The void structure of zeolites MCM-22, MCM-36 and ITQ-2 were discussed on the bases of catalytic reaction tests. The hydromerization of n-decane on bifunctional Pt/Zeolite Catalysts have been used as model reactions. Beta and ZSM-5 zeolites were used for comparison. It is concluded that all materials show features of 10MR zeolites and have also pores bigger than 12MR in this order MCM-22<MCM-36<ITQ-2.

The layered precursor of MCM-22 was prepared with different Si/Al ratios: 15, 25, 50, 100 and ¥. Upon heat treatment these precursors form MCM-22 zeolite. Both layered precursor and MCM-22 zeolite were characterized by several techniques: Chemical Analysis by Atomic Absorption Spectroscopy (AAS), X-Ray Diffraction (XRD), Thermo-gravimetric Analysis (TGA), Pore Analysis by N2 and Ar adsorption, Scanning Electron Microscopy (SEM), Infrared Spectroscopy (IR) and Temperature Programmed Desorption of ammonium (TPD).

Montmorillonite clay from Brazil was pillared with aluminium polyhydroxications. The influence of Al/Mont ratio and calcination temperature in the properties of the prepared materials was studied. Results showed that the pillarization process increases the basal spaces of the natural clay from 9,7 to 18,5Å and the superficial area from 41 to ~230m2/g. The calcination process at different temperatures showed that the pillared material was stable until 600oC but the adequate temperature for calcination was 450oC. Materials prepared with different Al/Mont ratios showed the maximum Al incorporation for ratios >10meq Al/g and a good distribution for rations >15meq Al/g.