Abstract. The transformation of agricultural waste into activated carbon represents an attractive approach as new and alternative source, but also as a reduction of pollution associated to the degradation of precursors. The organic residues sugarcane (Saccharum officinarum) bagasse-shell, orange (Citrus sinensis) peel-bagasse, and eucalyptus (Eucalyptus globulus) leaves, obtained from a biodrying process were transformed into activated carbons using phosphoric acid as activating agent. The resulting materials were physicochemically characterized and after that, carbonaceous electrodes were prepared to test the feasibility of using them in a discoloration electro-Fenton wastewater treatment process. Orange peel-bagasse biodried precursor transformed into activated carbon showed the highest efficiency when used as the modifier in a carbon paste electrode due to its highest porosity, electroactive area (24.9x10-2 cm2), and roughness (1.21 a.u.), also to its chemical affinity for anionic molecules. These properties, in addition to the capability of electro-sorb iron ions on the surface during the Fenton reaction, allowed a 44 % methyl orange discoloration efficiency. Sugarcane bagasse-peel and eucalyptus leaves biodried residues were also evaluated with efficiencies under 30 %, mainly attributed to intrinsic composition of the precursor materials.

Resumen. La transformación de los residuos agrícolas en carbón activado representa un enfoque atractivo y novedoso, además de que representa una alternativa a la reducción de la contaminación asociada a la degradación de residuos orgánicos. Los residuos orgánicos de bagazo de caña de azúcar (Saccharum officinarum), bagazo y cáscara de naranja (Citrus sinensis), y hojas de eucalipto (Eucalyptus globulus), que fueron obtenidos de un proceso de biosecado, se transformaron en carbón activado utilizando ácido fosfórico como agente activante. Los materiales resultantes se caracterizaron fisicoquímicamente y después de eso, se prepararon electrodos de pasta de carbón modificados con estos materiales, para estudiar la viabilidad de utilizarlos en un proceso de tratamiento de aguas residualesmediante electro-Fenton. El precursor biosecado de bagazo y cáscara de naranja transformado en carbón activado mostró la mayor eficiencia cuando se usó como modificador en un electrodo de pasta de carbón, debido a su mayor porosidad, área electroactiva (24.9x10-2 cm2) y rugosidad (1.21), también debido a su mayor afinidad química por moléculas aniónicas. Estas propiedades, aunadas a la capacidad de electro-sorber iones de hierro en la superficie durante la reacción de Fenton, permitieron una eficiencia de decoloración del naranja de metilo del 44 %. También se evaluaron residuos biosecados de bagazo de caña de azúcar y hojas de eucalipto, con eficiencias inferiores al 30 %, atribuidas principalmente a la composición intrínseca de los materiales precursores.

Abstract: Fluoride compounds are widely distributed in nature and are generated in many industrial processes. In many parts of the world, significant causes of diseases are associated with elevated concentrations in drinking water. In comparison with other techniques, adsorption onto a solid surface (activated alumina, activated charcoal, zeolites, etc.) is a simple, versatile, and appropriate process for removal the fluoride. In this study, we synthesized Gamma alumina (γ-Al2O3) by homogeneous precipitation and compared its effectiveness at removing fluoride from water to a commercial brand activated charcoal. Process was carried out at pH 5 and 7. Fibrillar morphology of the γ-Al2O3 powder presents high porosity in comparison with the activated charcoal that has many small pores in its compact structure. Mesoporous γ-Al2O3 powder has a lower surface area (332 m2 • g-1) than microporous charcoal powder (601 m2 • g-1), as determined by both gas nitrogen adsorption-desorption and scanning electron microscopy. However, γ-Al2O3 has a higher zeta potential and lower particle size than that determined for the activated charcoal. Adsorption isotherms of the fluoride removal concur with the Langmuir model for both adsorbents. γ-Al2O3 removes up to 95.5% of fluoride ions, significantly more than the activated charcoal (26%) at pH 5. Thus, based on results obtained, the adsorption process is controlled by the diffusion of fluoride ions in liquid immediately adjacent the outer surface of the adsorbent material.

Resumen: Los compuestos de fluoruro están ampliamente distribuidos en la naturaleza y se generan en varios procesos industriales. En muchas partes del mundo, las causas importantes de enfermedades están asociadas con concentraciones elevadas de estos elementos en el agua potable. En comparación con otras técnicas, la adsorción sobre una superficie sólida (alúmina activada, carbón activado, zeolitas, etc.) es un proceso simple, versátil y adecuado para la eliminación del fluoruro. La gamma alúmina (γ-Al2O3) sintetizada por precipitación homogénea se comparó con carbón activado comercial para la eliminación del fluoruro presente en el agua. El proceso se realizó a pH 5 y pH 7. La morfología fibrilar del polvo de γ-Al2O3 presenta alta porosidad en comparación con el carbón activado, que muestra una gran cantidad de pequeños poros en su estructura compacta. Según lo determinado por adsorción-desorción de gas nitrógeno, el polvo de γ-Al2O3 mesoporosa tiene un área de superficie menor (332 m2 • g-1) que la obtenida para el polvo de carbón activado microporoso (601 m2 • g-1), concordando con la porosidad observada por microscopía electrónica de barrido. Por otra parte, la γ-Al2O3 tiene un potencial zeta mayor y tamaño de partícula menor que la determinada para el carbón activado. Las isotermas de adsorción del fluoruro concuerdan con el modelo de Langmuir para ambos adsorbentes. La γ-Al2O3 elimina hasta el 95.5% de ion fluoruro mucho más que el carbón activado (26%) a pH 5. Así, con base en los resultados obtenidos se puede decir que el proceso de adsorción es controlado por la difusión de iones de fluoruro que están presentes en el agua inmediatamente adyacente a la superficie exterior del material adsorbente.

Avaliou-se o efeito da administração de clenbuterol (CB) como promotor de ganho de peso em frangos, dos 28 (início do experimento) aos 56 dias de idade (final do experimento). CB foi adicionado às dietas nas dosagens de 0 (controle), 0,21, 0,42 e 0,84ppm. Utilizaram-se 75 frangos em cada tratamento, registrando-se o peso corporal, o consumo de alimento, a gordura abdominal e a proteína muscular. A partir do 20º dia do experimento (48 dias de idade) até o seu final o efeito da administração de CB foi significativo. Frangos que receberam dosagens mais elevadas de CB estavam mais pesados. Observou-se também diminuição na deposição de gordura no abdômen com o aumento das dosagens de CB na dieta.

The objective of this study was to evaluate the effect of clenbuterol (CB), a beta2-adrenergic agonist, as a growth and weight gain promoter in broilers. Effects of CB were assessed, mixing it in feed at 0.0, 0.21, 0.42 and 0.84ppm, and feeding during four weeks to four groups (n=75) of 28 day-old Arbor Acres chickens. The body weight (BW) and food intake at 0, 12, 20 and 28 days of the study were recorded. Also abdominal fat (AF) and total muscle proteins were measured. Results indicate that from day 20 until the last of the experimental period (56-day-old), efficacy of CB was evident to increase growth and decrease AF deposition rates (P<0.01), in a dose-response pattern, suggesting that CB has a profitable growth promoting effect in broiler chickens.