This study aimed to synthesize a composite material composed of bio-based, porous carbon matrix and Cu nanoparticles through a simple, low-cost, and environmentally friendly method. Concentrated Kraft black liquor was used as a carbon precursor, and Cu nanoparticles were homogeneously deposited on the carbon matrix using electrochemical deposition. The textural properties determined using N2 isotherms indicated increased surface area of a carbon matrix with a micro-mesoporous structure. Voltammetric tests demonstrated that the composite exhibited catalytic properties for electrochemical CO2 reduction. Compared to the bio-based, porous carbon sample (C matrix), the bio-based carbon electrode electrochemically decorated with Cu nanoparticles (C–Cu composite) exhibited increased current values of approximately 2.4 times, a potential shift of approximately 90 mV, and an onset potential of −1.02 V, under CO2 saturation.

RESUMO Atualmente, existe uma demanda na busca por materiais com alta densidade de potência, longo ciclo de vida e baixo impacto ambiental que são em sua maioria utilizados para a produção de supercapacitores, sendo esses considerados fontes promissoras de energia para sistemas eletrônicos. Os tipos de materiais mais promissores para essa aplicação são os baseados em carbono, devido à sua flexibilidade, área superficial e boa estabilidade eletroquímica. Para a produção de materiais carbonosos, o principal precursor utilizado é a poliacrilonitrila (PAN) e suas variações a partir da adição de monômeros, como o acrilato de metila (MA). Geralmente, esses materiais são utilizados em formas de mantas, fios ou nanofibras produzidos a partir de processos de fiação e posteriormente carbonizados para gerar o material carbonáceo. Um dos processos de fiação que tem sido amplamente estudado para a obtenção de nanofibras de carbono é o processo de eletrofiação. Portanto, este trabalho apresenta os resultados obtidos do processo de carbonização de mantas eletrofiadas a partir de solução de PAN homopolímero (PANH) e PAN-co-acrilato de metila 6 % (PA6MA) com dimetilformamida (DMF) com o intuito de obter material para uso em supercapacitores. Os polímeros utilizados foram analisados por DSC para a obtenção dos valores relacionados a faixa de ciclização, sendo possível observar uma melhor estabilidade térmica relacionada as amostras de PAN6MA com faixa de temperatura de 240-312 °C e temperatura máxima do pico exotérmico de 292 °C. As mantas obtidas pelo processo de eletrofiação foram oxidadas a 235°C por 5min e carbonizadas a 900 °C por 5 min. As mantas obtidas, antes e após o processo de carbonização, foram analisadas por MEV apresentando fibras de superfície lisa, dispersas aleatoriamente e de dimensões nanométricas, sendo os valores de diâmetro aproximado de 219 nm para as nanofibras de carbono de PANH (NfcPANH) e 185 nm para as nanofibras de carbono de PAN6MA (NfcPAN6MA). As mantas carbonizadas foram analisadas pela técnica RAMAN e foi possível a obtenção de dados referentes a estrutura carbônica presente nas amostras, onde os valores obtidos demonstraram que as amostras de NfcPAN6MA apresentaram menor valor de grau de cristalinidade medida a partir da relação entre as bandas D e G conhecido como fator ID/IG, sendo o valor obtido igual a 1,06 para as NfcPNA6MA e 1,24 para as NfcPANH, isso demonstra uma maior presença de estruturas grafíticas cristalinas quando comparadas as amostras produzidas a partir da PANH. Para obtenção das características capacitivas foram realizados levantamento das curvas carga/ descarga por análise cronopotenciométrica, foi possível observar as melhores características relacionadas a capacitância específica e estabilidade de ciclagem em baixas correntes aplicadas para as amostras de PAN6MA com valores de capacitância específica de 270,9 F/g, densidade de energia de 30,0 Wh/kg e densidade de potência de 153,5 W/kg. Os resultados obtidos demonstraram que o material apresentou potencial para a aplicação proposta.

