Titania-supported Ir catalysts were used in the hydrogenation of furfural. Reactions were carried out in a stirred batch type reactor at 0.62MPa and 363K using a 0.10M solution of furfural in a 1:1 mixture n-heptane -ethanol as solvent. Catalysts containing 2 wt% of Ir were reduced in H2 flow at different temperatures in the range 473-773K. The catalysts were characterized by H2 chemisorption, TEM, TPR, TPD of NH3 and XPS. Conversion of furfural is higher at lower reduction temperatures, but leads to byproducts whereas reduction at higher temperatures shows selectivity to furfuryl alcohol close to 100%.

Se evaluó el comportamiento de diferentes catalizadores de Ir, en la hidrogenación de aldehídos a,b-insaturados, acroleína y crotonaldehído, para la obtención de sus alcoholes insaturados alcohol alílico y crotílico respectivamente, cuya utilidad en la industria de la química fina es de amplio reconocimiento. Los aldehídos objeto de esta investigación representan un alto riesgo ambiental, por lo que la investigación presentada en este trabajo resulta de gran importancia en ese campo. En general los resultados obtenidos muestran que factores como temperatura de reducción y contenido de TiO2 en los catalizadores son determinantes en el comportamiento catalítico; análisis de caracterización permitieron establecer que en los catalizadores reducidos a alta temperatura se presenta el efecto de interacción fuerte metal soporte, conocido por su símbolo SMSI, lo que favorece la conversión, actividad inicial y TOF. De igual manera los catalizadores evaluados son altamente selectivos hacia los alcoholes insaturados que representan los productos de interés en este estudio.

The behavior of different Ir catalysts in the hydrogenation of a,b-unsaturated acrolein and crotonaldehyde aldehydes has been evaluated to obtain their allyl and crotyl unsaturated alcohols respectively; their products are used in fine chemicals industry. The present work is of great importance in this field because of the unsaturated aldehydes studied having high environmental risk besides the great academic contribution. The results show that factors such as reduction temperature and TiO2 content are critical in the catalytic behavior, through the analysis of characterization was established that the catalysts reduced at high temperature shows the Strong Metal Support Interaction effect (SMSI), which favors conversion percentage, initial activity and TOF. The analyzed catalysts were highly selective towards the unsaturated alcohols.

Se estudió la hidrogenación de crotonaldehído en fase líquida, sobre catalizadores Ir/TiO2-SiO2; este aldehído es altamente contaminante y proviene de fuentes tan diversas como humo de tabaco, gases de escape de motores de gasolina o diesel y humo de combustión de madera [1]. El objetivo principal de esta investigación fue la obtención del alcohol insaturado (crotil alcohol). A partir de los estudios realizados logró demostrarse que un aumento en el contenido de TiO2, lo mismo que la reducción de los catalizadores a altas temperaturas favorece parámetros como selectividad hacia el producto de interés, actividad catalítica y en general se logró mejorar de manera notable los niveles de conversión. El comportamiento observado se atribuyó principalmente a la fuerte influencia del efecto SMSI (Strong Metal Support Interaction), presente a altas temperaturas en óxidos parcialmente reducibles.

Liquid phase crotonaldehyde hydrogenation over Ir/TiO2-SiO2 catalysts was studied; this aldehyde is highly pollutant comes from cigarette smoke, exhaust from gasoline and diesel engines and the burning of wood [1]. The main objective of this research was unsaturated alcohol (crotyl alcohol) obtention. This study showed that an increase in TiO2 content and high temperature reduction in catalysts produce high selectivity to crotyl alcohol, high activity, and an increase in conversion levels. This behavior is due to SMSI (Strong Metal Support Interaction) effect, at high temperatures in partially reducible oxides.