The purpose of this work was to evaluate the microstructural alterations associated to the aging thermal treatments performed at 450, 475, 800 and 850°C, for 1, 3 and 12h, besides evaluating the influence of the precipitation of the alpha line phase on corrosion resistance. The samples were characterized by scanning electron microscopy, energy dispersion spectrometry, X-ray diffraction, feritscope, hardness, microhardness, in addition cyclic potentiodynamic polarization and double loop electrochemical potentiokinetic reactivation. In the agings performed at 450°C for 1h and 475°C for 12h, there was precipitation of the alpha line phase inside the ferrite and there was no significant effect on the resistance to pitting corrosion and the phenomenon of sensitization was not promoted. In the aging at 800 and 850°C for 1, 3 and 12h, the sigma phase was formed from the consumption of ferrite, and in the aging at 850°C there was the precipitation of the chi phase, promoting the increase in steel hardness. In agings for 12 h at 800 and 850°C, there was resistance to pitting corrosion decrease and the phenomenon of sensitization was moderated promoted at 800°C, with just the sigma phase precipitation and promoted at 850°C with sigma and chi phases precipitation.

Abstract Aluminum alloys have been widely used in multiple applications, such as in civil construction and engine pistons. They are subjected to loads that may impair their mechanical properties. Thereby, this research aims to study the influence of anodization on the mechanical properties of alloy samples and evaluate the behavior of oxide films when subjected to tensile testing. The mechanical properties of specimens have been evaluated based on tensile and Knoop hardness tests, and strain, tensile strength, and modulus of elasticity of specimens have been determined based on the stress-strain curve. The morphology of oxide films was analyzed by scanning electron microscopy (SEM) and optical microscopy (OM). Results of anodized Al-Si alloys in both modes, i.e. pulsed and direct currents, were compared, and it was found that pulsed current was more efficient than direct current with respect to uniformity of the formed film, and that the anodization process can affect a few mechanical properties of samples. The tension testing results also revealed that the oxide film has been fractured perpendicularly towards traction. However, the oxide film hardness was not affected by the anodization mode (pulsed or direct currents). In addition, a heat treatment was efficient at improving the uniformity of anodic films.

Austenitic stainless steels processed by rolling are widespread in technological applications, since they have excellent mechanical and corrosion properties. This study investigated the effect of the cooling rate, microstructure and properties of 316L austenitic stainless steel under cold rolled conditions and by rapid solidification. The microstructure of the cold rolling processing steel was composed of austenite and a low percentage of delta ferrite. For the rapid solidification condition, the microstructure evolved from columnar and acicular dendrites to equiaxed dendrites with decreasing cooling rates, without the presence of delta ferrite due to the high cooling rate. Furthermore, thermal analyses in both routes revealed that oxidation kinetics was slower after rapid solidification in synthetic air. The microhardness in the cold rolling condition was lower than in the rapid solidification condition since the microstructure under the solidification condition is more refined. The sample in the rapid solidification condition region RS1 presented the highest corrosion resistance considering the pit potential. The passivation current density in the cold rolled condition was 5.72x10-5A/cm2, while under the rapid solidification condition, regions RS1 and RS2 were 2.24x10-5 A/cm2 and 3.72x10-6 A/cm2, respectively, and region RS3, did not present a passivation region in a broad range of potentials.

The objective of this work was the conformation of ribbons from Sn3Zn alloy and Sn pure, using the melt-spinning fast cooling technique, in order to investigate the applicability as biomaterial. The ribbons were coated with 1% poly-caprolactone (PCL) and subsequent incorporation of silver nanoparticles (NPAg). In the uncoated ribbon was observing a surface roughness due of agglomerate caused by rapid solidification. In the ribbon coated with PCL and NPAg incorporation, it was observed that these compounds adhered to the ribbon. X-ray diffraction analysis showed no ribbons amorphization. The analysis by differential scanning calorimetry, indicated that the Sn3Zn ribbon had a lower melting temperature (198.1°C) than the Sn ribbon (228.7°C). The microhardness of Sn3Zn ribbon was 13.38 HV and Sn ribbon was 11.00 HV, both for the face without contact with the cooling wheel. In the bioactivity assays, performed in simulated body fluid medium, all samples showed apatites formation after four weeks of testing.

