Abstract Six sample preparation procedures were evaluated for selective extraction of Cr(VI) from commercial samples of chromium oxide green (Cr2O3) pigments prior to formation of its diphenylcarbazone complex [CrDPCO]- for determination by visible spectrophotometry: (I) water-soluble chromium; (II) EPA method 3060A without Mg2+; (III) EPA method 3060A with Mg2+; (IV) Na3PO4 based extraction; (V) method IRSA16 based on acidic extraction and; (VI) Na2CO3 based extraction. Evaluation of the influence of concomitant Cr(III) ions, time and stability of the [CrDPCO]- complex was investigated. Recoveries of soluble and insoluble Cr(VI) species were 86% and 80%, respectively, using procedure (VI). Direct calibration against aqueous standards prepared in the extraction medium was successful for Cr(VI) in the concentration range 0.05-1.50 μg L-1. Limits of detection and quantitation were 0.3 µg g-1 and 1.0 µg g-1, respectively, for 250 mg subsamples/25 mL. Procedure (VI) was applied to the analysis of four commercial samples of Cr2O3 pigments, three determined to have Cr(VI) within compliance limits below 1.0 µg g-1, but one at 16.6 ± 0.6 µg g-1, prohibiting use of this pigment in cosmetic formulations. This sample was conveniently employed to evaluate the accuracy of the method. The recommended procedure is simple and accurate and has been adopted by Tecpar’s laboratory of Parana Institute of Technology (Curitiba, Brazil).

ABSTRACT Determination of potential contaminants elements in food packing films arising from contact with acidic aqueous foods was undertaken by inductively coupled plasma optical emission spectrometry (ICP OES) in accordance with DIN EN 1186-1. Test sections from plastic films were totally immersed in 3% w/v CH3COOH used as the food simulant. Testing was conducted under three conditions: (1) 10 days at 40 ºC; (2) 30 min at 70 ºC and 10 days at 40 ºC; and (3) 30 min at 100 ºC and 10 days at 40 ºC. These time and temperature conditions were considered to be the most severe situations likely to be encountered in practice. Several different containers were investigated, including a borosilicate glass beaker, a glass bottle used for food canning, as well as one of polystyrene. The glass bottle was selected for testing treatments according to procedure (3) and a polystyrene one was chosen for use with procedures (1) and (2). Limits of quantitation were adequate for the determination of Ag, B, Ba, Cd, Cr, Cu, Pb, Sb, Sn and Zn by solution nebulization ICP OES and As by chemical vapor generation (CVG-ICP OES). Results for the analysis of AccuStandard certified reference materials as well as spike recoveries show good agreement with expected concentrations, demonstrating the accuracy and precision of the determinations. Eleven samples of food packing material were analyzed. The lead was present in the range 4.8 - 85.3 µg L-1 in 10 of 11 evaluated packing material, showing the importance of quality control measures.

An on-line method for Cd and Pb pre-concentration and simultaneous determination in acid digested seafood by inductively coupled plasma optical emission spectrometry (ICP OES) was developed. The on-line pre-concentration was based on the complex formation of the analytes with the ammonium salt of O,O-diethyldithiophosphate (DDTP) and using the Amberlite XAD-4 resin as a solid support in a homemade column. Different conditions of the flow injection system, such as solutions flow rates, nebulizer pressure and eluent concentration were optimized. Three certified reference materials of lobster hepatopancreas, dogfish liver and fish protein, three samples of fish muscle and three samples of shrimp were digested with HNO3, H2O2 and H2SO4 in a microwave system under reflux. DDTP was added in the solutions obtained, and the mixture was injected in the FI system. Calibration curves for Cd and Pb were obtained using the standard solutions in the concentration range 0.05-0.5 µg mL-1 in the digestion medium, submitted to the same pre-concentration procedure. The quantification limits (3.3 x LOD) for 5 min of pre-concentration time were 0.005 mg kg-1 Cd2+ and 0.1 mg kg-1 Pb2+ in the sample of fish or shrimp in natura, considering 1.0 g of the sample in a final volume of 50 mL. The agreement of the obtained concentrations with the certified ones (Student t-test, 95% confidence) and the recoveries of spiked real samples, from 90 to 120%, demonstrated good accuracy. Precision was also adequate, with relative standard deviations from 2 to 13%. The method was accurate, precise and certainly could be applied to the digested samples of different natures.

A method for evaluating inorganic constituents in the grass by ICP OES is proposed. The samples were digested with nitric acid plus hydrogen peroxide in a microwave system. Seventeen samples were collected in the metropolitan area of Curitiba and Castro in the Paraná State, Brazil. The following elements were studied: Al, As, Ba, Ca, Cd, Co, Cr, Cu, Fe, K, Mg, Mn, Mo, Na, Ni, P, Pb, Sb, Se and Zn. The linear coefficients of the curves were higher than 0.999 and the precision, expressed as the relative standard deviation, which was below 10%, being considered adequate. The accuracy was validated by using the recovery test (recoveries from 80 to 107%) and by the analysis of botanical certified materials. For one sample, two other digestion procedures, using two different mixtures of nitric and hydrochloric acids, produced results in agreement with the adopted procedure. Eleven out of the twenty studied elements could be quantified in real samples. High concentrations of Ca, K, Mg and P, the essential elements for bovines and other animals, were found. The results were evaluated using the principal component analysis that gathered the samples in three groups, according to the areas where the plants were grown.

