In this work, proton NMR relaxometry was used to measure the behavior of spin-lattice relaxation time with T1H as the time constant, and also of spin-spin relaxation time with the time constant T2H. These relaxometry parameters were determined to better understand the changes in the main structures present in commercial and in nature forms of origanum. The T1H relaxation data showed that the structures which had higher molecular mass were more sensitive to degradation with increased temperature treatment. According to the values of the T2H parameter, up to 150 degrees no significant change in the mobility and organization of water was observed. These data infer that the ideal cooking temperature and tea preparation mode for this herb should be around 100 degrees for the sample not to lose its characteristics. Also, it is not advisable to cook this herb at higher than 150 degrees but better to consume it at room temperature, especially give commercial herb has already been dehydrated.

Poly (ε-caprolactone) (PCL) based hybrids containing different amounts of modified (Aerosil® R972) and unmodified (Aerosil® A200) silica oxide were prepared employing the solution method, using chloroform. The relationships of the amount of nanofillers, organic coating, molecular structure and intermolecular interaction of the hybrid materials were investigated mainly using low-field nuclear magnetic resonance (NMR). The NMR analyses involved the hydrogen spin-lattice relaxation time (T1H) and hydrogen spin-lattice relaxation time in the rotating frame (T1ρH). The spin-lattice relaxation time measurements revealed that the PCL/silica oxide hybrids were heterogeneous, meaning their components were well dispersed. X-ray diffraction (XRD), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) were also employed. The DSC data showed that all the materials had lower crystallization temperature (Tc) and melting temperature (Tm), so the crystallinity degree of the PCL decreased in the hybrids. The TGA analysis demonstrated that the addition of modified and unmodified silica oxide does not cause considerable changes to PCL's thermal stability, since no significant variations in the maximum temperature (Tmax) were observed in relation to the neat polymer.