Metastable β-type Ti alloys with non-toxic addition elements such as Mo, Zr, Sn, Ta and Nb were developed as an alternative to the widely used Ti-6Al-4V alloy for biomedical applications. These alloys possess enhanced biocompatibility and reduced elastic modulus in comparison with Ti-6Al-4V. Moreover, for orthopedic implants, low Young's modulus is required in order to avoid the stress shielding phenomenon. This study analyzes the microstructure and mechanical properties of a new Ti-12Mo-8Nb alloy after hot swaging, annealing at 950 ºC for 1h and water quenching. The alloy was characterized by X-ray diffraction, optical microscopy and transmission electron microscopy. Tensile tests were performed at room temperature. Young's modulus and hardness values were also measured. The structural characterization reveals a metastable β structure containing only a small amount of α and ω phases. Exhibiting a lower Young's modulus than Ti-6Al-4V and other previously studied Ti-Mo-Nb alloys, the Ti-12Mo-8Nb alloy can be a promising alternative for orthopedic application.

β-metastable titanium alloys with high strength to Young’s modulus ratio have been developed by different authors aiming their use as biomaterials for hard tissue replacement. However, it is not easy to combine low elastic modulus with high mechanical strength. In this work, a β-Ti alloy (Ti-10Mo-20Nb) was produced by arc-melting, then homogenized, cold swaged and aged in order to obtain fine α-Ti precipitates in a β-Ti matrix. The microstructures were characterized by transmission electron microscopy and X-ray diffraction. Mechanical properties characterization was based on Vickers microhardness tests and Young’s modulus measurements. The cold swaged material subjected to an ageing treatment at 500 °C for 4 h showed the highest hardness/ Young’s modulus ratio, associated to very fine α phase precipitates in a β-Ti matrix.

Beta titanium alloys were developed for biomedical applications due to the combination of its mechanical properties including low elasticity modulus, high strength, fatigue resistance, good ductility and with excellent corrosion resistance. With this perspective a metastable beta titanium alloy Ti-12Mo-13Nb was developed with the replacement of both vanadium and aluminum from the traditional alloy Ti-6Al-4V. This paper presents the microstructure, mechanical properties of the Ti-12Mo-13Nb hot swaged and aged at 500 °C for 24 h under high vacuum and then water quenched. The alloy structure was characterized by X-ray diffraction and transmission electron microscopy. Tensile tests were carried out at room temperature. The results show a microstructure consisting of a fine dispersed α phase in a β matrix and good mechanical properties including low elastic modulus. The results indicate that Ti-12Mo-13Nb alloy can be a promising alternative for biomedical application.

In this paper the influence of calcination temperature on the corrosion resistance of a Ti/SnO2-Sb electrode prepared according to Pechini's method and its efficiency for phenol oxidation in chloride medium were investigated. When calcination was performed at 600 °C tin distribution throughout the film was more uniform, providing a more homogeneous film structure. Electrolysis of a 0.34 mol.L-1 NaCl solution containing 100 mg.L-1 phenol at 10 mA.cm-2 for 30 minutes lead to corrosion of the electrodes calcined at 400 and 500 °C, whereas the one calcined at 600 °C remained practically unchanged, indicating that the coating structure, which is dependent of calcination temperature, plays an important role on the structural integrity of electrode material. Phenol concentration was reduced in 90% with the Ti/SnO2-Sb electrode calcined at 600 °C after 60 minutes of electrolysis at 10 mA.cm-2.

This study has investigated the niobium (Nb) additions effect on both microstructure and heat-treated Ti-10Mo-xNb (x = 3, 6 and 9) alloys mechanical properties. The microstructures were characterized by optical microscopy, X-ray diffraction and transmission electron microscopy. The mechanical characterization was carried out by Vickers microhardness test and Young's modulus measurements. The outcomes show that the addition of Nb in alloys decreased the proportion of ω and α' phases. The Ti-10Mo-3Nb alloy presented the best hardness and elastic modulus combination among the three developed alloys and also with respect to Ti-6Al-4V alloy and commercially pure Ti.