) and epoxy (EP) were evaluated. According to ISO 3129 standard, the experimental specimens were made from Oriental beech wood. Wood specimens were subjected to 3% aqueous solutions of boric acid, borax, a boric acid and borax mixture (1:1; weight: weight), ammonium sulphate, and polyurethane/polyurethane, and epoxy resins before being coated with these substances. Results showed that oven-dry and air-density values of PU coated wood were much higher than EP coated wood. Water absorption (WA) levels of PU coated of wood were lower than EP coated wood. While FRC treated and PU coated wood resulted in lower WA levels than only PU coated wood, FRC treated and EP coated wood resulted in higher WA levels than only EP coated wood.

Abstract In this study, the hybrid Entropy-TOPSIS method is applied to the problem of selecting an optimal impregnation material with maximum performance requirements. Swelling, shrinkage, bending strength, modulus of elasticity, compressive strength and shock strength values were used to rank the impregnation materials. Barite, boric acid, borax and their mixture were used to impregnation material. The impregnation materials used in the study generally increased the physical and mechanical properties of the spruce specimens, except swelling. The impregnation materials reduced the swelling of the specimens. According to the entropy method, the most important factor affecting the success of the impregnation process was the modulus of elasticity. According to the TOPSIS method, the most successful impregnation material was a mixture of barite and boric acid. Moreover, the proposed method was compared with other Multi-Criteria Decision-Making (MCDM) approaches and it can be used to ranking of impregnation materials with reliable accuracy. EntropyTOPSIS Entropy requirements Swelling shrinkage elasticity Barite acid specimens Moreover MultiCriteria Multi Criteria DecisionMaking Decision Making MCDM (MCDM accuracy

Abstract: This study was designed to investigate the weathering characteristics of Calabrian pine (Pinus brutia) wood. The wood specimens were impregnated with some copper-based chemicals and then varnish coated. As copper-based chemicals, Celcure C4, Korasit KS, and Tanalith E 8000 were used for impregnation. Polyurethane varnish (PV) and water-based varnish (WBV) were used as coating materials. Firstly, Calabrian pine wood was impregnated with 2,5 % and 5 % aqueous solutions of chemicals then coated with PV and WBV. Impregnated and coated Calabrian pine wood specimens were subjected to 6 months of natural weathering in Muğla, Turkey. After weathering, surface hardness, surface roughness, and adhesion strength changes of Calabrian pine wood specimens were determined. Impregnation caused to increase in surface hardness values of Calabrian pine. Surface hardness increases of WBV coated Calabrian pine specimens were higher than that of PV coated Calabrian pine specimens. Impregnation resulted in higher surface roughness values of Calabrian pine specimens. PV coated Calabrian pine specimens gave higher surface roughness than that of WBV coated Calabrian pine specimens. The adhesion strength values of all treatment groups were decreased after weathering. In general, adhesion strength decreases of WBV coated Calabrian pine specimens were higher than that of PV coated Calabrian pine specimens. The concentration levels of chemicals did not have a significant effect on surface roughness and adhesion strength of Calabrian pine wood after weathering.

Abstract In the study, sweetgum tree (Liquidambar orientalis), which is an endemic species that grows in Mugla, Köyceğiz and is applied for medicinal purposes among the public, its leaves was examined. The antioxidant ability of the extract obtained from dried plant leaves has been evaluated using a variety of methods which are Total Phenolic Substance, Total Flavonoid, FRAP, CUPRAC, DPPH, and ABTS+. Simultaneously, the antimicrobial activity of the plant extract was examined using disk diffusion and microdilution methods to determine the minimum inhibitor concentration (MIC). While the total phenolic content of Liquidambar orientalis extract was 96.34 mg GAE/g, the total amount of flavonoid was 2.15 mg QE/g. When the results of the antioxidant analysis were examined, it was observed that it had a good level of antioxidant activity with the results of 49.25 ± 0.54 mmol TEAC/g according to the CUPRAC method, 39.83 ± 0.25 µmol Fe/g according to the FRAP method, 80.34 μg/mL according to the DPPH method and 51.20 μg/mL according to the ABTS+ method. As a result of the antimicrobial analysis, it was indicated that L. orientalis extract was more effective on Staphylococcus aureus (S. aureus), which is a gram-positive bacterium and causes a wide variety of clinical diseases. Even, L. orientalis extract with an MIC value of 10 mg/mL has been found to have a higher antibacterial effect than Amoxicillin+Clavulanic acid, which is used as a standard drug in that field. This research is significant because it is the first to report the determination of all biological activities for L. orientalis, including total polyphenols, flavonoid contents, antioxidant content, and antimicrobial activity.

Abstract In this study, four different wood species walnut (Juglans regia L.), chestnut (Castanea sativa Mill.), Poplar (Populus nigra), scotch pine (Pinus sylvestris L.) were chosen and test samples were prepared according to TS 2470 principles. Especially the pine wood by taking the structure (with fungus, fungus/insect, insect), flawless wood structure is compared with the flawed wood structure. The impregnation process was carried out according to ASTM D 1413 -76 principles. Effects of the chemical characteristics of the determined Stone Water (Firetex) on the thermal decomposition properties of wood (burning degrees, degradation temperature points and residue amount) were determined with TGA (thermogravimetric analysis). According to the results of the experiment; the highest retention value was found in poplar (23.56%) and the lowest retention (12.79%) in chestnut was determined. Amount of residue; 60.84% of the highest on scotch pine wood with fungus and 56.70% of the lowest value was determined on poplar wood. Thermal deterioration was determined between 226.41-405.04 oC on wood .