The per-O-acetylation of D-ribono-1,4-lactone and representative carbohydrates through the combination of acetic anhydride and molecular sieves under solvent-free conditions is demonstrated. The use of 13X/KCl molecular sieves as the heterogeneous catalyst was found to be more efficient than the excess of pyridine normally employed in the conventional method, giving high yields of the expected peracetylated product after 3 h at 25 ºC or 1 h at 50 ºC. The transformation can be carried out in gram scale and in an open flask. Additionally, the catalyst is readily separated from the reaction medium and can be reutilized without significant loss of activity. This green procedure for acetylation was extended to D-ribonolactone derivatives and natural carbohydrates. To demonstrate the synthetic utility of the method, 2,3,5-tri-O-acetyl-D-ribonolactone was selected as the substrate for the regioselective alcoholysis of acetyl group catalyzed by Candida antarctica lipase B in EtOH to selectively produce 2,3-di-O-acetyl-D-ribonolactone in gram scale.

Os polímeros intrinsecamente condutores (PIC), como a polianilina (PAni), têm sido estudados com alternativa em filmes protetores de metais oxidáveis contra a corrosão. Dada a dificuldade de fusão ou dissolução da PAni para a produção de filmes, investigou-se a possibilidade de obter filmes pela mistura de PAni no estado oxidado e desdopado, conhecida como base esmeraldina, com plastificante não dopante 4-cloro-3-metilfenol (CMF) e solvente conveniente. Filmes produzidos desta forma foram caracterizados por espectroscopia FTIR e RAMAN, por TGA e ensaio de voltametria cíclica. A caracterização mostrou filmes termicamente estáveis até a temperatura de 200 ºC com indícios de interação da PAni com o CMF, com a PAni se mantendo no estado oxidado no filme produzido, condição necessária para futura aplicação como filme anticorrosivo de proteção anódica.

The intrinsically conductive polymers (PCI), such as polyaniline (PAni), have been studied as an alternative in the development of protective films of oxidizable metals against corrosion. Given the difficulty of mixing and dissolving PAni for the production of films, here we investigated the possibility of obtaining a mixture of PAni films in the oxidized, undoped state, referred to as emeraldine base, with the non-doping plasticizer 4-chloro-3-methylphenol (CMF) and a convenient solvent. Films produced in this way were characterized by FTIR and Raman spectroscopy, TGA and cyclic voltammetry. The characterization showed films thermally stable up to 200 ºC with evidence of interaction between PAni and CMF, with PAni remaining in the oxidized state in the film produced, which a necessary condition for application as anodic protection in anticorrosion films.