The influence of Nb content variation on the microstructural and thermal characteristics of NiTiNb alloys was evaluated since these aspects are relevant to the control and adequacy of its shape memory properties for application purposes. The aim of this study was to observe how the Nb content acts in the formation of Nb-rich precipitates and the eutectic structures, which can make this alloys more complex. Microstructural characterization of the alloys was performed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and microanalysis by energy-dispersive X-ray spectroscopy (EDS), besides the thermal characterization by differential scanning calorimetry (DSC), and the comparison between the Nb alloys and the NiTi binary alloy. The results demonstrated a proportional dependence between the amount of β-Nb phase in the microstructures and the amount of Nb dissolved in the NiTi matrix with the Nb content. Although it was found that the increase in the Nb content causes the decrease of the martensitic (Mi) and reverse (Ai) transformation temperatures, the magnitude of thermal hysteresis was not significantly changed.

The formation of intermetallic phases alters the properties of duplex stainless steel and is therefore a crucial factor in its performance. For example, the formation of sigma phase in duplex steel increases its brittleness and decreases its corrosion resistance because this phase consumes chromium and molybdenum in solid solution, thus leading to the depletion of these elements in the matrix. This study investigated the corrosion resistance of as-cast SAF 2205 duplex stainless steel after solution annealing treatment at 1100 °C for 240 minutes, under varying cooling rates. The objective was to evaluate the correlation between cooling condition, microstructural changes and corrosion resistance based on cyclic potentiodynamic polarization and double loop electrochemical potentiokinetic reactivation (DL-EPR) measurements. The results revealed a significant reduction in the corrosion resistance of a slowly cooled sample, which presented an increase in the degree of Cr (Qr / Qa) depletion resulting from the formation of sigma phase.

Neste trabalho, tubos de aço inoxidável supermartensítico (AISM) foram soldados por fricção radial (SFR) e suas propriedades de corrosão foram estudadas através de ensaios de polarização anódica em solução de 3,5 % de NaCl e da técnica eletroquímica de reativação potenciocinética de ciclo duplo (DL-EPR). As medidas foram realizadas em amostras extraídas de diferentes regiões da solda SFR, i.e., metal de base (MB), interface de soldagem e anel consumível (AC). As propriedades de corrosão foram discutidas em termos da microestrutura metalúrgica resultante em cada região. A precipitação de carbonetos de Cr que ocorre durante o tratamento de revenimento causa um empobrecimento em Cr substancial na estrutura revenida do MB (Ir/Ia = 54,22%). Por outro lado, as regiões do AC e da interface de soldagem, que tiveram suas microestruturas transformadas e seus precipitados de carboneto de Cr redissolvidos pelo ciclo termomecânico de soldagem SFR, apresentam um baixo grau de empobrecimento em Cr (Ir/Ia < 1%). A microestrutura do AC, composta de uma mistura de martensita temperada e austenita retida, apresenta maior resistência à corrosão localizada do que a estrutura revenida do MB. Também foi observado que a ferrita-δ diminui a resistência à corrosão por pites na região da interface de soldagem.

In this work, supermartensitic stainless steel pipes were radial friction (RF) welded and their corrosion behavior were studied based on potentiodynamic polarization and double loop - electrochemical potentiokinetic reactivation (DL-EPR) tests. Measurements were performed on samples taken from the base metal (BM), weld interface, and consumable ring (CR) of the RF weldment. The corrosion properties were discussed in terms of their resulting metallurgical microstructure. The precipitation of Cr carbides that takes place during the tempering treatment induces a substantial Cr depletion value (Ir/Ia = 54,22%). On the other hand, CR and weld interface regions, which had their microstructure transformed and their Cr carbide precipitates redissolved by the RF welding thermomechanical cycle, present a low level of Cr depletion (Ir/Ia < 1%). The AC microstructure, which is composed of a mixture of virgin martensite and stable retained austenite, presents an increase in pitting corrosion resistance compared to the tempered structure of the BM region. It was also observed that the δ-ferrite decreases the pitting resistance of the weld interface region.

