Abstract Low density sugarcane plantation (LDSP) has been implemented by some sugarcane producers in Brazil, aiming to save seeds and operational costs. The study was carried out in the municipality of Areia, Paraíba, Brazil. Five planting densities were used, varying from 5 to 25 m-2 of buds arranged in randomized blocks, with four replications. Data were measured annually over three cultivation cycles (2017 to 2020), during which the field was fertilized with NPK and the harvests were carried out manually without prior burning. The lower planting density presents higher productivity only in the cane plant (101.03 t ha-1) due to the higher plant height (2.37 m) and the higher number of stalks (11 stalks m-2), suggesting that these variables are due to the greater availability of light, water and photosynthate. However, there is a drastic reduction in sugarcane yield for this lower population in the 2nd ratoon by up to 65.62%, which is correlated with number of stalks per meter. We demonstrate the agronomic viability of LDSP in the population of 10 buds m-2 in relation to conventional planting of sugarcane until the 2nd ratoon. Data are important for future studies to present additional considerations for other production factors, such as the effects of mechanized harvesting and the management of nutrients and water, assessing the sustainability of this large-scale planting system.

Resumo O método de plantio de cana-de-açúcar de baixa densidade (LDSP) vem sendo implementado por alguns produtores de cana-de-açúcar no Brasil, visando economia de sementes e custos operacionais. O estudo foi realizado no município de Areia, Paraíba, Brasil. Utilizou-se cinco densidades de plantio, variando de 5 a 25 m-2 de gemas dispostas em blocos casualizados, com quatro repetições. Os dados foram medidos anualmente ao longo de três ciclos de cultivo (2017 a 2020). Menor densidade de plantio mostrou maior produtividade (101,03 t ha-1) devido à maior altura de planta (2,37 m) e ao maior número de hastes (NS) (11 hastes m-2), sugerindo que essas variáveis são devido à maior disponibilidade de luz, água e fotoassimilados. No entanto, houve redução drástica na produtividade da cana-de-açúcar para esta população menor na 2ª soca em 65,62%, estando correlacionado com o número de colmos por metro. Demonstramos a viabilidade agronômica do LDSP em uma população de 10 gemas m-2 em relação ao plantio convencional de cana-de-açúcar até a 2ª soca. Os dados são importantes para que estudos futuros apresentem considerações adicionais sobre outros fatores de produção, como os efeitos da colheita mecanizada e do manejo de nutrientes e água, avaliando a sustentabilidade desse sistema de plantio em larga escala.

This paper presents the experimental results for the leaching of printed circuit boards (PCB) from obsolete computers for extracting and recovering tin and copper by means of leaching followed by precipitation. Printed circuit boards were dismantled, cut into small pieces, and fed into a cylinder mill. The powder obtained was leached by using the aqueous solutions 2.18N H2SO4, 2.18N H2SO4 + 3.0N HCl, 3.0N HCl, and 3.0N HCl + 1.0N HNO3. The lowest values for the percentage of metal extraction were obtained with 2.18N H2SO4 (2.7% for Sn and lower than 0.01% for Cu), while the 3.0N HCl + 1.0N HNO3 leach system exhibited an extraction of 98% for Sn and 93% for Cu. Precipitates were obtained at different pH values by neutralizing the leach liquors using NaOH. The 3.0N HCl + 1.0N HNO3 leach system presented the highest recovery values from the powder feed (84.1% for Sn and 31.9% for Cu), as well as from the leach liquor (85.8% for Sn and 34.3% for Cu).

Indium can be recovered by treating residues, flue dusts, slags, and metallic intermediates in zinc smelting. This paper investigates the adsorption characteristics of indium and iron on an iminodiacetic acid chelating resin, Amberlite®IRC748 (Rohm and Haas Co.-USA). High concentrations of iron are always present in the aqueous feed solution of indium recovery. In addition, the chemical behaviour of iron in adsorptive systems is similar to that of indium. The metal concentrations in the aqueous solution were based on typical indium sulfate leach liquor obtained from zinc hydrometallurgical processing in a Brazilian plant. The ionic adsorption experiments were carried out by the continuous column method. Amberlite®IRC748 resin had a high affinity for indium under acidic conditions. Indium ions adsorbed onto the polymeric resin were eluted with a 0.5mol/dm³ sulphuric acid solution passed through the resin bed in the column. 99.5% pure indium sulfate aqueous solution was obtained using the iminodiacetic acid chelating resin Amberlite®IRC748.

The experimental research work was carried out in accordance with the Factorial Design Statistical Method to evaluate and analyze the influence of calcium, magnesium, silica and phosphorus on the precipitation of vanadates. Precipitation was performed by neutralization with H2SO4 of alkaline aqueous solutions containing vanadium pentoxide (V2O5) at 60± 2ºC. The experimental responses measured were percent of vanadium recovery and vanadium pentoxide content in the precipitate. These impurities are considered representative of those present in a leach liquor from the ore obtained at Campo Alegre de Lourdes (Brazil). The operational variables in this work were used under optimum conditions as determined by the statistical approach. Among the impurities under study, phosphorus exhibited the highest negative influence on the experimental responses. Phosphorus diminished the percent of vanadium recovered from 98.9 to 34.5 and the vanadium oxide content in the precipitate from 91.2 % to 39.3 %.