Abstract Carbon nanostructures have been extensively studied due to combination of properties they present. With different geometries and reactivities, carbon nanotubes, graphene and fullerene were oxidized and modified with octadecylamine (ODA) in order to decrease van der Waals’s interaction and consequently improve the polymer-carbon nanostructures affinity for use in nanocomposites. Nanostructures were characterized as morphology, chemical structure, molecular conformation and thermal properties. All nanostructures showed results that confirm the modification with ODA, without geometry being altered. Modified nanostructures showed different percentages of ODA: graphene 86%, carbon nanotubes 83% and fullerene 63%. It was attributed to distinct reactivities, shapes and specific surface area available, due to different amounts of reactive terminals obtained before oxidation reactions. However, they showed a lower interfacial interaction, which is highly favorable for use in polymer nanocomposites.

Abstract Polymeric membranes were developed using a SPEEK (sulfonated poly(ether ether ketone)) polymer matrix, containing titanium oxide (TiO2) (incorporated by sol-gel method). SPEEK with different sulfonation degrees (SD): 63% and 50% were used. The influence of sulfonation degree on membrane properties was investigated. The thermal analysis (TGA and DTGA) and X-ray diffraction (XRD) were carried out to characterize the membranes and electrochemical impedance spectroscopy (EIS) was carried out to evaluate the proton conductivity of the membranes. The proton conductivities in water were of 3.25 to 37.08 mS.cm-1. Experimental data of impedance spectroscopy were analyzed with equivalent circuits using the Zview software, and the results showed that, the best fitted was at 80 °C.

Proton-conducting hybrid membranes consisting of poly(ether ether ketone) sulfonated (SPEEK) and titanium oxide (TiO2) were prepared using the sol-gel technique for application in direct ethanol fuel cells. The effect from TiO2 incorporation on membrane properties such as ethanol uptake, pervaporation and proton conductivity was investigated. The uptake and permeated flux decreased with increasing content of TiO2. The ethanol permeability was about one order of magnitude smaller than Nafion® 117. FTIR spectra indicated that PEEK was sulfonated and the second degradation temperature of SPEEK58 samples confirmed the titanium oxide incorporation. The proton conductivity in ethanol solution was of the order of 10-3 S cm-1 when 4 or 8 wt% TiO2 were added, and generally increased with addition of TiO2.