O aço inoxidável AISI 444 tornou-se uma opção para substituir a liga AISI 316L devido ao seu menor custo e satisfatória resistência à corrosão. Entretanto, o uso da liga AISI 444 no feixe tubular de trocadores de calor acarreta na soldagem de uma junta dissimilar. O presente estudo teve por objetivo avaliar a resistência à corrosão da junta tubo-espelho soldada pelo processo TIG composta pelas ligas AISI 316L e AISI 444. A manufatura das amostras consistiu em replicar o projeto da junta tubo-espelho de trocadores de calor. Realizou-se em juntas soldadas ensaios de sensitização, perda de massa por imersão desde a temperatura ambiente até 90 ºC, e ensaios eletroquímicos de polarização potenciodinâmica nos eletrólitos 0,5 mol/L de HCl e 0,5 mol/L de H2SO4. Os resultados mostraram que a junta dissimilar sofreu corrosão galvânica com maior degradação na zona afetada pelo calor (ZAC) do tubo AISI 444. Porém, os mecanismos de corrosão localizada (pite e intergranular) demonstraram ser mais ativos para a liga AISI 316L. Conclui-se que a junta dissimilar apresentou melhor resistência à corrosão do que a junta soldada composta unicamente pela liga AISI 316L em temperaturas de até 70 ºC, conforme as condições observadas neste trabalho.

The AISI 444 stainless steel (SS) has become an option to substitute the AISI 316L SS because its low cost and satisfactory corrosion resistance. However, the use of AISI 444 alloy tubes in heat exchangers cause the welding of a dissimilar joint. The aim of this study was evaluate the corrosion resistance of the tube-to-tubesheet welded by TIG process composed of AISI 316L and AISI 444. Preparation of samples was executed through replication of tube-to-tubesheet joints. In order to test the corrosion resistance of welded joint the following tests were applied, sensitization, mass loss from room temperature up to 90 ºC, and electrochemical corrosion tests in 0,5 mol/L HCl and 0,5 mol/L H2SO4 electrolytes. The results have shown that the dissimilar joint suffers galvanic corrosion with increased degradation of the heat affected zone (HAZ) of the AISI 444 tube. Nevertheless, the mechanisms of localized corrosion (pit and intergranular) was more active in the AISI 316L alloy. It is concluded that the dissimilar joint showed better corrosion resistance than the welded joint composed solely by AISI 316L at temperatures up to 70 ºC, as the conditions observed in this work.

The corrosion properties of a 22.5 wt. (%) Cr duplex stainless steel were investigated after long-term aging of 3000, 5000 and 7000 hours at 300 and 400 ºC. The corrosion resistance was measured based on mass loss in a FeCl3 10 wt. (%) solution and electrochemical measurements in a 0.1 M H2SO4 solution. The results indicate that the corrosion resistance decreased steadily up to 5000 hours of aging. However, the samples subjected to 7000 hours of aging showed better corrosion resistance than those aged for 3000 and 5000 hours. This effect is attributed to the phase transformation that occurs during aging, a finding which was confirmed by hardness, transmission electron microscopy and X-ray photoelectron spectroscopy measurements.

Os aços inoxidáveis supermartensíticos são utilizados nas indústrias de petróleo e gás, pois aliam boas propriedades mecânicas, soldabilidade e excelente resistência à corrosão. Eles são endurecidos pelo tratamento térmico de têmpera e, para otimizar suas propriedades mecânicas, são submetidos ao revenimento. Durante o revenimento, ocorre precipitação de fases, que, dependendo dos parâmetros temperatura e tempo, induz alterações indesejadas nas propriedades desses aços. Nesse trabalho, o objetivo foi estudar a microestrutura e a resistência à corrosão de um aço inoxidável supermartensítico em diferentes condições de revenido (550°C, 600°C e 650°C). Observou-se, na microestrutura da amostra revenida a 650°C, a formação de austenita e precipitados de cromo do tipo Cr3C2 e Cr7C3. As curvas de polarização indicaram que o tratamento térmico influencia o comportamento anódico, modificando a região passiva e as características do filme passivo. O revenido altera a resistência à corrosão, com o grau de sensitização diminuindo com o aumento de temperatura de 550°C para 650°C, devido à recuperação das zonas empobrecidas de cromo.

Supermartensitic stainless steels have been used in the oil and gas industry for onshore and offshore tubing applications, due to their good mechanical properties, weldability and excellent corrosion resistance. They are hardened by quenching heat treatment, and to improve their toughness, are submitted to tempering. During the tempering, some phase precipitation occurs, which depending on the time and temperature parameters, produces some undesired changes in the steel properties. The aim of this research was to study the microstructure and the corrosion resistance of supermartensitic stainless steel in quenched and different tempered conditions (550°C, 600°C and 650°C). At the microstructure of the 650°C tempered sample was observed the formation of austenite and precipitates of chromium, like Cr3C2 and Cr7C3.The polarization curves indicated that the heat treatment influences the anodic behavior, changing the passive region and the passive film characteristics. The tempering changes the corrosion resistance, decreasing the degree of sensitization when increasing the temperature from 550°C to 650°C, this occurs due to the recovery of the chromium impoverished zones.

