ABSTRACT This research aimed at evaluating the quality of bonded joints of Eucalyptus wood by using different faces and adhesives to produce EGP (Edge Glued Panels). Glue line shear specimens were obtained from bonded joints glued with PVAc (Polyvinyl Acetate) and EPI (Emulsion Polymer Isocyanate) adhesives, using pieces oriented with tangential, radial and intermediary faces, as well as the combination between them. The specimens were submitted to two pretreatments in order to simulate the use of joints in dry and wet environments. For shear tests, 12 treatments were obtained. The results indicated that the use of tangential x tangential and tangential x intermediary bonding faces and EPI adhesive presented better glue line shear strength for EGP in dry and wet pretreatments, respectively. The joints bonded in the radial x radial direction presented statistically inferior values when compared to the other treatments.

RESUMO O objetivo do estudo foi o de avaliar a viabilidade técnica da produção de painéis aglomerados a partir de fibras oversize resinadas em proporção reduzida de adesivo. Como matéria-prima, foram utilizadas fibras oversize resinadas descartadas do processo produtivo do MDF (Medium Density Fiberboard), partículas flake de Pinus spp. derivadas do cepilhador de uma empresa de MDP (Medium Density Particleboard) e adesivo formado pela resina uréia formaldeído e pela emulsão de parafina. O experimento foi composto por cinco tratamentos, misturando partículas e fibras em diferentes proporções (100:0%; 75:25%; 50:50%; 25:75%; 0:100%). Foram produzidos três painéis por tratamento, com densidade nominal de 650 kg.m-3, 8% de resina e ciclo de prensagem de 160ºC, 40 kgf.cm-2 por 8 minutos. As propriedades dos painéis foram avaliadas por meio dos procedimentos descritos na ASTMD 1047(1993), DIN 53362(1982) e ABNT/NBR 14810(2013). Os resultados demonstraram que as fibras oversize resinadas apresentam potencial para utilização no setor, principalmente, em quantidade acima de 75%, fato que foi evidenciado pelos valores encontrados para estabilidade dimensional e resistência / rigidez. Para adesão interna, o aumento da quantidade de fibras acima de 25% não foi significativo

ABSTRACT The objective of this study was to evaluate the technical feasibility of producing particleboard from oversize resin fibers in a reduced proportion of adhesive. It was used as raw material, oversize resin fibers discarded from the MDF (Medium Density Fiberboard) production process, flake particles of Pinus spp. derived from an MDP (Medium Density Particleboard) company’s chipper and adhesive formed by the urea-formaldehyde resin and paraffin emulsion. The experiment consisted of five treatments, mixing particles and fibers in different proportions (100: 0%; 75: 25%; 50: 50%; 25: 75%; 0: 100%). Three panels were produced per treatment, with nominal density of 650 kg.m-3, 8% resin and pressing cycle of 160ºC, 40 kgf.cm-2 for 8 minutes. The properties of the panels were evaluated by the procedures described in ASTM D-1047 (1993), DIN 53362 (1982) and ABNT / NBR 14810 (2013). The results showed that oversize resin fibers have potential for use in the sector, especially in quantities above 75%, a fact that was evidenced by the values found for dimensional stability and strength/stiffness. For internal adhesion, the increase in the number of fibers above 25% was not significant.

RESUMO Esta pesquisa teve como objetivo avaliar a qualidade de painéis aglomerados produzidos com resíduos de exploração florestal de Pinus taeda. O material na forma de galhos e ponteiras e de tocos e raízes, foram obtidas de um plantio florestal localizado no Município de Mafra - SC. Todo o material foi transformado em cavacos para biomassa e transportados até o local de estudos. As partículas industriais de Pinus foram utilizadas como testemunha e em mistura com os resíduos em diferentes proporções. O plano experimental consistiu na produção de painéis com 100% de cada tipo de material e em mistura destes com proporções de 75/25%, 50/50% e 25/75% com partículas industriais de pinus, além da mistura em partes iguais dos três tipos de materiais. Foram produzidos painéis experimentais com densidade nominal de 0,75 g/cm3, utilizando a resina uréia-formaldeído na proporção de 8% de sólidos -base peso seco das partículas. Os painéis foram prensados com pressão específica de 4,0 MPa, temperatura de 160 ºC e tempo de prensagem de 8 minutos. Os resultados dos ensaios de tração perpendicular atenderam aos requisitos da norma E 312, sendo indicativo de que houve uma colagem adequada destas partículas provenientes de resíduos de exploração florestal. Avaliações gerais dos resultados das propriedades físicas e mecânicas dos painéis experimentais indicam a possibilidade de uso de partículas obtidas a partir de galhos e ponteiras e de tocos e raízes em mistura com as partículas industriais de pinus na proporção de até 50% para produção de painéis aglomerados.

ABSTRACT This study aimed to evaluate the quality of particleboards manufactured with forest exploitation waste from Pinus taeda. The material in the form of branches, tree tops, stumps and roots, was obtained from a forest plantation located in the Municipality of Mafra -SC. All the material was processed into wood chips for biomass and transported to the place of studies. The Pinus industrial particles were used as control and mixed with the waste in different proportions. The experimental plan consisted of the panels manufacture with 100% of each type of material and mixture of these com proportions of 75/25%, 50/50% and 25/75% with Pinus industrial particles, in addition to the mixture in equal parts, of the three types of materials. Experimental panels were manufactured with nominal density of 0.75 g/cm3, using the urea-formaldehyde resin, in the proportion of 8% of solids -dry weight basis of the particles. The panels were pressed with specific pressure of 4.0 MPa, temperature of 160ºC and pressing time of 8 minutes. The results of the internal bond tests met the requirements of the standard EN 312, is indicative that there has been a proper bonding of these particles originating forest exploitation wastes. General evaluations of the physical and mechanical properties results of the experimental panels indicate the possibility of use of particles obtained from branches, tree tops, stumps and roots, mixed com the industrial Pinus particles, in proportion of, up to, 50%, for particleboard manufacture.

RESUMO O objetivo deste estudo foi avaliar as diferentes etapas do ciclo de corte, buscando uma relação hipsométrica adequada para estimar alturas dessas diferentes fases em um reflorestamento de Pinus taeda. Foram realizados cinco tratamentos, sendo o quinto a junção dos dados pertencentes aos demais tratamentos (modelo reduzido). A amostragem seguiu o método de área fixa, no qual o tamanho das parcelas e o número de árvores dominantes diferenciaram-se nos ciclos de corte. Definiu-se a localização das parcelas através de amostragem aleatória simples (oito parcelas por ciclo de corte). Foram determinadas as estatísticas de ajustes, coeficiente de determinação ajustado, erro-padrão e análise de resíduos. Efetuou-se o teste de identidade de Graybill para verificação da necessidade da utilização de diferentes modelos para distintas classes de idade. Os resultados comprovaram que existem diferenças significativas entre adotar-se um modelo específico para cada fase e utilizar um único melhor modelo para o povoamento total.

ABSTRACT This study aimed to evaluate the different phases of the cutting cycle, seeking a proper hypsometric rate to estimate the height of these different phases in a reforestation of Pinus taeda. The study consisted of five treatments, being the fifth the combination of the data belonging to the other treatments. The sampling followed the fixed area method where plots size and number of dominant trees varied with each cutting cycle. The plots location was defined by simple random sampling (eight portions by cutting cycle). We determined the statistical adjustments, adjusted coefficient of determination, standard error and residual analysis. We performed the Graybill identity test to assess the need to use different models for different age classes. Results showed that there are significant differences between adopting a specific model to each stage and use a single best model for the full settlement.