In this work, La0.6M0.4Ni0.6Cu0.4O3 (M = Ag, Ba, and Ce, denoted as LANC, LBNC, and LCNC, respectively) electrocatalysts were synthesized by the Pechini method at 1023 K for two hours in air. Rietveld refinement allowed the identification of the crystallographic phases present in all oxides. The electrocatalytic performance of these oxides towards the oxygen reduction reaction (ORR) was examined in alkaline medium by rotating disk electrode (RDE) technique and scanning electrochemical microscopy (SECM) in the redox competition mode. The results indicate that the best performance was found with the LANC electrocatalyst prepared with carbon as a conducting agent (LANC/Carbon), which showed good catalytic activity towards the ORR via a pseudo four-electron transfer pathway. The enhanced electrocatalytic activity of LANC is probably a result of the presence of a Ag phase, which improves the synergistic effect between the perovskite and carbon added to increase the conductivity, thus leading to a higher ORR performance when compared to other materials.

Solid solution of iron doped potassium strontium niobate with KSr2(FeNb4)O15-Δ stoichiometry was prepared by high efficiency ball milling method. Structural characterization was carried out by X-ray diffraction. Crystalline structure was analyzed by the Rietveld refinements using the FullProf software. The results showed a tetragonal system with the tetragonal tungsten bronze structure - TTB (a = 12.4631 (2) Å and c = 3.9322 (6) Å, V = 610.78 (2) ų). In this work, the sites occupancy by the K+, Sr2+ and Fe3+ cations on the TTB structure were determined. NbO6 polihedra distortion and its correlation with the theoretical polarization are discussed.