ABSTRACT Currently, there is a demand in the search for materials with high power density, long life cycle and low environmental impact that are mostly used fot the supercapacitors production, which are considered promising energy power for electronic systems. The most promising types of materials for this application are those based on carbon, due to their flexibility, surface area and good electrochemical stability. For the production of carbonaceous materials, the main precursor used is polyacrylonitrile (PAN) and its variations from the addition of monomers, such as methyl acrylate (MA). Generally, these materials are used in forms of blankets or yarns produced from spinning processes and later carbonized to generate the carbonaceous material. One of the spinning processes that has been widely studied for obtaining carbon nanofibers is the electrospinning process. Therefore, this paper presents the results obtained from the carbonization of electrospun blankets manufactured from solutions of polyacrylonitrile homopolymer (PANH) and poly (acrylonitrile-co-6 % methyl acrylate) (PAN6MA) combined with dimethylformamide in order to obtain material for use in supercapacitors. The polymers used were analyzed by DSC to obtain the values related to cyclization, by that were possible to observe a better thermal stability related to the samples of PAN6MA, with a temperature range of 240-312 ºC and maximum temperature of the exothermic peak of 292 °C. The electrospun mats were oxidized at 235°C per 5 min and carbonized at 90 °C per 5 min. Both pre-carbonization and post-carbonization mats were analyzed by SEM, showing fibers with smooth surface, randomly dispersion and nanometric size, with values of diameter of approximately 219 nm for PANH carbon nanofibers (NfcPANH) and 185 nm for PAN6MA carbon nanofibers (NfcPAN6MA). The carbonized mats were analyzed by RAMAN technique and it was possible to obtain the data related to the carbon structure present in the samples, where the obtained values showed that the mats manufactured from PAN6MA presented the lower value of degree of crystallinity measured from the relationship between bands D and G known as factor ID/IG, the value obtained being equal to 1.06 for NfcPAN6MA and 1.24 for NfcPANH, this shows a higher concentration of crystalline graphitic structures when compared with the samples produced from PANH. To obtain the capacitive characteristic, the load/discharge curves were surveyed by chronopotentiometric analysis, where it was possible to observe the best characteristics related to the specific capacity and low current cycling stability applied to the PAN - co- 6% methyl acrylate sample with specific capacity values of 270.9 F/g, energy density of 30.0 Wh/kg and power density of 153.5 W/kg. The results obtained demonstrated that the material presented potential for the proposed application.

ABSTRACT The electromagnetic properties of Carbon-Graphene Xerogel (CGX), Flaky graphite (GR) and Nickel-Zinc ferrite (FeNiZn) composites in polystyrene (PS) matrix were studied in the X-Band range (8.2 – 12.4 GHz). In this work the Expanded Polystyrene (EPS) waste material was processed into polystyrene through the recycling of EPS. The polystyrene obtained was utilized as dielectric matrix, mainly because PS is a well-known organic polymer that presents low dielectric loss and light weight, which contribute to applications in composites for the aerospace field. In order to produce the final composite specimens, the CGX additive was previously synthesized through a sustainable method that employed the use of waste from the paper and pulp industry (black liquor). Afterwards, the morphological and structural analysis were made through Scanning Electron Microscope (SEM) and Raman Spectrometer, respectively. On the other hand, the magnetic ferrite material, FeNiZn, was obtained for the composite production through calcination, whereas the GR utilized was commercially obtained. It was observed that the increase of CGX and GR influenced on the increase of the Complex Permittivity, and that 10 wt% CGX + 50wt% FeNiZn composite sample demonstrated an absorption peak at 10.5 GHz. The results are relevant concerning the recycling of EPS waste through its use as dielectric matrix, thus developing greener and low-weight composite materials to be used in microwave applications.

RESUMO Compósitos poliméricos reforçados com fibras de carbono são materiais cada vez mais utilizados em diferentes segmentos industriais, em especial, os segmentos aeronáuticos e automobilísticos devido a sua elevada resistência mecânica e baixa massa específica. Desta forma, existe grande preocupação com o descarte e a reciclagem dos componentes que representam produtos de alto valor econômico agregado, principalmente fibras de carbono. O processo de pirólise tem sido um dos métodos de reciclagem de compósitos para recuperar as fibras de carbono a partir da degradação da matriz polimérica. No setor de energia, fibras de carbono são traduzidas como bons materiais de armazenamento de energia, por apresentar desejáveis características condutoras e capacitivas que potencializam sua aplicação como material de eletrodo em supercapacitores. Neste sentido, a proposta deste trabalho consiste em viabilizar o uso de fibras de carbono recicladas por pirólise de compósitos epóxi reforçado com fibras de carbono como material de eletrodo de supercapacitores e avaliar a influência dos tratamentos termoquímico e químico sobre suas propriedades capacitivas. Imagens FEG-MEV mostraram que as fibras de carbono foram praticamente limpas permanecendo um mínimo de carbono residual sobre a superfície. A área BET e as análises FTIR, Raman e de voltametria cíclica mostraram que os tratamentos termoquímico e químico realizados na FCP não contribuíram para melhorar a capacidade de armazenamento de cargas na interface eletrodo/eletrólito, pelo contrário, o tratamento químico levou a uma grande redução da capacidade da FCP no armazenamento de energia devido a incorporação de grupos OH e COOH. As curvas de carga/descarga evidenciam boa ciclabilidade e os valores de capacitância específica para a fibra de carbono reciclada de 34 Fg-1, densidade de potência de 37,6 Wkg-1 e densidade de energia de 4,7 Whkg-1encontram-se dentro da faixa para aplicações como eletrodos de supercapacitores.

