Abstract Core-shell particles were produced on seeded suspension polymerization by using polystyrene (PS) as polymer core, or seed, and methyl methacrylate (MMA) as the shell forming monomer. Two synthesis routes were evaluated by varying the PS seed conversion before MMA addition. The main purpose of this work was to investigate the influence of synthesis routes on the morphology and chemical resistance of the resulting particles. 1H NMR spectroscopy showed that the use of PS seeds with lower conversion led to the formation of higher amount of poly(styrene-co-MMA). The copolymer acted as a compatibilizer, decreasing the interfacial energy between both homopolymers. As a consequence, a larger amount of reduced PMMA cluster were formed, as was revealed by TEM measurements. Samples in this system showed enhanced resistance to cyclohexane attack compared with pure PS, with a PS extraction of only 37% after 54 hours test.

Abstract Films and sheets composed by poly (lactic acid) (PLA)/thermoplastic starch (TPS) and TPS/gelatin blends have already been produced and characterized in the literature. However, materials produced with these three biopolymers have not been clearly investigated. In this work, extruded sheets were produced with PLA, TPS (glycerol as plasticizer) and different amounts of gelatin (0, 1, 3 and 5 wt%) in a pilot scale co-rotating twin-screw extruder coupled with a calender. The extruded sheets were characterized in regards to their water solubility, thickness, density, water vapor permeability (WVP), moisture sorption isotherms, mechanical properties and microstructure. The results showed an increase in solubility and WVP besides a decrease of about 30% in tensile strength, Young's modulus and elongation at break. Extruded sheets microstructure revealed smother surfaces and homogeneous morphology with the addition of gelatin. The experiments demonstrated that extrusion and calendering process is a viable way to produce PLA/TPS/gelatin sheets with interesting properties.

Abstract Encapsulation of bioactive compounds has been carried out to improve bioavailability and to protect them against harm conditions. However, encapsulation processes are often aggressive and it is important that encapsulated substances keep their biological activity. In this work curcumin was nanoencapsulated using dichloromethane as solvent and ultrasound as dispersion device. Nanoparticles were obtained using different curcumin concentrations and encapsulants (PLLA and Eudragit S100) and the encapsulation efficiency was inferred using spectroscopic and calorimetric techniques as well as optical microscopy. Total phenolic contents and antioxidant activity tests were applied to the curcumin before and after encapsulation and also to blank polymer nanoparticles. Results demonstrated that the encapsulation process had no deleterious influence on its antioxidant activity.

Miniemulsion homopolymerization reactions of methyl methacrylate (MMA) and styrene (STY) using poly(L-lactide) as co-stabilizer were carried out in order to prepare poly(L-lactide)/poly(methyl methacrylate) (PLLA/PMMA) and poly(L-lactide)/polystyrene (PLLA/PS) binary blend nanoparticles. The effect of PLLA concentration on methyl methacrylate (MMA) and styrene (STY) homopolymerization reactions was evaluated. It was found that the incorporation of PLLA resulted on acceleration of MMA and STY homopolymerization reactions and led to a molar mass increase of up to 70% for PS in PLLA/PS blend nanoparticles in relation to those prepared without PLLA, which can be attributed to an increase of reaction loci viscosity (gel effect). PLLA also acted as an efficient co-stabilizer, since it was able to retard diffusional degradation of droplets when no other kind of co-stabilizer was used. Two isolated Tgs were found in both PLLA/PMMA and PLLA/PS blend nanoparticles which can be associated to blend immiscibility. TEM images corroborate these results, suggesting that immiscible PLLA/PMMA and PLLA/PS blend nanoparticles could be formed with two segregated phases and core-shell morphology.

O objetivo deste trabalho foi estudar formas de minimizar efeitos indesejáveis como a colmatação em leitos constituídos de argila através de sua fixação sobre a superfície de partículas poliméricas. Foram realizados ensaios preliminares aquecendo a argila Tonsil Terrana 580FF em estufas para se observar a variação da sua capacidade de adsorção de antocianinas de repolho roxo. Posteriormente, foram utilizadas 5 amostras de polietileno de alta densidade para a fixação da argila a temperaturas de 180°C-210°C durante 2 horas. As análises morfológicas das partículas obtidas foram realizadas através de microscopia eletrônica de varredura. Os experimentos preliminares demonstraram um incremento máximo de 15,65% na capacidade adsortiva da argila (120°C, 30 horas) e 16,80% (170ºC, 2 horas). Estes resultados mostram que é possível obter pellets com depósito de adsorventes de fina granulometria fixados superficialmente.

The main purpose of this work was to produce a pellet to minimize undesirable effects in fixed beds, such as colmatation, through clay fixation on the surface of polymeric particles. Preliminary experiments were carried out by heating the clay, namely Tonsil Terrana 580FF, in order to observe variations on its capacity to adsorb anthocyanins derived from red cabbage. Clays was fixed on five samples of high density polyethylene (HDPE) at 180°C -210°C for two hours. The morphological analyses of the resulting particles were accomplished through Scanning Electron Microscopy (SEM). The experiments demonstrated an increase on clay's adsorptive capacity of 15.65% at 120°C for 30 hours and 16.80% at 170°C for two hours. The SEM analysis showed that the clay particles adhered on the external surface of the pellets .These results show that it is possible to obtain polymeric pellets using HDPE coated with clay.