ABSTRACT Lignin, the second most abundant biopolymer on the planet, has properties that can be widely explored, moving from waste to products with high added value. Therefore, this work aimed to extract and characterize Klason and Kraft lignins from sawdust and black liquor, considered industrial waste. The raw material used was Eucalyptus grandis chips. To obtain Klason lignin according to TAPPI 222 om-02 (2002), part of the chips were transformed into sawdust. To obtain Kraft lignin, another part of the chips passed through a digester to obtain black liquor, which was subsequently subjected to acid precipitation. The characterization of lignins was performed by granulometry analysis, scanning electron microscopy with elemental chemical analysis (EDS), transmission electron microscopy, medium infrared spectroscopy, thermogravimetric analysis and differential calorimetry. Microscopy analyzes showed irregular structures of various shapes, including spherical structures, most evident and frequent in Kraft lignin. The elementary chemical analysis showed that the lignin washing process was satisfactory, due to the small percentage of sulfur detected in the samples. The results of the granulometry confirmed that the lignins had micrometric dimensions. The medium infrared spectra showed the characteristic peaks of the chemical composition of lignin. The thermal analysis showed three ranges of degradation, attributed to the drying of the samples, degradation of the hemicelluloses and the lignin itself. All results confirmed the obtaining of Klason and Kraft lignins. Therefore, the techniques were satisfactory in transforming waste into lignin with the potential for a variety of commercial applications, mainly in the chemical and pharmaceutical industries.

RESUMO A lignina, o segundo biopolímero mais abundante do planeta, possui propriedades que podem ser amplamente exploradas, passando de resíduos a produtos de alto valor agregado. Portanto, este trabalho teve como objetivo extrair e caracterizar as ligninas Klason e Kraft de serragem e licor negro, considerados resíduos industriais. A matéria-prima utilizada foram cavacos de Eucalyptus grandis. Para a obtenção da lignina Klason conforme TAPPI 222 om-02 (2002), parte dos cavacos foi transformada em serragem. Para a obtenção da lignina Kraft, outra parte dos cavacos passou por um digestor para a obtenção do licor negro, que posteriormente foi submetido à precipitação ácida. A caracterização das ligninas foi realizada por análise de granulometria, microscopia eletrônica de varredura com análise química elementar (EDS), microscopia eletrônica de transmissão, espectroscopia de infravermelho médio, análise termogravimétrica e calorimetria diferencial. As análises microscópicas mostraram estruturas irregulares de vários formatos, incluindo estruturas esféricas, mais evidentes e frequentes na lignina Kraft. A análise química elementar mostrou que o processo de lavagem da lignina foi satisfatório, devido ao pequeno percentual de enxofre detectado nas amostras. Os resultados da granulometria confirmaram que as ligninas apresentaram dimensões micrométricas. Os espectros de infravermelho médio mostraram os picos característicos da composição química da lignina. A análise térmica mostrou três faixas de degradação, atribuídas à secagem das amostras, degradação das hemiceluloses e da própria lignina. Todos os resultados confirmaram a obtenção das ligninas Klason e Kraft. Portanto, as técnicas foram satisfatórias na transformação de resíduos em lignina com potencial para diversas aplicações comerciais, principalmente nas indústrias química e farmacêutica.

Objetivou-se, com este trabalho, analisar a variabilidade da cor da madeira nas seções anatômicas (radial, tangencial e transversal) das espécies Breu-vermelho, Tauari-vermelho e Pequiarana, por meio de colorimetria quantitativa, utilizando o sistema CIELAB de cores. As espécies são provenientes da área de exploração florestal da empresa Mil Madeiras Preciosas, localizada no município de Itacoatiara/AM. Foram selecionadas 5 amostras da madeira de cada espécie, sendo determinados os parâmetros colorimétricos: L*, a*, b*, C e h*. Foram realizadas 225 medições no total, por meio do espectrofotômetro Konica Minolta CM-5 acoplado ao computador. As espécies Breu-vermelho, Tauari-vermelho e Pequiarana apresentaram diferenças estatísticas nos parâmetros colorimétricos, e baixa saturação na coordenada a*. De acordo com agrupamento de Cluster, a madeira de Breu-vermelho é oliva e/ou rosa-acinzentada, Tauari-vermelho é cinza-rosado e Pequiarana é rosa-acinzentado e/ou cinza-rosado. As espécies florestais apresentaram diferença de cor entre os planos anatômicos (radial, tangencial e transversal), sendo influenciados pela coloração amarela, definida no parâmetro b*. A utilização da colorimetria para conhecimento da cor da madeira mostrou-se de aplicação simples e podendo ser empregada desde o desdobro da tora, até aproveitamento final, com possibilidade de agregação de valor ao produto.

