The present work deals with the study of some aluminum (Al) composites reinforced with metallized-graphite (MG) particles prepared by mechanical milling and powder metallurgy routes. Density, morphology evolution and mechanical performance of composites were investigated as a function of MG concentration and milling time. The as-milled powders were characterized by X-ray diffraction and optical/electron microscopy; meanwhile, the mechanical testing was carried out on cylindrical specimens prepared from powders by powder metallurgy. Evidence reveals that high-energy ball milling induce a homogeneous dispersion of graphite nanoparticles in the Al matrix; this is related to an enhancement of hardness and strength response of studied composites. The composite sample with 0.5% MG addition (in weight) reached an increase of 40% on hardness and 50% on strength (compared with pure Al sample); nevertheless an adverse effect was observed with longer milling and/or higher MG concentration.

The effect of Ni 1-2 wt.% addition on the microstructure and hardness of the aged A319 alloy were studied. Characterization analyses by x-ray diffraction, optical microscopy and scanning electron microscopy suggest clearly that Ni addition forms Al-Ni-Cu-Fe, Al-Cu-Ni and Al-Ni intermetallic compounds that correlates well with equilibria conditions. Analyses by transmission electron microscopy show that aging heat treatment promotes microstructural changes in morphology, size, and spatial distribution of precipitates. Vickers micro-hardness test of Ni 1 and 2 wt.% specimens have a hardness increase from that of A319 alloy of ~6-8% with mean values of 140.98 and 142.93 HV, respectively.

Equiatomic AlCoNi alloy matrix were reinforced by the dispersion of SiC nanoparticles (SiCnp) using the mechanical alloying process. The metallic powders were milled for 10, 20 and 30 h and sintered at 1200 0C under vacuum. Through particle size distribution, X-ray diffraction and scanning electron microscopy investigations, the mechanically alloyed powders for 10 h were selected to be reinforced with SiCnp (2.5, 5 and 10 wt.%). The microstructural features, and improvement in microhardness and porosity of sintered AlCoNi-SiC composites were investigated as a function of SiCnp content. Microhardness Vickers test showed that the enhanced microhardness of the AlCoNi-SiCnp composite could be attributed to the decrease of porosity in comparison to the AlCoNi alloy.

Abstract The mechanical alloying technique was employed to produce series of high entropy alloys, combining in equiatomic percentage Al, Co, Cr, Cu, Fe, Mo, Ni and Ti. Milling times were 0, 10, 20 and 30 h, and experiments were performed in a high energy ball mill (SPEX-8000M) under argon atmosphere. The structural and microstructural changes due to mechanical alloying process were studied by X-ray diffraction and electron microscopy. Although there is the presence of pure elements with HCP crystalline structure, the XRD patterns of as-milled powders revealed the presence of a mixture of nanocrystalline solid solution with FCC and BCC structure phases. The hardness of the powder samples was evaluated by Vickers microhardness testing. The average microhardness values indicate that the alloy with the greatest hardness is the NiCoAlFeMoCr.