Asphaltenes can cause enormous losses in the oil industry, because they are soluble only in aromatic solvents. Therefore, they must be removed from the petroleum before it is refined, using flocculant agents. Aiming to find new materials that can work as flocculant agents to asphaltenes, cobalt ferrite nanoparticles were chemically modified through acid-base reactions using dodecylbenzene sulfonic acid (DBSA) to increase their lipophilicity. Nanoparticle synthesis was performed using the co-precipitation method followed by annealing of these nanoparticles, aiming to change the structural phase. Modified and unmodified nanoparticles were tested by FTIR-ATR, XRD and TGA/DTA. In addition, precipitation onset of the asphaltenes was performed using modified and unmodified nanoparticles. These tests showed that modified nanoparticles have a potential application as flocculant agents used to remove asphaltenes before oil refining, since the presence of nanoparticles promotes the asphaltene precipitation onset with the addition of a small amount of non-solvent.

O objetivo principal deste trabalho é o de avaliar do ponto de vista ambiental a possibilidade da incorporação de resíduo sólido proveniente do setor siderúrgico em massas argilosas para fabricação de cerâmica estrutural. A indústria cerâmica apresenta enorme potencial para absorver resíduos industriais poluentes. Até 3% em peso de resíduo foi adicionado em proporções graduais a uma massa argilosa. Os corpos cerâmicos foram conformados por extrusão, secados a 110 °C e queimados em forno industrial a 950 °C. Os corpos cerâmicos incorporados foram submetidos a ensaios ambientais de lixiviação e solubilidade. Além disso, foi feita a análise preliminar dos gases evoluídos durante o processo de queima. Os resultados revelaram que a utilização de massas cerâmicas contendo até 3% em peso de resíduo sólido de siderurgia, para fabricação de produtos de cerâmica vermelha, não oferece nenhum risco direto ao meio ambiente.

The main objective of this work is to evaluate from an environmental viewpoint the incorporation of solid waste from the siderurgical industry into clayey masses for red ceramics. Ceramic masses containing up to 3 wt% waste were prepared. Ceramic bodies were extruded, dried at 110 °C and fired in an industrial kiln at 950 °C. Leaching and solubility tests were done on the incorporated ceramic bodies. In addition, the emission of gases was also analyzed. The results indicated that the use of up to 3 wt.% siderurgical solid waste in red ceramics does not cause significant environmental impact.

Este trabalho mostra os resultados de um estudo sobre a incorporação de resíduo sólido proveniente do setor siderúrgico na formulação de uma massa argilosa utilizada na fabricação de cerâmica vermelha. As massas preparadas continham os seguintes teores de resíduo de siderurgia: 0; 0,5; 1,0; 1,5; 2,0; 2,5 e 3,0% em peso. Os resultados de difração de raios X, distribuição de tamanho de partículas e limites de Atterberg são apresentados para as massas argilosas. Os corpos-de-prova foram conformados por extrusão a vácuo e queimados nas temperaturas de 850 ºC, 900 ºC, 950 ºC, 1000 ºC e 1050 ºC. As propriedades físico-mecânicas foram determinadas em função da temperatura de queima e do conteúdo de resíduo de siderurgia. Os resultados obtidos indicaram que o resíduo sólido de siderurgia adicionado modificou as características físico-químicas e, também, as propriedades da massa argilosa pura. As massas cerâmicas contendo resíduo de siderurgia têm potencial para serem empregadas na fabricação de produtos de cerâmica vermelha para a construção civil.

This work presents the results of a study on the incorporation of solid waste from siderurgical industry in the formulation of a clayey mass used in the production of red ceramics. The prepared masses contained the following amounts of siderurgy waste: 0, 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0wt%. The results of X-ray diffraction, granulometry and Atterberg's limits are presented for the ceramic masses. Test specimens were conformed by vacuum extrusion and fired at temperatures of 850 ºC, 900 ºC, 950 ºC, 1000 ºC and 1050ºC. The physical-mechanical properties were determined as a function of firing temperature and content of siderurgy waste. The results indicate that the addition of siderurgy solid waste modify the physic-chemical characteristics of the clayey mass and the ceramic properties of the test specimens. The results suggest also that the ceramic masses containing siderurgy waste could be used in the production of red ceramic for civil construction.