Abstract The environmental impacts caused by the disposal of ornamental rock waste require studies for its reuse. Gypsum, a binder widely used in civil construction, can help this recycling process. Thus, some research was carried out in gypsum composites with ornamental rock residue at levels of 0, 5%, 10%, 15%, and 20% and with the water/gypsum (w/g) ratio of 0.6 and 0.8. The properties of setting time, porosity, hardness, compressive strength, thermal conductivity, and tensile bond strength were evaluated. The setting time did not show significant changes for the different contents and w/g ratios. Porosity tended to decrease with the insertion of waste and water decrease. Hardness and compressive strength increased with the inclusion of the residue on the w/g ratio of 0.6. Thermal conductivity and tensile bond strength did not vary greatly.

Abstract This research evaluates the behavior of plaster with a water-repellent additive when submitted to a natural aging process. Casting plaster and silane/siloxane-based water-repellent were used as materials. The water/plaster ratio was set at 0.7 and the contents of 0.2% and 0.4% of water-repellent were used, in relation to the plaster mass. Plaster pastes without water-repellent (reference) and containing mass water-repellent were evaluated at ‘zero’ age and after 30, 60, 90, 120, and 150 days of natural aging. After 150 days of natural aging, it was observed that the mechanical properties of the material (compressive strength and hardness) did not undergo significant variations and remained above the minimum required by a standard. The addition of water-repellent resulted in a considerable reduction in water absorption, demonstrating the water repellency capacity of the material, compared to the reference specimen.

Resumo Materiais compósitos com matriz de poli-hidroxibutirato e material de reforço de hidroxiapatita (PHB/HA) foram produzidos por moldagem a partir de prensagem em 100 MPa e 165 °C durante 30 min. A quantidade de reforço variou de 0 a 20% em massa para avaliar o efeito das partículas de HA nas propriedades mecânicas e na bioatividade dos compósitos. O aumento da quantidade de HA reduziu a resistência à compressão dos compósitos em aproximadamente 20%, enquanto a resistência à flexão diminuiu 30%. No entanto, a bioatividade após 14 dias de imersão em SBF foi melhorada com o aumento da quantidade de HA, sendo observada camada de apatita na superfície do compósito PHB/HA.

Abstract The composite materials using polyhydroxybutyrate as matrix and hydroxyapatite as reinforcement (PHB/HA) were produced by molding, using pressing at 100 MPa and 165 °C for 30 min. The amount of filler was varied from 0 to 20 wt% to evaluate the effect of the HA particles on mechanical properties and the bioactivity of the composites. The increase of the HA amount reduced the compressive strength of the composites nearly 20% while bending strength reduced nearly 30%. However, the bioactivity after 14 days immersion in SBF was improved with the increase of HA amount, with formation of apatite layer on the surface of the PHB/HA composite.