Since epoxy resins are used as composite matrix with excellent results, and silica is one of the fillers most often employed, this study compared the performance of rice husk ash (RHA) as filler in epoxy composites, in replacement for high-purity silica. Composites were molded containing 20%, 40%, and 60% (wt) silica or RHA. Viscosity analysis, infrared spectroscopy (IR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) as well as mechanical and water absorption tests were carried out to evaluate composites. Glass transition temperature after curing and thermal degradation temperature of all samples analyzed were approximately 140 ºC and 370 ºC, respectively. RHA and silica exhibited similar mechanical and water absorption characteristics, indicating that rice husk ash may be a suitable replacement for silica. SEM imaging showed good filler dispersion and distribution in the polymer matrix, highlighting the more effective adhesion interface between RHA particles and the matrix.

ABSTRACT This study evaluates the thermal, morphological and mechanical behavior of polypropylene (PP) composite with different natural fibers. The fibers used were wood, sugarcane, bamboo, babassu, coconut and kenaf with and without coupling agent. The thermal, morphological and mechanical properties were evaluated, and a composite PP+GFPP (glass fiber) was used as reference. The interaction at the interface fiber-polymer matrix was studied by scanning electron microscopy (SEM) at the fractured surface of the composites, as expected the presence of maleic anhydride (MA) as coupling agent increasedthe interaction at the interface. The influence of natural fiber in the degree of crystallinity of the composites was evaluated by DSC analysis. The samples of PP+GFPP and PP+(PP-MA)+WF (wood flour) showed better temperature stability. PP+GF also presented superior flexural modulus. The thermal dynamic mechanical behavior was evaluated by DMA, a decrease in storage modulus with increasing temperature was observed, the PP+GF and the composite containing maleic anhydride and sugarcane fiber showed higher modulus. The natural fiber biocomposites studied, consistently presented lower flexural modulus and tensile strength than the reference composite, with and without the use of coupling agent. As expected the use of natural fibers lowered the density compared to the reference material.