Fuels and biofuels have a major importance in the transportation sector of any country, contributing to their economic development. The utilization of these fuels implies their closer contact to metallic materials, which comprise vehicle, storage, and transportation systems. Thus, metallic corrosion could be related to fuels and biofuels utilization. Specially, the corrosion associated to gasoline, ethanol, diesel, biodiesel, and their mixtures is discussed in this article. Briefly, the ethanol is the most corrosive and gasoline the least. Few investigations about the effect of biodiesel indicate that the corrosion is associated to their unsaturation degree and the corrosion of diesel is related to its acidity.

O concreto armado tem cada vez mais despertado interesse científico e tecnológico, principalmente no que se refere a sua melhoria e inovação, seja pela utilização de novos materiais ou pelo estudo da corrosão para evitar a deterioração das estruturas. Dessa forma, têm-se intensificado os estudos da corrosão em concreto armado, sendo que a maior dificuldade está em detectar o início da corrosão na armadura. Uma das causas de degradação do concreto armado e sua posterior corrosão da sua armadura é a sua exposição a ambientes industriais. Assim, é necessário melhorar o desempenho das estruturas, prevendo a vida útil e conhecendo as formas de prevenção para minimizar o processo corrosivo. Há métodos de controle da corrosão do aço, como a incorporação de inibidores no concreto, como o molibdato de sódio, que é um inibidor anódico e não poluente tóxico. Nesse trabalho, foi avaliada a eficiência do molibdato de sódio, nas concentrações de 0, 1, 2 e 4% em relação à massa de cimento, empregando espectroscopia de impedância eletroquímica, simulando uma atmosfera ácida como agente agressor. A concentração de 4% do inibidor foi a mais eficiente.

The reinforced concrete has more and more arisen scientific and technological interest concerned mainly to its innovation and improvement either by the utilization of new materials or by the study of corrosion to avoid structure deterioration. In that way, the study of corrosion in reinforced concrete has been intensified but the biggest difficult is to detect the beginning of the corrosion in the steel. One of the reasons of the reinforced concrete degradation and afterwards the corrosion in the steel is its exposition to industrial environments. Thus, it is necessary to improve the performance of the structures, foreseeing its useful life and knowing the manners of prevention to minimize the corrosive process. There are methods to control the corrosion of the steel as the annexation of concrete inhibitors such as the sodium molybdate, an anodic inhibitor and not a toxic pollutant. In this work the efficacy of the sodium molybdate was evaluated with concentrations of 0, 1, 2 and 4% related to the cement mass, employing the electrochemistry impedance spectroscopy, simulating an acid atmosphere as an aggressive agent. The concentration of 4% in the inhibitor was the most efficient.

Nesse trabalho, a microscopia de varredura por sonda (Scanning Probe Microscopy - SPM), nos modos contato (Atomic Force Microscopy - AFM) e de força magnética (Magnetic Force Microscopy - MFM), foi utilizada para analisar a microestrutura de um aço inoxidável dúplex 2205 solubilizado e envelhecido. Foi feita uma análise por AFM da superfície do aço solubilizado após crescimento de filme passivo. Por AFM, obteve-se indicação de crescimento de filme sobre a microestrutura do aço solubilizado, enquanto por MFM a distribuição de fases pôde ser observada sem a necessidade de ataque da superfície.

In this work, Scanning Probe Microscopy (SPM), in the contact (Atomic Force Microscopy - AFM) and magnetic force (Magnetic Force Microscopy - MFM) modes, has been used to analyze the microstructure of a solution-treated and aged 2205 duplex stainless steel. A surface analysis of the solution-treated steel has been performed by AFM after passive film growth. By AFM it was obtained a indication of film growth on the microstructure of the solution-treated steel, while by MFM the phase distribution could be observed without the need of surface etching.

Esse trabalho estuda a resistência à corrosão do aço inoxidável martensítico fundido em meio marinho sintético saturado com CO2 e também faz uma comparação com solução aerada. A liga foi usada na condição temperada e revenida. A corrosão foi avaliada usando a técnica de polarização potenciodinâmica cíclica. As medidas de polarização foram obtidas em meio marinho sintético com concentrações de cloreto de 20000ppm e 80000ppm na temperatura ambiente. As curvas de polarização cíclica obtidas mostram uma região de passivação definida para as condições adotadas para o ensaio, sendo possível para a identificação dos parâmetros eletroquímicos, o potencial de pite, o potencial de proteção e a susceptibilidade ao pite. Em solução saturada com CO2 e concentração de cloreto de 20000ppm, o potencial de proteção aumentou e a susceptibilidade ao pite diminuiu, em comparação com a solução aerada. Em contraste, os potenciais de pite e de proteção decresceram em solução saturada com CO2 e concentração de cloreto de 80000ppm, indicando que a resistência ao pite é influenciada por um sinergismo entre a concentração de cloreto e a solução saturada com CO2.

