Objective: To compare, using photoelasticity, internal stress produced by USS II type screw with 5.2 and 6.2 mm external diameters, when submitted to three different pullout strengths. Methods: Two photoelastic models were especially made. The simulation was performed using loads of 1.8, 2.4 e 3.3 kgf.The fringe orders were evaluated around the screws. In all the models analyzed the shear stress were calculated. Results: Independently of the applied load, the smaller screw showed higher values of shear stress. Conclusion: According to the analysis performed, we observed that the place of highest stress was in the first thread of the lead, close to the head of the screws. Experimental study.

OBJETIVO: Analisar as tensões geradas no corpo vertebral L4 quando submetida à força de compressão, utilizando a técnica da fotoelasticidade de transmissão. MÉTODOS: Doze modelos fotoelásticos foram utilizados e divididos em três grupos, sendo cada grupo formado por quatro modelos, de acordo com a localização do corte sagital nas vértebras L4-L5 (cortes A, B e C). A simulação foi realizada utilizando uma força compressão de 15 N e as ordens de franjas foram avaliadas no corpo vertebral L4 utilizando o método de compensação de Tardy. RESULTADOS: A análise fotoelástica mostrou que em geral, as tensões se distribuíram de forma homogênea nos corpos vertebrais. As tensões no corte C foram maiores que no B, que por sua vez foram maiores que no corte A. CONCLUSÃO: A região posterior do corpo vertebral L4, principalmente no corte C, apresentou maiores concentrações de tensões, sendo assim, é a área mais susceptível à fratura vertebral e à espondilolistese. Análises econômicas e de decisão. Desenvolvimento de modelo econômico ou de decisão, Nível de evidência I.

OBJECTIVE: to analyze the shear forces on the vertebral body L4 when submitted to a compression force by means of transmission photoelasticity. METHODS: Twelve photoelastic models were divided into three groups, with four models per group, according to the positioning of the sagittal section vertebrae L4-L5 (sections A, B and C). The simulation was performed using a 15N compression force, and the fringe orders were evaluated in the vertebral body L4 by the Tardy compensation method. RESULTS: Photoelastic analysis showed, in general, a homogeneous distribution in the vertebral bodies. The shear forces were higher in section C than B, and higher in B than A. CONCLUSION: The posterior area of L4, mainly in section C, showed higher shear concentrations, corresponding to a more susceptible area for bone fracture and spondylolisthesis. Economic and Decision Analyses - Development of an Economic or Decision Model. Level I

INTRODUÇÃO: O sistema de fixação vertebral utilizando o parafuso pedicular é um dos métodos mais eficientes no tratamento de patologias da coluna vertebral. Quando o parafuso estiver submetido á força de arrancamento, este gera tensões ao seu redor, principalmente próximas do canal medular, situação esta que pode ser analisada pela técnica da fotoelasticidade. OBJETIVO: Foram analisadas as tensões internas geradas próximas ao canal medular de modelos fotoelásticos de vértebras utilizando diferentes medidas de parafusos do sistema de fixação vertebral submetidos à força de arrancamento. MÉTODO: Foi utilizado um modelo de vértebra lombar em material fotoelástico utilizando três medidas de parafusos pediculares (5, 6 e 7mm) do tipo USS1. As tensões internas ao redor do parafuso foram avaliadas em 12 pontos pré-determinados utilizando um polariscópio de transmissão plana. RESULTADOS: As regiões de maiores concentrações de tensões foram observadas entre o canal medular e as curvas do processo transverso. Nas comparações das médias das tensões cisalhantes máximas entre os parafusos 5 e 7, e 6 e 7 foram observadas diferenças estatísticas significativas e entre 5 e 6 não. CONCLUSÃO: Foi observada que as tensões internas são mais elevadas em áreas irregulares próxima ao canal medular, mostrando ser uma região crítica.

INTRODUCTION: The vertebrae fixation system using pedicular screws is one of the most efficient methods to treat vertebral spine pathologies. When the screw is submitted to pullout strength, it causes internal tension near the medullar canal and this situation can be analyzed by using the photoelasticity technique. OBJECTIVE: Were analyzed those internal tensions near the medullar canal of photoelastic vertebra models using different sizes of screws of the vertebral fixation system submitted to pullout strength. METHODS: A lumbar vertebral model made of photoelastic material with three different USS1-type pedicular screw sizes (5, 6, and 7mm) was used. The internal tensions around the screw were tested in 12 predetermined points by a plain transmission polaroscope. RESULTS: The areas of greater tension concentration were between the medullar canal and the curves of the transverse process. Comparing the maximum average pulling tension, statistical differences were observed between screws 5 and 7, and 6 and 7. On the other hand, for screws 5 and 6, there were no significant differences. CONCLUSION: The study evidenced that the internal tensions are greater in irregular areas, next to the medullar canal, showing that this is a critical region.

INTRODUÇÃO: A fotoelasticidade é utilizada para avaliar as tensões/deformações produzidas nos materiais fotoelásticos, quando submetidos a determinado carregamento, através da observação de efeitos óticos. O desempenho do parafuso e as funções mecânicas estão diretamente relacionados com a qualidade da fixação dos parafusos nas vértebras. A fotoelasticidade é uma ferramenta importante para realizar estudos comparativos desta natureza. OBJETIVO: O objetivo deste estudo foi comparar por meio da fotoelasticidade, as tensões internas produzidas pelo parafuso com 6 mm de diâmetro externo, quando submetido a duas diferentes forças de arrancamento. MATERIAIS E MÉTODOS: Para isso, foram confeccionados quatro modelos fotoelásticos. A simulação foi realizada utilizando duas forças de arrancamento 0,75 e 1,50 kgf. As tensões cisalhantes foram calculadas nos 19 pontos em torno dos parafusos, utilizando o método de compensação de Tardy. RESULTADOS: Os valores das tensões cisalhantes foram maiores quando utilizada a força de arrancamento de 1,50 kgf. CONCLUSÃO: Assim sendo, o parafuso estará mais suscetível ao arrancamento com a aplicação de força de maior intensidade. De acordo com as análises realizadas verificamos também que o local de maior tensão cisalhante foi observado no pico das cristas, principalmente próxima às pontas dos parafusos, independente da força utilizada.

INTRODUCTION: The photoelasticity is used for assessing the tensions/deformations involved in photoelastic materials when submitted to a given load by the observation of optical effects. The screw performance and mechanical functions are directly associated to the quality of the screws fixation in the vertebrae. Photoelasticity is an important tool to perform comparative studies of this nature OBJECTIVE: The aim of this study was to compare, by using photoelasticity, internal stresses produced by the screw with an external diameter of 6 mm, when submitted to two different pullout strengths. MATERIALS AND METHODS: For this, four photoelastic models were produced. The simulation was conducted by using two pullout strengths: 0.75 and 1.50 kgf. The maximum shear stresses were calculated on 19 points around the screws, using the Tardy compensation method. RESULTS: The values of maximum shear stress were higher with the load of 1.50 kgf. CONCLUSION: Thus, the screw will be more susceptible to pullout when heavier loads are applied. According to our analysis, we also found that the site with the highest maximum shear stress was found to be at the peak of creast, particularly near the tips of the screws, regardless of the load employed.