With technological advances in the several areas of knowledge, the constant search for materials with characteristics that meet certain applications has been growing, especially in the chemical and petrochemical industries, where materials capable of withstanding the conditions of corrosion in aggressive environments are required. The aim of this paper was to analyze the influence of the alloy element molybdenum on the microstructure and the resistance to corrosion of two duplex stainless steels identified as A (with molybdenum) and B (without molybdenum), after solution-treated under the following conditions: heating at 1100ºC for 30, 120 and 240 minutes. The steels were characterized by SEM, EDS, DRX and microhardness. The rise in solution treatment time fostered an increase in the volumetric fraction of the ferrite phase, in both steels. The solution treatment at 1100ºC for 120 minutes, for steels A and B, provided good resistance to pit corrosion, as well as the development of a passivating film in the solution of lithium chloride (120,000 ppm of chloride ions).

Titanium is used in orthopedic and orthodontic implants because it has good corrosion resistance and excellent biocompatibility. Thus, studies seek to obtain a coating to improve the adhesion between the bone and the implant, by modifying the metal’s surface. The objective of this work was to biomimetically coat C.P. Ti with hydroxyapatite doped with silver nitrate, a component with antimicrobial properties, coating the metallic-ceramic composite with a polycaprolactone polymer film, which is known by generate improved implant-tissue interaction, and reducing postoperative complications from bacterial infections. The characterization of the material demonstrated the existence of the coating overall surface of the metallic substrate. The results obtained from the bacterial culture tests with Staphylococcus aureus showed that nitrate was effective in reducing the amount of live bacteria present in the supernatant, as well as those adhered to the surface of the material. In addition, the polymeric coating did not prevent the release of the bactericidal agent, not interfering in the effect there.

Sigma phase leads to deterioration of corrosion resistance of super duplex stainless steels (SDSS) and its volume fraction increases as the time which the materials is exposed in determined temperature increases. In the present study, the effect of the short aging time on the formation of the sigma phase and on the corrosion behavior of UNS S32520 SDSS at 3.5% sodium chloride solution was evaluated using microstructural characterization, linear potentiodynamic polarization curve and electrochemical impedance spectroscopy. The results indicated that the SDSS sample solution-treated at 1150ºC and aged at 850ºC for 5 min may improve the corrosion resistance in comparison with the as-received and solution-treated conditions, due to the better partition of the elements Cr, Mo and dissolution of certain amount of sigma phase in the microstructure. However, results also showed that when SDSS solution-treated at 1150ºC is aged at 850ºC with the aging time slightly superior (10 min), the precipitation of sigma phase increases leading to a rapid deterioration of the corrosion resistance of the material.

Heart diseases affect part of world population and generally involves the functioning of valves. Valves replacement is the most common treatment and the choice between synthetic or natural/biological implants depends on several factors. Synthetic implants have greater durability, whereas biological ones are more biocompatible. This work proposes the use of polymeric coating on titanium metal surface to increase implant biocompatibility. Poly-caprolactone (PCL) has demonstrated greater efficacy for biomedical applications due to its biocompatibility. It can easily form films and coat surfaces. Titanium discs were submitted to alkaline and thermal treatments and coated with 1%PCL and 1%PCL+TiO2. For both conditions, PCL crystals were found in titanium coated surface (SEM and EDX) and X-ray diffractogram confirmed PCL coating. Infrared Spectroscopy spectra showed both PCL and TiO2 characteristic peaks. Moreover, corrosion resistance of coated disc has considerably increased, proving the effectiveness of PCL as coating material and its potential application in cardiac valves.