This work studies the corrosion resistance of the martensitic stainless steel cast in CO2-saturated synthetic seawater. A comparison is also made with an aerated solution. The alloy was used in a quenched and tempered condition. The corrosion behavior was evaluated using the cyclic potentiodynamic polarization technique. The potentiodynamic polarization measurements were taken in synthetic seawater with 20000ppm and 80000ppm chloride contents at room temperature. The obtained cyclic polarization curves show a defined passive region for the adopted test conditions making possible the identification of the electrochemical parameters: pitting potential, protection potential and susceptibility to pitting. In the CO2 saturated solution and in the 20000ppm chloride contents, the protection potential increased and the pitting susceptibility decreased in comparison with the aerated solution. In contrast, the pitting and the protection potentials decreased in the CO2 saturated solution and in the 80000ppm chloride content indicating that the pitting resistance is influenced by a synergy between the chloride concentration and the CO2 saturated solution.

Atualmente, há muito interesse no desenvolvimento de materiais nanocristalinos e amorfos, que apresentem alta resistência mecânica combinada com boa ductilidade, abrindo grandes perspectivas tecnológicas para o processamento desses materiais. Devido a sua versatilidade, as ligas amorfas têm mostrado ter propriedades que podem ser utilizadas em diversas áreas, como em memórias de computadores, aplicações em vários tipos de transformadores para potência e usos eletrônicos. A técnica para obter as ligas amorfas utilizada nesse trabalho foi a de solidificação rápida a partir do estado líquido, por melt spinning. O processamento das fitas foi efetuado em duas etapas, inicialmente foi realizado a fusão da liga por indução magnética, posteriormente, a liga foi submetida a nova refusão para melhorar a homogeneização e, em seguida, produziu-se a fita metálica amorfa, utilizando uma taxa de resfriamento em torno de 10³°C/s. Durante o processamento, a fita obtida apresentou-se amorfa e com uma espessura em torno de 25µm.

Now, there is a lot of interest in the development of nanocrystalline and amorphous materials, that present high mechanical resistance combined with good ductility, opening great technological perspectives for the processing these of materials. Due to its versatility, the amorphous alloys have been showing to have properties that can be used in several areas, as in memory of computers, applications in several types of transformers for potency and electronic uses. The technique used to obtain of amorphous alloys in this work, it went to of rapid solidification starting from the liquid state, for melt spinning. The processing of the ribbons of was made in two stages, initially the coalition of the alloy was accomplished by magnetic induction, later on, the alloy was submitted the new remelting to improve the homogenizationand soon after, the amorphous metallic ribbon was produced, used of the high cooling rate, around 10³°C/s. During the processing, the obtained ribbon came amorphous and with a thickness around 25µm.

O aumento nos custos de equipamentos de Pesquisa e Desenvolvimento - P&D além da necessidade de aperfeiçoamento constante da mão-de-obra especializada, tem sido uma das principais razões para o fechamento de vários laboratórios de P&D das indústrias. Entretanto, como a pesquisa e desenvolvimento são essenciais para novos produtos em um mercado cada vez mais competitivo, diversos centros de P&D foram criados nos países desenvolvidos. No Brasil, o primeiro centro de prestação de serviços criado pelo Estado está localizado no campus da Universidade Federal de São Carlos: o Centro de Caracterização e Desenvolvimento de Materiais - CCDM, um projeto de US$ 5 milhões. A principal diferença entre o CCDM e os existentes centros de P&D no Brasil, é a de que o CCDM é uma entidade sem fins lucrativos, deve ser auto-sustentável e presta serviços para as empresas, universidades e institutos de pesquisas. Este trabalho apresentará a experiência deste primeiro centro no Brasil. O crescimento contínuo e o sucesso deste centro - exemplo de terceirização - deve conduzir a um progresso na pesquisa e desenvolvimento na área de Ciência e Engenharia de Materiais.

The increase of research and development equipment costs and the need of updating specialized staff has been the main reason for the cease of several industrial R&D laboratories. As R&D is essential for new products in a very competitive market, several industry-university cooperative research centers have been created in the developed countries. In Brazil the first center created by the government is located at the Federal University of São Carlos: the Center for Characterization and Development of Materials - CCDM, a US$ 5 millions project. The main difference among CCDM and the existing R&D centers in Brazil is that the CCDM is a non-profitable institution, has to be selfsupported and provides services to the industries, universities and research centers. This paper will present the experience of this first center in Brazil. The continued growth and success of this outsourcing center should lead to considerable progress in research and development in the field of Materials Science and Engineering.