In devices used in open-heart surgery and dialysis, blood must be continuously processed using extracorporeal circuits composed of peristaltic pumps and active components such as specific filters and oxygenators. Several procedures have been employed to avoid blood coagulation induced by contact with the artificial surfaces of such devices. Often heparin, a bioactive protein able to prevent clot formation, is employed. In this work, we have used heparin-containing gas plasmas to evaluate the possibility of depositing adherent anticoagulant films onto PVC and glass surfaces. The films were produced by radiofrequency plasma enhanced chemical vapor deposition from heparin/isopropanol and heparin/hexamethyldisiloxane solutions. In addition, the effects of exposure to SF6 plasmas on the compatibility of such surfaces have also been investigated. The blood compatibility was evaluated through the determination of the density of platelets and fibrinogen and activated partial thromboplastin (APTT) and prothrombin times (PT) of human blood freshly collected and after contact for 2.5 hours with different surfaces. The deposited films were also characterized by infrared spectroscopy, contact angle and surface energy measurements. The coagulation time of blood, placed in contact with glass substrates coated by PECVD films of heparin/isopropanol mixtures, and in contact with SF6 plasma-treated PVC, increased by about 60 and 20%, respectively, compared to the values measured with untreated samples.

In this work, thin polymer films were prepared from acetylene and argon radiofrequency (13.56 MHz, 80 W) glow discharges. Post-deposition treatment was performed by plasma immersion ion implantation in nitrogen or helium glow discharges (13.56 MHz, 70 W). In these cases, samples were biased with 25 kV negative pulses. Exposure time to the bombardment plasma, t, ranged from 900 to 7200 s. Chemical composition of the film surfaces was investigated by X-ray Photoelectron Spectroscopy and the resistance to oxidation by the etching process, in reactive oxygen plasmas. Oxygen and nitrogen were detected in all the samples. While the concentration of the former continuously changed with t, that of N kept practically constant in small proportions. The film is predominantly formed by sp² states, but the proportion of sp³ hybridization slightly increased with t. The etching rate dropped under certain conditions of nitrogen bombardment whereas helium implantation has not significantly improved it. These results are ascribed to the crosslinking degree of the polymeric chains, ruled by the total amount of energy delivered to the film.

The properties of hydrophilicity or hydrophobicity of materials are defined mainly, though not exclusively, by their composition, morphology and surface energy. In this work, titanium dioxide (TiO2) and aluminum oxide-alumina (Al2O3) ceramics prepared by uniaxial pressing were studied in terms of surface energy. The surfaces of these ceramics were treated with nitrogen plasma, using a stainless steel reactor excited by a 13,6 MHz radio frequency operating at 50 W input power and 13 Pa nitrogen pressure. The surface morphology was investigated by scanning electron microscopy (SEM) analysis. Surface energy and contact angle measurements were taken using a RAMÉ-HART goniometer. These measurements were taken as function of time, over a 21-day period. The contact angle and surface energy values were found to change by almost 34% in comparison to their initial values immediately following plasma treatment. Nonetheless, the hydrophilic character of the Al2O3 and TiO2 remained constant throughout the test period.