The thermal treatments employed in alloys are essential to obtaining desired microstructures and corrosion resistance properties. In this paper the low carbon martensitic steel 13Cr4Ni0.2C with different tempering temperatures was studied using potentiodynamic polarization technique in synthetic marine environment, in order to evaluate the effect of the tempering temperature on the steel corrosion resistance in an environment that simulates the conditions of use in oil and gas production. Microscopy results showed differences in the microstructure of tempered steel at low (620°C) and high (770°C) temperatures, indicating the appearance and extending of martensite laths with increasing temperature. Polarization tests showed that tempering temperature located between 620°C and 710°C indicated passive film formation and tempering temperatures of around 620 °C showed better resistance values to pitting corrosion.

Biomaterials are effective alternatives for tissue substitution, including the bone tissue, since they do not pose risks of transmission of diseases or immune rejection. Nowadays, there is an interest in new materials capable of being associated with other substances which favor bone formation, especially natural biopolymers, in particular chitosan, which may present a potential for repairing bone defects and forms films that adhere to metal surfaces. Titanium, despite being a material greatly employed in implants because of its excellent physical properties, does not present bioactive characteristics, making it necessary to use methods of surface modification to enhance its biological response, favoring bone formation. This work aims at studying commercially pure titanium (cp-Ti) coating with chitosan using the biomimetic method and the evaluation of the effects of process variables as substrate surface conditions. Subsequently, the incorporation of AgNO3 was studied and its effects on corrosion resistance were evaluated. To evaluate the coating process, several tests were conducted, such as scanning electron microscopy, X-ray diffraction and infrared spectroscopy. From the results obtained, the efficacy of the chitosan film in inhibiting the corrosion of the metals is concluded, which was the target of this study, thus justifying its use for osseointegration and in several implants.

This study aimed to investigate the effects of difference in nickel content and the tempering temperatures on the corrosion resistance in 13Cr2Ni0.1C and 13Cr1Ni0.15C steels. Results showed that passive film in 13Cr2Ni0.1C steel is formed more quickly at the lowest and highest tempering temperature (650°C and 750°C) but the lowest tempering temperature (650°C) showed better resistance to corrosion pitting. There was passive film formation and pitting corrosion in all tempering temperatures of the 13Cr1Ni0.15C steel and changes in tempering temperature does not significantly alter polarization curves, showing similar behavior to steel 13Cr2Ni0.1C tempered at 650°C.

The formation of intermetallic phases alters the properties of duplex stainless steel and is therefore a crucial factor in its performance. For example, the formation of sigma phase in duplex steel increases its brittleness and decreases its corrosion resistance because this phase consumes chromium and molybdenum in solid solution, thus leading to the depletion of these elements in the matrix. This study investigated the corrosion resistance of as-cast SAF 2205 duplex stainless steel after solution annealing treatment at 1100 °C for 240 minutes, under varying cooling rates. The objective was to evaluate the correlation between cooling condition, microstructural changes and corrosion resistance based on cyclic potentiodynamic polarization and double loop electrochemical potentiokinetic reactivation (DL-EPR) measurements. The results revealed a significant reduction in the corrosion resistance of a slowly cooled sample, which presented an increase in the degree of Cr (Qr / Qa) depletion resulting from the formation of sigma phase.

AbstractPrimarily, tempering is used in martensitic stainless steels with low carbon in order to change their mechanical properties. However, it also modifies the corrosion properties; usually depending on the temperature and duration of the heat treatment. This work investigated the impact of tempering on the corrosion of 13Cr4Ni0.02C and 13Cr1Ni0.15C (% weight) steels. Samples were tempered at 650º, 700º and 750ºC, characterized by optical microscopy and cyclic anodic polarization tests in a synthetic marine environment. The results showed differences in the microstructure of the 13Cr4Ni0.02C tempered samples, which changed from lath to lamellar with precipitates in the prior austenite grain boundaries. On the other hand, tempering did not affect the 13Cr1Ni0.15C microstructure. The anodic polarization tests showed that the pitting potential of the 13Cr4Ni0.02C samples decreased with the tempering temperature increasing. Similar values of pitting potential were found with the 13Cr1Ni0.15C tempered samples, which were lower than the 13Cr4Ni0.02C samples after tempering. It shows that even though the corrosion resistance of the 13Cr4Ni0.02C reduces when the tempering temperature was increased, it is better than that presented by 13Cr1Ni0.15C.

