Composite iron oxide-Zinc oxide (γ-Fe2O3/ZnO) was synthesized by two step method: in the first one step γ-Fe2O3 particles were obtained by a cetyltrimethylammonium hydroxide (CTAOH) assisted hydrothermal method at low temperature (60°C). In the second step, the γ-Fe2O3 particles were included in the ZnO particles synthesis, which were obtained by a hexamethylenetetramine (HMTA) assisted hydrothermal method at low temperature (90° C). SEM study of the samples revealed that the γ-Fe2O3/ZnO composites present a compact morphology. The γ-Fe2O3 and ZnO phases were identified by XRD, energy dispersive X-ray analysis (EDX) and analysis of the IR spectrum. The composite exhibit the characteristic emissions of ZnO under UV radiation and ferromagnetic behavior of γ-Fe2O3 under an external magnetic field.

En este trabajo el compuesto formado entre el óxido de hierro y el óxido de zinc (γ-Fe2O3/ZnO) fue sintetizado por el método sol-gel en dos pasos: en el primer paso partículas del óxido de hierro γ-Fe2O3 fueron obtenidas por el método hidrotérmico asistido con hidróxido de cetiltrimetilamonio (CTAOH) a baja temperatura (60°C). En el segundo paso, las partículas del óxido γ-Fe2O3 fueron incluidas en la síntesis de las partículas de ZnO las cuales fueron obtenidas por el método hidrotérmico asistido con hexametilentetramina HMTA) a una temperatura de 90°C. El análisis SEM de las muestra revele) que las partículas del compuesto γ-Fe2O3/ZnO presentan una morfología redonda compacta. Las fases γ-Fe2O3 y ZnO fueron identificadas por XRD, análisis de rayos x con energía dispersiva (EDX), y análisis de espectro IR. El compuesto exibe emisión característica del ZnO bajo radiación UV y comportamiento ferromagnético del γ-Fe2O3 bajo un campo magnético.

Electrical characteristics of thin films of aluminum oxide prepared by spray pyrolysis were studied. The films were prepared from solution onto single crystal GaAs (100) substrates at temperatures from 300°C to 600°C. The electrical characteristics of these films as a function of the substrate temperature were determined from the capacitance and current versus voltage measurements of metal-oxide-semiconductor (MOS) structures incorporating them. The interface states density was of the order of 10(12) 1/eV-cm² and the films can stand electric fields higher than 5MV/cm, without observing destructive dielectric breakdown. The refractive index at 633 nm near to 1.64 was measured by ellipsometry.

Se estudiaron las características eléctricas de películas delgadas de óxido de aluminio preparadas por la técnica de rocío pirolítico ultrasónico. Las películas delgadas se depositaron a partir de una solución de acetilacetonato de aluminio en N,N-dimetilformamida sobre substratos monocristalinos de GaAs (100) tipo-p. La temperatura de depósito fue de 300 a 600 ºC. Las propiedades eléctricas de las películas en función de la temperatura de substrato se determinaron por medidas de capacitancia y corriente contra voltaje mediante la incorporación de las películas en estructuras tipo MOS (metal-óxido-semiconductor). La densidad de estados de interfaz resultó del orden de 10(12) 1/eV-cm² y el dispositivo MOS soportó campos eléctricos mayores a 5MV/cm, sin mostrar rompimiento dieléctrico. El índice de refracción se determinó por elipsometría a 633nm, con un valor máximo del orden de 1.64.

Titanium Carbide TiCx was deposited onto quartz substrates by the chemical vapour deposition (CVD) method. TiCx thin films were obtained from titanium tetrachloride (TiCl4) and toluene (C6H5CH3) as carbon source. Deposits were carried out in the range of substrate temperatures from 300 to 1100 °C, with a source gas molar ratio (C6H5CH3/TiCl4 + C6H5CH3 ) of 0.8. There was two deposit processes; the first was to carry out without nickel as catalyst and the second with nickel as catalyst. Results showed that the effect of nickel as catalyst is very relevant to obtain TiCx. TiC0.87 thin films, 0.5 mum thickness, were obtained for deposition temperatures above 900°C using nickel as catalyst. In this case a cubic structure, with a lattice parameter of 4.327 Å and a hardness of 2900 Vickers, was obtained at 1100(0)C. whilst for substrate temperatures between 300 to 900°C with nickel as catalyst amorphous carbon samples were obtained. For the samples prepared without the presence of the nickel as catalyst only C amorphous thin films were obtained for all deposit temperatures.

Purpose: To show the utility of optical coherence tomography (OCT) for studying the anterior segment and to explain its potential advantages as compared to ultrasonic biomicroscopy (UBM). Materials and methods: We have described the findings in 5 patients with different pathologies of the anterior segment, all of whom were studied with UBM and OCT-3 adjusted for the anterior segment. There were 2 cases of an acute attack of closed angle glaucoma, 1 case of rubeosis iridis, 1 case of penetrating ocular trauma and 1 case of a primary stromal iris cyst. Results: OCT was found to be as useful as UBM in detecting angle closure in patients affected by an acute attack of glaucoma. In addition, OCT was more comfortable for the patient and faster than UBM in obtaining images, with the exploration mean time using OCT being less than five minutes while that with UBM was over ten minutes. OCT has also been demonstrated to be a safe and valuable non-contact examination in other iris pathologies such as rubeosis iridis, for checking the permeability of iridotomies and even for studying iris masses such as primary stromal iris cysts. In these entities OCT may reach a higher resolution than ultrasonic biomicroscopy. Conclusion: OCT-3, with an adjustable focus, can obtain images from the scleral angle, as well as from other ocular structures like the iris, thus assisting in the diagnosis of numerous pathologies.

Objetivo: Dar a conocer la utilidad de la Tomografía de Coherencia Óptica (OCT) para el estudio de patología del segmento anterior así como presentar sus posibles ventajas frente a la biomicroscopía ultrasónica (BMU). Material y métodos: Presentamos 5 pacientes con diversas patologías del segmento anterior estudiados mediante OCT: 2 pacientes con ataque agudo de glaucoma de ángulo estrecho, 1 paciente con rubeosis iridis, 1 paciente con un traumatismo ocular penetrante y un paciente con un quiste estromal primario del iris. Resultados: En los pacientes con ataque agudo de glaucoma, el OCT ha mostrado ser una herramienta tan útil como la BMU para la detección del cierre angular. Además, la tomografía óptica fue más cómoda y rápida en la obtención de las imágenes que la BMU, así la el tiempo medio de exploración con OCT suele ser inferior a 5 minutos, a diferencia de la BMU cuyo tiempo suele ser superior a 10 minutos. El OCT también ha demostrado ser una prueba útil para el estudio de otras patologías del iris, permitiendo valorar la permeabilidad de las iridotomías, mostrar neovascularización iridiana e incluso estudiar masas iridianas como el quiste estromal de iris. En estos casos, el OCT permite la obtención de imágenes con una mayor resolución espacial que la BMU. Conclusiones: El OCT 3 mediante el ajuste del enfoque puede servir para obtener imágenes del ángulo camerular así como de otras estructuras del segmento anterior ayudando así a establecer determinados diagnósticos de forma no invasiva, cómoda y segura para el paciente.