Abstract The present research aims to evaluate the incorporation of vegetable biomass ash, eucalyptus chips (ECA), sugarcane bagasse ash (SCBA) and rice husk ash (RHA), in mixed mortars of cement and lime, considering its properties and mechanical performance. The volume ratio was 1: 1: 6 for a partial replacement of Portland cement at a rate of 15 and 30%. The tests for the residues were a characterization of the particles and pozzolanic activity, while that of the mortars was an analyses in the fresh and hardened state. From the results, pretreatments (sieving and grinding) and lime added to the mixture improved the reactivity of the ashes and the best performance was presented for mortars with 15% substitution, mainly for those containing RHA.

Resumen La mezcla por volumen fue 1: 1: 6, para un reemplazo parcial de cemento Portland con un contenido de 15 y 30%. Las pruebas para los residuos fueron de caracterización de las partículas y actividad puzolánica, mientras que los morteros fueron sometidos a análisis en estado fresco y endurecido. De los resultados obtenidos, los pretratamientos (tamizado y molienda) y la cal añadida a la mezcla mejoraron la reactividad de las cenizas, el mejor comportamiento se presentó para los morteros con 15% de sustitución, principalmente para los que contienen RHA.

Resumo O presente trabalho tem como objetivo avaliar a incorporação de cinzas de biomassa vegetal, cavaco de eucalipto (ECA), bagaço de cana-de-açúcar (SCBA) e casca de arroz (RHA), em argamassas mistas de cimento e cal, considerando suas propriedades e desempenho mecânico. O traço em volume foi 1:1:6, para uma substituição parcial do cimento Portland a teores de 15 e 30%. Os ensaios para os resíduos foram de caracterização das partículas e atividade pozolânica, as argamassas foram submetidas a análises no estado fresco e endurecido. Dos resultados, os pré-tratamentos (peneiramento e moagem) e a cal adicionada a mistura melhoraram a reatividade das cinzas, o melhor desempenho foi apresentado para argamassas com 15% de substituição, principalmente para aquelas contendo RHA.

O uso eficiente da água se constitui em um dos principais quesitos a serem contemplados dentro do conceito de produção mais limpa e o uso da água residuária da produção do concreto pode ser uma importante medida para este fim. Contudo, não se dispõe no Brasil de um estudo que indique a qualidade desta água e em quais atividades poderia ser reutilizada. O objetivo deste trabalho é avaliar a qualidade da água residuária de uma usina de concreto e propor diretrizes para o seu tratamento tendo em vista o reúso para fins não potáveis. Para tanto, foram coletadas amostras da água residuária em três pontos do sistema de tratamento existente na usina em estudo, sendo depois realizados ensaios em laboratório para a avaliação da sua qualidade. Os resultados obtidos forma comparados com os valores limite dos parâmetros de qualidade existentes nos principais documentos que vêm sendo empregados para a análise da água não potável para fins de abastecimento no pais. Os resultados obtidos indicam a necessidade de acrescentar ao sistema de tratamento existente, pelo menos, os processos de coagulação e a correção do pH.

Efficient water use is one of the most important requirements of cleaner production, and the use of the wastewater from concrete production can be an important means to this end. However, there are no Brazilian studies on the quality of concrete plant wastewater and the activities in which such water can be used. This paper aims to evaluate the quality of concrete plant wastewater and to propose guidelines for its treatment for non-potable applications. Wastewater samples were collected from three points in the studied treatment system, and tests were later performed in the laboratory to evaluate the water quality. The results obtained were compared with the limit values for the quality parameters that have been used for the analysis of the non-potable water supply in Brazil. The results indicate a need to at least add coagulation and pH correction processes to the treatment system.

The preferred temperature of the yellow scorpion Tityus serrulatus was investigated since its dispersion is a matter of concern. Adult T. serrulatus, weighing 1.24 + 0.20 g (mean + sd) and with a standard length of 59.3 + 2.5 mm, were used. A metallic corridor (120 cm long, 5 cm large and 10 cm high) with thermal gradient ranging from 0°C to 40°C was used. Tityus serrulatus chose and stayed in temperatures ranging from 14°C to 38°C when safe conditions were offered (dark and thigmotactic stimuli). The number of animals that remained in the 11°C-20°C, 21°C-30°C, and 31°C-40°C temperature zones were 8, 8, and 9, respectively. The chi-square test (degree of freedom = 2) showed that differences were not significant (p>0.05). Some animals moved to lower temperature areas (less than 8°C) when the corridor was completely illuminated and thigmotactic stimuli were absent, which led the animals to present a torpor state. It is concluded that T. serrulatus does not select a specific environmental temperature. Associated with the capacity of temporally surviving at low temperatures, this species seems to be highly adaptable to different thermal zones.