Aim this review aims to present the mechanisms of protein interactions with titanium dental implant surfaces. Methods the analyses were based on searches of scientific articles available in English and Portuguese in PubMed (MEDLINE), Bireme (LILACS), Scielo, Web of Science and Google Scholar. Results titanium dental implant treatments success rates (95-98%) are mainly due to the biocompatibility of titanium oxide on the implant surface, surgical techniques adopted, good implants manufacturing processes and biomechanical knowledge of the systems. Studies in past decades has empirically developed implant surfaces with significant changes in morphologies, roughness, wettability, surface energy, chemical composition, and chemical groups density or deposited molecules. These changes promoted better protein adsorption, osteoblast adhesion, and changes in the mechanisms involved in osseointegration. Thus, the time to put the implant in function has been reduced and the success rates have increased. In the osseointegration process, at the nanoscale, there is no contact between the bone and the implant surface, but there is the formation of a protein anchorage between the periosteum and the implant with an interface formed by proteins. In all the reactions between the body and the implant surface, the activities of fibronectin and integrin are essential, since they are responsible for transmitting information to the cell for its differentiation, adhesion and mobility. Conclusion thus, the analyses of protein-implant interactions are indispensable for a better understanding of the performance of osseointegrated dental implants.

Approximately thousand years ago it was reported the use of mandibles of ants for suture. In this sense, bioinspired components, as absorbable surgical clamps, can be designed. This study is aimed to characterize the mandible of the ant Atta laevigata in order to help the selection of candidate biomaterials for application as surgical clamps. Three pairs of mandibles were used and ten nanoindenations were performed in each pair. The average hardness for the samples in the internal and external regions were 0.36 ± 0.06 GPa and 0.19 ± 0.04 GPa, respectively and the average elastic modulus for the internal and external regions were 6.16 ± 0.23 GPa and 2.74 ± 0.44 GPa, respectively. The morphology of the mandible was observed in detail by scanning electron microscopy, as well as Energy-dispersive X-ray spectroscopy. The average roughnesses on the internal and external regions, measured by atomic force microscopy, were 6.73 ± 0.90 nm and 11.87 ± 1.42 nm, respectively. From these results, it was possible to identify biomaterials that mimic the mandible behaviour for surgical clamp.