ABSTRACT Carbon fiber reinforced polymeric composites are increasingly used materials in aeronautical and automotive industries, due to their excellent mechanical, chemical and electrical properties and low specific mass. In this way, there is a great concern regarding the components discard and recycling of the composites, which are considered as high economic value products to be wasted, mainly carbon fiber. The pyrolysis process has been one of the methods of recycling composites to recover carbon fibers from the degradation of the polymer matrix. In energy sector, carbon fibers are known as good energy storage materials due to adequate conducting and capacitive properties as supercapacitor electrodes. In this sense, the purpose of this work is to enable the use of recovered carbon fibers frompyrolysis of carbon fiber epoxy composites as electrode material for supercapacitors and to evaluate the influence of thermochemical and chemical treatments on their capacitive properties. FEG-MEV images showed that the carbon fibers were practically clean with a minimum of residual carbon remaining on the surface. The BET area and FTIR, Raman and cyclic voltammetry analyzes showed that thermochemical and chemical treatments carried out at the FCP did not contribute to improving the charge storage capacity at the electrode/ electrolyte interface. On the contrary, the chemical treatment led to a great reduction on energy storage capacity due to the incorporation of OH and COOH groups. The charge/discharge curves show good cycling and the specific capacitance values for the recycled carbon fiber of 34 Fg-1, power density of 37,6 Wkg-1 and energy density of 4,7 Whkg-1 are within range for applications such as supercapacitor electrodes.

The main challenge for the development of a high efficiency supercapacitor is the electrode material. Developing electrode materials with high specific electrical capacitance and low electrical resistance enables an increase in the energy accumulated in the device. In addition, it is expected that the electrode material presents a simple procedure for preparation having low production cost and being environmentally friendly. This work is based on the deposition of silver nanoparticles on activated carbon felt (Ag@ACF) as a supercapacitor electrode. The samples were characterized by field emission gun scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and textural analysis. Supercapacitor behavior was evaluated by galvanostatic charge-discharge curves, cyclic voltammetry and electrochemical impedance spectroscopy using a symmetrical two-electrode Swagelok type cell, and three different aqueous solution electrolytes: 2 M H2SO4, 6 M KOH and 1 M Na2SO4. Ag@ACF presented a high specific capacitance in KOH, about 170 F g-1, which makes it an interesting material for supercapacitor electrodes and it showed good specific electrical capacitance, low resistance and high cyclability.

ABSTRACT: This paper presents the preparation and characterization of carbon fiber felt and activated carbon fiber felt from textile polyacrylonitrile fiber. Carbon fibers are usually related to aircraft manufacturing or high mechanical purposes. Activated carbon fibers are known as excellent adsorbent materials. Despite all advantages, carbon fiber and activated carbon fiber are expensive materials because of their raw material cost. On the other hand, in this study, carbon fiber felt and activated carbon fiber felt were produced from textile polyacrylonitrile fiber, which is cheaper than their precursor, polyacrylonitrile fiber, and can be converted into carbon fiber felt and activated material with high micropore content and surface area. This research describes the transformation of textile polyacrylonitrile fiber in its oxidized form. After that, the oxidized material was transformed in felt and, in the sequence, converted into carbon fiber felt and activated carbon felt. The carbon fiber felt and activated carbon fiber felt were characterized by X-ray photoelectron spectroscopy, Raman spectroscopy and scanning electron microscope. N2 isotherms were performed to qualify the material obtained for further electrochemical applications. The main result was the conversion dynamics of textile polyacrilonitrile fiber into carbon fiber in felt form and activated carbon fiber in felt with high surface area and high micropores content.

This paper presents the electrolyte influence on deposition and dissolution processes of Cu nanoparticles on boron doped diamond electrodes (BDD). Morphological, structural and electrochemical analysis showed BDD films with good reproducibility, quality and reversible in a specific redox system. Electrodeposition of Cu nanoparticles on DDB electrodes in three different solutions was influenced by pH and ionic strength of the electrolytic medium. Analyzing the process as function of the scan rate, it was verified a better efficiency in 0,5 mol L-1 Na2SO4 solution. Under the influence of the pH and ionic strength, Cu nanoparticles on DDB may be obtained with different morphologies and it was important for defining the desired properties.