The present work aims to prepare and characterize very thin films of poly(fullerene)s in order to investigate their electrical properties and the influence of xylene and chloroform solvents on these materials. The fullerenes studied were phenyl-C61-butyric acid methyl ester (PCBM), oligo{(phenyl-C61-butyric acid methyl ester)-alt-[1,4-bis(bromomethyl)-2,5-bis(octyloxy)benzene]} (OPCBMMB) and poly{[bispyrrolidino(phenyl-C61-butyric acid methyl ester)]-alt-[2,5-bis(octyloxy) benzene]} (PPCBMB), along with poly(3-hexylthiophene) (P3HT). The Langmuir-Schaeffer technique was used to prepare films, which were deposited on interdigitated gold substrates, and electrically characterized, with emphasis on the study of transport, conductivity and mobility mechanisms with respect to the solvents used. We found that the addition of P3HT significantly increased the conductivity of these materials. The xylene cast PPCBM, in both pure and mixed forms under dark conditions, presented the best conductivity results with respect to the other materials. However, when chloroform was used, it was found that OPCBMMB in both pure and mixed forms under light, exhibited the best conductivities. This is the first treatment, to our knowledge, of the impact of solvents on the electronic properties of poly(fullerene)s.

In this paper, devices fabricated with a diode-like structure (electrode/polymer/electrode) from spin-coated and nanostructured (Langmuir-Schaefer) films of polythiophene derivatives were characterized by impedance spectroscopy and studied by theoretical fitting to reach a better understanding of the physical processes in the devices. The materials used for this research were the polyalkylthiophene (P3AT) derivatives poly(3-butylthiophene) (P3BT), poly(3-hexylthiophene) (P3HT), poly(3-octylthiophene) (P3OT) and poly(3-decylthiophene) (P3DT). Electrical measurements were performed from 1 Hz to 1 MHz (100 mV ac) while increasing the dc bias in the range from 0 to 2.5 V. The fittings of the experimental results were performed using equivalent circuits. By plotting the theoretical and experimental spectra on a single graph, it was possible to obtain information related to the film morphology, interfacial effects, resistance, capacitance and conductivity of the polymer, thereby enhancing the understanding of this particular type of device. Among the P3AT films, those grown by the Langmuir-Schaefer technique showed higher electrical conductivity, with the only exception being that of P3BT.