Novas classes de aços inoxidáveis martensíticos, com baixo teor de carbono, têm sido desenvolvidas, para atender, principalmente, às necessidades do segmento da indústria do petróleo. Contudo o seu uso tem sido restrito pelo fato de ser um desenvolvimento recente e muitas de suas propriedades ainda são motivos de investigação. Nesse trabalho, foram determinados os valores das temperaturas inicial e final da transformação austenítica e as temperaturas de início e fim da formação martensítica, para a liga 13Cr2Ni0,1C, através de ensaios dilatométricos com resfriamento contínuo. Com base nesses resultados, foram obtidas as condições otimizadas dos tratamentos térmicos de têmpera e revenido. A caracterização microestrutural das ligas na condição de bruta fusão foi realizada por microscopia ótica observando-se uma matriz martensítica com a presença de ferrita delta.

New classes of martensitic stainless steels, with low carbon levels, have been developed aiming to meet the needs of the petroleum industry segment. However, their use has been restricted due to the fact it is a recent development and many of its properties are still under investigation. This work determines the values of initial and final temperatures for the austenitic transformation and the initial and final temperatures of martensitic formation for alloy 13Cr2Ni0,1C, by means of dilatometric tests under continuous cooling. Based on these results the optimized conditions for quench and temper heat treatments were obtained. The microstructural characterization of the alloys under coarse fusion condition was carried out by optical microscopy and the presence of delta-ferrite in the martensitic matrix was observed.

O concreto armado tem cada vez mais despertado interesse científico e tecnológico, principalmente no que se refere a sua melhoria e inovação, seja pela utilização de novos materiais ou pelo estudo da corrosão para evitar a deterioração das estruturas. Dessa forma, têm-se intensificado os estudos da corrosão em concreto armado, sendo que a maior dificuldade está em detectar o início da corrosão na armadura. Uma das causas de degradação do concreto armado e sua posterior corrosão da sua armadura é a sua exposição a ambientes industriais. Assim, é necessário melhorar o desempenho das estruturas, prevendo a vida útil e conhecendo as formas de prevenção para minimizar o processo corrosivo. Há métodos de controle da corrosão do aço, como a incorporação de inibidores no concreto, como o molibdato de sódio, que é um inibidor anódico e não poluente tóxico. Nesse trabalho, foi avaliada a eficiência do molibdato de sódio, nas concentrações de 0, 1, 2 e 4% em relação à massa de cimento, empregando espectroscopia de impedância eletroquímica, simulando uma atmosfera ácida como agente agressor. A concentração de 4% do inibidor foi a mais eficiente.

The reinforced concrete has more and more arisen scientific and technological interest concerned mainly to its innovation and improvement either by the utilization of new materials or by the study of corrosion to avoid structure deterioration. In that way, the study of corrosion in reinforced concrete has been intensified but the biggest difficult is to detect the beginning of the corrosion in the steel. One of the reasons of the reinforced concrete degradation and afterwards the corrosion in the steel is its exposition to industrial environments. Thus, it is necessary to improve the performance of the structures, foreseeing its useful life and knowing the manners of prevention to minimize the corrosive process. There are methods to control the corrosion of the steel as the annexation of concrete inhibitors such as the sodium molybdate, an anodic inhibitor and not a toxic pollutant. In this work the efficacy of the sodium molybdate was evaluated with concentrations of 0, 1, 2 and 4% related to the cement mass, employing the electrochemistry impedance spectroscopy, simulating an acid atmosphere as an aggressive agent. The concentration of 4% in the inhibitor was the most efficient.