The aim of this study was to analyze wood color variability in the (radial, tangential and transversal) anatomic sections of Breu-vermelho, Tauari-vermelho and Pequiarana species through quantitative colorimetry using CIELAB color system. Such species come from a forest sustainable area of Thousand Precious Woods Company, located in Itacoatiara in the Amazon region of Brazil. Five wood samples from each species were selected so as to determine the following colorimetric parameters: L*, a*, b*, C e h*. In addition, 225 measurements were carried out with Konica Minolta CM-5 spectrophotometer connected to the computer. Results pointed out to statistical differences in the colorimetric parameters and also a low saturation in a* in the analyzed species. According to the cluster gathering, Breu-vermelho wood presents olive and/or grayish pink color, Tauari-vermelho is pinkish-gray and Pequiarana is grayish-pink and/or pinkish-gray. Such species presented differences in color among the three anatomic sections cited above and were also influenced by the yellow color defined in b* parameter. To summarize, colorimetric analysis to establish wood color is a simple procedure which may be used from the sawing of the logs until their final exploitation enabling value aggregation to the final product.

No presente estudo, objetivou-se comparar a resistência da linha de cola de painéis de Pinus taeda colados lateralmente com diferentes adesivos industriais. Foram analisados três tipos de adesivos (poli(vinil) acetato (PVAc), emulsão polimérica de isocianato (EPI) e poliuretano (PU)) colados em duas orientações (radial e tangencial) e avaliados após os condicionamentos de ensaio (a seco e a úmido). Foram preparados 360 corpos de prova para a determinação da resistência ao cisalhamento dos painéis colados lateralmente de Pinus taeda e, estes foram testados em máquina universal de ensaio EMIC. A resistência da linha de cola ao cisalhamento a seco foi inferior nas peças coladas no sentido tangencial para os três tipos de adesivos analisados. O adesivo PU apresentou os maiores valores médios de resistência ao cisalhamento nos condicionamentos aplicados, diferindo, estatisticamente, do adesivo PVAc e do adesivo EPI quando testado a seco e não diferindo dos demais adesivos quando testado a úmido. O maior valor percentual de falha na madeira foi observado após o ensaio de resistência ao cisalhamento a seco para o adesivo EPI colado no sentido radial. E em cisalhamento a úmido, o adesivo EPI e o adesivo PU colados no sentido tangencial apresentaram valores médios superiores de falha na madeira. Assim, foi possível concluir que a resistência da linha de cola da madeira de Pinus taeda foi influenciada pelo tipo de adesivo e pela orientação de colagem, além de se comportar diferenciadamente conforme a condição de uso (seco ou úmido).

The study compares the strength of the glue line of edge glued panels of Pinus taeda made with different industrial adhesives. Three types of adhesives (poly(vinyl) acetate (PVAc), emulsion polymer isocyanate (EPI) and polyurethane (PU)) glued in two side gluing orientation (radial and tangential) and analyzed after the conditioning tests (dry and wet) were analyzed. The 360 specimens were prepared for determining the shear strength of edge glued panels of Pinus taeda, and these were tested in a universal testing machine called EMIC. The shear strength of the glue line at dry condition was lower in the tangential side for the three types of adhesives analyzed. The PU adhesive showed the highest values of shear strength in the applied conditions, differing from PVAc and EPI adhesive when tested on dry condition and did not differ from the others adhesives when tested on wet condition. The highest percentage of wood failure was observed after the shear strength test at dry condition to EPI adhesive glued in the radial side. And in the wet condition, the EPI adhesive and PU adhesive glued in tangential side showed higher mean values of wood failure. Thus, it was possible to conclude that the strength of the glue line of Pinus taeda wood was influenced by the type of adhesive and side gluing orientation, and showed differently behavior according to the condition of use (wet or dry).