Propõe-se uma nova maneira de gerar vapor de mercúrio em altos valores de pH pela adição de NaOH ou de outra base a uma solução contendo íons de mercúrio, sem utilizar redutor, como NaBH4 ou SnCl2. Após dissolução total da amostra em sistema de microondas fechado, empregando HNO3 e H2O2, o pH da solução da amostra é elevado para 13 com NaOH. Após 90 min de repouso, o vapor frio é transportado até o plasma por um fluxo de gás argônio. O Hg é determinado em 253,652 nm em um espectrômetro de emissão óptica com plasma indutivamente acoplado com configuração axial. O procedimento foi aplicado a cinco amostras biológicas certificadas obtendo-se um limite de detecção (3s, n = 10) de 0,04 µg g-1 para uma massa da amostra de 0,5 g em um volume final de 50 mL. A calibração foi realizada com soluções padrão aquosas em NaOH 0,1 mol L-1. O procedimento foi eficiente, com recuperações dos valores certificados entre 85 e 113%, demonstrando concordância entre o valor encontrado e o certificado para um nível de 95% de confiança (teste-t). A precisão apresentou resultados aceitáveis com desvios padrão relativos de 7 a 9%. Mercúrio a partir de espécies orgânicas em solução, não foi detectado; somente Hg2+ em solução produz sinal. O procedimento é novo, simples, pode permitir estudos de especiação e serve para demonstrar liberação de vapor de mercúrio de soluções aquosas em altos valores de pH.

A novel approach to the generation of mercury vapor at high pH by the simple addition of NaOH or other base to a solution containing mercury ions is described. Subsequent addition of another reducing agent, such as NaBH4 or SnCl2, is unnecessary. Following total dissolution of sample using HNO3 and H2O2 in a closed microwave vessel, the pH of the sample solution is increased to 13 by the addition of NaOH. After standing for 90 min in a closed vessel, the Hg0 is directed to the plasma by a flow of argon. Emission from mercury is measured at 253.652 nm by an axial view inductively coupled plasma optical emission spectrometer (ICP OES). The procedure was applied to five certified biological samples, yielding a detection limit (3s, n = 10) of 0.04 µg g-1 based on a nominal sample mass of 0.5 g in a final volume of 50 mL. Calibration was achieved using simple aqueous standard solutions containing 0.1 mol L-1 NaOH. The procedure was efficient, with determined values lying in the range of 85-113 % of the certified values, showing good agreement at the 95% confidence level (t-test). The precision was fit for purpose, with relative standard deviations ranging from 7 to 9%. Organomercury species in solution were not detected; only Hg2+ in solution produces a signal. This new procedure provides for a simple approach to quantitation (and potentially speciation).

O presente trabalho apresenta um estudo comparativo das técnicas ICP-MS e ICP OES com configuração axial e também de dois métodos diferentes de tratamento das amostras, ou seja, por dissolução total com e sem separação do cobre por eletrodeposição, para as determinações de As, Fe, Mn, Pb, Sb e Sn em amostras de cobre eletrolítico. Amostras comerciais e industriais foram dissolvidas com HNO3 5% v/v e o cobre foi eletrodepositado em meio de HNO3 (1,4% v/v) e H2SO4 (2,0% v/v). Verificou-se que a separação do cobre foi eficiente, contudo se constatou contaminação de Fe e Sn durante o processo de eletrodeposição. As determinações foram realizadas utilizando-se um ICP OES Axial Varian (Vista Pro) e um ICP-MS Perkin Elmer (Elan Sciex 6000). Foi aplicada a calibração externa, com soluções padrão contendo ou não cobre na concentração equivalente à da amostra. Os limites de detecção (3s, n=10) para a técnica de ICP OES foram bastante semelhantes na presença ou não do cobre). Já usando ICP-MS, os limites foram melhores na ausência do cobre. Com o objetivo de estabelecer o nível de significância entre as técnicas de quantificação, ou seja, entre ICP OES e ICP-MS,foi aplicado o teste t emparelhado, que demonstrou, para um nível de confiança de 95%, não haver diferença significativa, tanto para as soluções sem ou com cobre. Os resultados obtidos no presente trabalho demonstraram que as técnicas ICP-MS e ICP OES fornecem resultados similares em determinadas faixas de concentração dos analitos, podendo ambas serem utilizadas, no controle de qualidade do cobre eletrolítico. Contudo, a técnica ICP-MS foi superior em termos de limite de detecção.

The performance of axial view ICP OES and ICP-MS techniques were compared through the determination of As, Fe, Mn, Pb, Sb and Sn in electrolytic copper. Samples were prepared by two procedures: 1. Total dissolution with 5 % v/v HNO3 and 2. Dissolution with 1.4 % v/v HNO3 plus 2.0 % v/v H2SO4, followed by separation of the Cu by electrodeposition. The methods were applied for the analysis of standard copper solutions, using calibration against aqueous solutions with or without the addition of Cu. The results obtained by the two techniques were similar, but the separation of Cu from the sample matrix proved to be more adequate for practical reasons.