Several studies have reported the benefits of sonic and/or ultrasonic instrumentation for root debridement, with most of them focusing on changes in periodontal clinical parameters. The present study investigated possible alterations in the tensile bond strength of crowns cemented with zinc phosphate cement to natural teeth after ultrasonic instrumentation. Forty recently extracted intact human third molars were selected, cleaned and stored in physiologic serum at 4°C. They received standard preparations, at a 16º convergence angle, and AgPd alloy crowns. The crowns were cemented with zinc phosphate cement and then divided into four groups of 10 teeth each. Each group was then subdivided into two subgroups, with one of the subgroups being submitted to 5,000 thermal cycles ranging from 55 ± 2 to 5 ± 2°C, while the other was not. Each group was submitted to ultrasonic instrumentation for different periods of time: group 1 - 0 min (control), group 2 - 5 min, group 3 - 10 min, and group 4 - 15 min. Tensile bond strength tests were performed with an Instron testing machine (model 4310). Statistical analysis was performed using ANOVA and Tukey's test at the 5% level of significance. A significant reduction in the tensile bond strength of crowns cemented with zinc phosphate and submitted to thermal cycles was observed at 15 min (196.75 N versus 0 min = 452.01 N, 5 min = 444.23 N and 10 min = 470.85 N). Thermal cycling and ultrasonic instrumentation for 15 min caused a significant reduction in tensile bond strength (p < .05).

InCeram (Vita Zahnfabrik- Germany) is known as a high strength ceramic being used for core crowns and for fixed partial denture frameworks. InCeram system consists of slip-casting technique which is used for to build the framework, which is then pre-sintered obtaining an open-pore microstructure. The material gains its strength by infiltration of the lanthanum glass into the porous microstructure. In this work, commercial alumina (Al2O3), alumina-zirconia (Al2O3-ZrO2) and glasses lanthanum oxide-rich powders, used in InCeram system, were characterized, using x ray diffraction, dilatometry and scanning electron microscopy. The characteristics of these powders were related aiming to consider their substitution for new ceramic materials.